| PLASTIC INSTABILITY ANALYSIS OF 5052 ALUMINUM SHEETS IN MAGNETIC DYNAMIC TENSION PROCESS |
| LIU Dahai1,YU Haiping2, LI Chunfeng2 |
1.School of Aeronautical Manufacturing Engineering, Nanchang Hangkong University, Nanchang 330063
2.School of Materials Science and Engineering, Harbin Institute of Technology,Harbin 150001 |
|
Cite this article:
LIU Dahai,YU Haiping, LI Chunfeng. PLASTIC INSTABILITY ANALYSIS OF 5052 ALUMINUM SHEETS IN MAGNETIC DYNAMIC TENSION PROCESS. Acta Metall Sin, 2012, 48(5): 519-525.
|
|
|
Abstract In order to reveal the hyperplasticity mechanism of electromagnetic forming (EMF), the plastic instability mechanisms and formation behaviors of 5052 aluminum alloy sheets in pulsed magnetic tension process were investigated by theoretical analysis and microanalysis. Results show that inertia force plays an important role in dynamic forming, which has the suppression effect on structural instability and thus improves the formability of sheet and spreads instability. The nature of dynamic formation is much similar with that of quasi--static formation and no special formation structures arise in dynamic process for 5052 aluminum alloy sheets. The formation mechanism of both processes is dislocation slip mechanism. For quasi--static formation, the dislocations show a uniform single--slip pattern, fracture combined with dislocation tangling and climbing. While for dynamic formation, dislocation system tends to more slips, large areas showing clear cross-slip structures. The dislocation bands are narrower and much denser than those shown in the quasi--static process, and a much more uniform dislocation configuration is also exhibited after pulsed magnetic loadings. The characteristics of multi--slips and uniform effect of dislocations under pulsed magnetic loading conditions will result in much higher plasticity and strength of materials.
|
|
Received: 30 November 2011
|
| [1] Li C F. High Energy Rate Forming. Beijing: National Defense Industry Press, 2001: 1 (李春峰. 高能率成形技术. 北京: 国防工业出版社, 2001: 1)[2] Psyk V, Risch D, Kinsey B L, Tekkaya A E, Kleiner M. J Mater Process Technol, 2011; 5: 787[3] Vohnout V J. PhD Thesis, Ohio State University, Columbus, 1998[4] Balanethiram V S, Daehn G S. Scr Metall, 1992; 27: 1783[5] Balanethiram V S, Daehn G S. Scr Metall, 1994; 30: 515[6] Balanethiram V S, Hu X Y, Daehn G S. J Mater Process Technol,1994; 45: 595[7] Hu X Y, Wagoner R H, Daehn G S, Ghosh S. Metall Trans,1994; 25A: 2723[8] Hu X Y, Daehn G S. Acta Mater, 1996; 44: 1021[9] Oliveira D A, Worswick M J. J Phys IV France, 2003; 110: 293[10] Oliveira D A, Worswick M J, Finn M, Newman D. J Mater Process Technol, 2005; 170: 350[11] Imbert J M, Winkler S L, Worswick M J, Oliveira D A. J Eng Mater Technol, 2005; 27: 127[12] Seth M. PhD Thesis, Ohio State University, Columbus, 2006[13] Thomas J D, Seth M, Daehn G S, Bradley J R, Triantafyllidis N. Acta Mater, 2007; 55: 2863[14] Regazzoni G, Kocks U F, Follansbee P S. Acta Mater, 1987; 35: 2865[15] Follansbee P S, Kocks U F. Acta Mater, 1988; 36: 81[16] Gorham D A. J De Phys III, 1991; 1: 411[17] Dioh N N, Leevers P S, Williams J G. Polymer, 1993; 34: 4230[18] Meyers M A. Dynamic Behavior of Materials. New York: Wiley, 1994[19] Golovashchenko S F. J Mater Eng Perform, 2007; 16: 314[20] Hecker S S. J Eng Mater Technol, 1975; 97H: 66[21] Blazynsk T Z, translated by Li F Q, Wu B Q. Explosive Welding,Forming and Compaction. Beijing: China Machine Press, 1983: 76 (Blazynsk T Z著, 李富勤, 吴柏青译. 爆炸焊接、成形与压制.北京: 机械工业出版社, 1983: 76) |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|