Acta Metall Sin  2012, Vol. 48 Issue (5): 607-614    DOI: 10.3724/SP.J.1037.2012.00014
论文 Current Issue | Archive | Adv Search |
PRECIPITATION BEHAVIOR OF AZ91 MAGNESIUM ALLOYS WITH DIFFERENT La CONTENTS
ZHANG Jinling1,2,3, FENG Zhiyong1, HU Lanqing1,2,3,WANG Shebin1,2,3, XU Bingshe1,2,3
1. Taiyuan University of Technology, College of Material Science and Technology, Taiyuan 030024
2. Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education, Taiyuan 030024
3. Shanxi Research Center of Advanced Materials Science and Technology,Taiyuan 030024
Cite this article: 

ZHANG Jinling1,2,3, FENG Zhiyong1, HU Lanqing1,2,3,WANG Shebin1,2,3, XU Bingshe1,2,3. PRECIPITATION BEHAVIOR OF AZ91 MAGNESIUM ALLOYS WITH DIFFERENT La CONTENTS. Acta Metall Sin, 2012, 48(5): 607-614.

Download:  PDF(3322KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  The changes of microhardness, microstructures and precipitation phase morphologies of as--cast and aged AZ91 alloys with different La were characterized by TEM, OM, SEM and Vickers. The influences of discontinuous β phase and Al11La3 on AZ91 magnesium alloy were discussed and the diffusion coefficient of Al atom in the aging process was calculated. The results showed that the alloy with 0.16%La aged at 170 ℃ for 24 h has the largest hardness (138 HV). By extending aging time and adding La element, the discontinuous precipitation phases was transformed into continuous lath--sharped phases and the diffusion coefficient of Al atom was decreased, the volume and distribution of β phase were changed. During the process of heat treatment, the topography of Al11La3 in grain boundary was not changed, but the anchoring effect of Al11La3 restricted the growth of β phase. By controlling the content of La and parameters of aging treatment, the volume and size of β phase were changed, in the mean time the strengthening and toughness properties of alloys can been improved effectively.
Key words:  AZ91 magnesium alloy      aging treatment      La solution      diffusion coefficient     
Received:  09 January 2012     
ZTFLH: 

TG146.6

 
Fund: 

National Natural Science Foundation of China

URL: 

https://www.ams.org.cn/EN/10.3724/SP.J.1037.2012.00014     OR     https://www.ams.org.cn/EN/Y2012/V48/I5/607

[1] Aghion E, Bronfin B, Eliezer D.  J MaterProcess Technol,2001; 117: 381

[2] Mordike B L, Ebert T.  Mater Sci Eng, 2001; A302: 37

[3] Liu Q.  Acta Metall Sin, 2010; 46: 1458

    (刘庆. 金属学报, 2010; 46: 1458)

[4] Chen Z H, Yan H G.  Magnesium Alloy. Beijing: Chemical Industry Press, 2004, 29

    (陈振华, 严红革. 镁合金. 北京: 化学工业出版社, 2004, 29)

[5] Clark J B, Zabdyr L, Moser Z.  In: ASM Handbook, vol.3, Alloy Phase Diagrama. Materials Park, Ohio: ASM International, 1992: 285

[6] Zeng X Q, Wu Y J, Peng L M.  Acta Metall Sin, 2010; 46: 1041

    (曾小勤, 吴玉娟, 彭立明. 金属学报, 2010; 46: 1041)

[7] Xiao X L, Luo C P, Liu J W, Wu D X, Nie J F.  Chin J Nonferrous Met,2003; 13: 15

    (肖晓玲, 罗承萍, 刘江文, 吴东晓, 聂建峰. 中国有色金属学报, 2003; 13: 15)

[8] Xiao X L, Luo C P, Nie J F.  Acta Metall Sin, 2001; 37: 1

    (肖晓玲, 罗承萍, 聂建峰. 金属学报, 2001; 37: 1)

[9] Xiao X L, Luo C P, Liu J W, Nie J F.  Acta Metall Sin, 2002; 28: 709

    (肖晓玲, 罗承萍, 刘江文, 聂建峰. 金属学报, 2002; 28: 709)

[10] Cizek L, Greger M, Pawlica L, Dobrzanski L A, Tanski T.J Mater Process Technol, 2004; 157--158: 466

[11] Li P J, Tang B, Kandal ova E G.  Mater Lett, 2005; 59: 671

[12] Zhao Y H, Chen Y G, Tang Y B.  Rare Met Mater Eng, 2010; 39: 843

     (赵源华, 陈云贵, 唐永柏. 稀有金属材料与工程, 2010; 39: 844)

[13] Zhang J L, Wang S B, Xu B S.  Rare Met Mater Eng, 2007; 36: 1061

     (张金玲, 王社斌, 许并社. 稀有金属材料与工程, 2007; 36: 1061)

[14] Li W X.  Magnesium and Magnesium Alloy. Changsha: Central South University Press, 2005; 341

     (黎文献. 镁及镁合金. 长沙: 中南大学出版社, 2005; 341)

[15] Tang W, Han E H, Xu Y B.  Acta Metall Sin, 2005, 41: 1199

     (唐伟, 韩恩厚, 徐永波. 金属学报, 2005; 41: 1199)

[16] Zhang J M, Jiang B L, Wang Z H, Yuan S, Xia P J.  Heat Treat Met,2007; 32: 6

     (张菊梅, 蒋百灵, 王志虎, 袁森, 夏鹏举. 金属热处理, 2007; 32: 6)

[17] Wang S B, Qi X Y, Zhang J L, Xu B S.  Acta Metall Sin, 2011; 47: 743

     (王社斌, 祁小叶, 张金玲, 许并社. 金属学报, 2011; 47: 743)

[18] Wu Y R.  PhD Thesis, Hunan University, Changsha, 2007

     (吴玉蓉. 湖南大学博士论文, 长沙, 2007)

[19] Liu L F, Ding H L, Ding W J.  Rare Met Mater Eng, 2009; 38: 104

     (刘六法, 丁汉林, 丁文江. 稀有金属材料与工程, 2009; 38: 104)

[20] Yu K, Li W X, Zhang S J.  Rare Met Mater Eng, 2005; 34: 1105

     (余琨, 黎文献, 张世军. 稀有金属材料与工程, 2005; 34: 1105)

[21] Wang S B, Zhang J L, Qi X Y, Xu B S.  Mater Eng, 2009; (Suppl.1): 303

     (王社斌, 张金玲, 祁小叶, 许并社. 材料工程, 2009; (增刊1): 303)
 
[1] GENG Yaoxiang, TANG Hao, XU Junhua, ZHANG Zhijie, YU Lihua, JU Hongbo, JIANG Le, JIAN Jianglin. Formability and Mechanical Properties of High-Strength Al-(Mn, Mg)-(Sc, Zr) Alloy Produced by Selective Laser Melting[J]. 金属学报, 2022, 58(8): 1044-1054.
[2] Yuanrong LIU,Weimin CHEN,Ying TANG,Yong DU,Lijun ZHANG. APPLICATION OF PRAGMATIC NUMERICAL INVERSE METHOD IN COMPUTATION OF INTERDIFFUSION COEFFICIENTS IN Al TERNARY ALLOYS[J]. 金属学报, 2016, 52(8): 1009-1016.
[3] Zujiang HUANG, Min ZHOU, Yang YANG, Quanzhi CHEN, Shiguang TANG, Weizhou LI. STUDY OF ANODIC ALUMINUM OXIDE FILM AS AN INTERLAYER TO SUPPRESS ELEMENT DIFFUSION[J]. 金属学报, 2016, 52(3): 341-348.
[4] LIU Fenjun, FU Li, ZHANG Wenyuan, MENG Qiang, DONG Chunlin, LUAN Guohong. INTERFACE STRUCTURE AND MECHANICAL PRO-PERTIES OF FRICTION STIR WELDING JOINT OF 2099-T83/2060-T8 DISSIMILAR Al-Li ALLOYS[J]. 金属学报, 2015, 51(3): 281-288.
[5] YANG Chenggong, SHAN Jiguo, REN Jialie. PHASE TRANSFORMATION TEMPERATURE CONTROL OF WELD METAL OF LASER WELDED TiNi SHAPE MEMORY ALLOY JOINT[J]. 金属学报, 2013, 49(2): 199-206.
[6] XIANG Hongliang FAN Jinchun LIU Dong GUO Peipei. EFFECTS OF ANTIBACTERIAL AGING TREATMENT ON MICROSTRUCTURE AND PROPERTIES OF COPPER-CONTAINING DUPLEX STAINLESS STEEL
I. Microstructure and Evolution of Copper-Rich Phase
[J]. 金属学报, 2012, 48(9): 1081-1088.
[7] HU Benfu LIU Guoquan WU Kai HU Penghui. MORPHOLOGICAL CHANGES BEHAVIOR OF FAN-TYPE STRUCTURES OF γ' PRECIPITATES IN NICKEL-BASED POWDER METALLURGY SUPERALLOYS[J]. 金属学报, 2012, 48(7): 830-836.
[8] . PHASE FIELD SIMULATION OF SINTERING PROCESS IN BIPHASIC POROUS MATERIAL[J]. 金属学报, 2012, 48(10): 1207-1214.
[9] WANG Shebin QI Xiaoye ZHANG Jinling LIU Lu XU Bingshe. EFFECT OF AGING TREATMENT AND La CONTENT ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF AZ91 ALLOY[J]. 金属学报, 2011, 47(6): 743-750.
[10] CHEN Yexin CHANG Qinggang. EFFECT OF TRAPS ON DIFFUSIVITY OF HYDROGEN IN 20g CLEAN STEEL[J]. 金属学报, 2011, 47(5): 548-552.
[11] ZENG Xiaoqin WU Yujuan PENG Liming LIN Dongliang DING Wenjiang PENG Yinghong. LPSO STRUCTURE AND AGING PHASES IN Mg-Gd-Zn-Zr ALLOY[J]. 金属学报, 2010, 46(9): 1041-1046.
[12] Cao Fa-he. Preparation and Corrosion resistance of Cerium-based Chemical Conversion Coating on AZ91 Magnesium alloy[J]. 金属学报, 2008, 44(8): 979-985 .
[13] . The distribution and diffusion of carbon atoms during deformation of undercooled austenite in medium carbon steel[J]. 金属学报, 2007, 43(8): 785-790 .
[14] Liu S F. The influence of cerium addition on the microstructure of AZ91 magnesium alloy and grain refinement mechanism[J]. 金属学报, 2006, 42(4): 443-448 .
[15] LIU Shi; ZHENG Hua; GUI Quanhong; MA Aihua; YU Hongbo; WANG Longbao. MEASUREMENTS OF HYDROGEN DIFFUSION COEFFICIENT FOR TUBE SAMPLES AT MEDIUM AND HIGH TEMPERATURES[J]. 金属学报, 2004, 40(4): 393-398 .
No Suggested Reading articles found!