| Transformation and deformation characteristics of Ti-50.8Ni-0.3Cr superelastic alloy |
| Zhi-rong HE |
| 陕西理工学院材料科学与工程学院 |
|
Cite this article:
Zhi-rong HE. Transformation and deformation characteristics of Ti-50.8Ni-0.3Cr superelastic alloy. Acta Metall Sin, 2008, 44(9): 1076-1080 .
|
|
|
Abstract Effects of annealing and deforming temperatures, and the stress-strain cycle on the transformation, deformation and stress cycling characteristics of Ti-50.8Ni-0.3Cr superelastic (SE) alloy wires and coil springs were investigated with differential scanning calorimetry, X-ray diffraction, tensile test, and cycling test. The 350—600 ℃ annealing Ti-50.8Ni-0.3Cr alloy shows SE property at the room temperature, and the microstructure at the room temperature consists of parent phase. The annealing temperatures influence remarkably transformation type of the alloy. With increasing the annealing temperature the martensitic (M) transformation temperature increases, the R transformation temperature increases firstly then decreases, and the stress-induced M stress decreases firstly then increases. With increasing the deforming temperature the stress-induced M critical shear stress of the SE spring increases. The decline of recovery ratio is quick at the beginning of the stress-strain cycle, and the ratio is slow with the increasing of cycle number. The prior cyclic training can enhance the SE stability of the alloy spring. To obtain stable SE property for the alloy spring, the annealing temperature should be 400—550 ℃, and the using temperature should be over room temperature.
|
|
Received: 23 November 2007
|
|
|
[1]He Z R,Wang F,Zhou J E.Heat Treat Met,2006;31(9): 18 (贺志荣，王芳，周敬恩．金属热处理，2006；31(9)：18)
[2]He Z R,Zhang Y H,Wang Y S,Zhou J E.Acta Metall Sin,2004;40:46 (贺志荣，张永宏，王永善，周敬恩．金属学报，2004；40：46)
[3]He Z R.Mater Rev,2005;19(4):50 (贺志荣．材料导报，2005；19(4)：50)
[4]Hosoda H,Wakashima K,Miyazaki S,Inoue K.Mater Res Soc Symp Proc,2005;842:353
[5]Choi M S,Ogawa J,Fukuda T,Kakeshita T.Mater Sci Eng,2006;A438-440:527
[6]He Z R,Wang F.Acta Metall Sin,2008;44:23 (贺志荣，王芳．金属学报，2008；44：23)
[7]Kishi Y,Yajima Z,Shimizu K,Morii K.J Phys IV,2001; 11(8):101
[8]Hosoda H,Hanada S,Inoue K,Fukui T,Mishima Y, Suzuki T.Intermetallics,1998;6:291
[9]Kinoshita K,Matsumoto E,Shibata T.Trans Jpn Soc Mech Eng,2004;70(689)A:43 (木下胜之，松本英二，柴田俊忍．日本机械学会论文集，2004；70(689)A：43)
[10]He Z R,Wang F,Wang Y S,Xia P J,Yang B.Acta Metall Sin,2007;43:1293 (贺志荣，王芳，王永善，夏鹏举，饧波．金属学报，2007；43：1293)
[11]He Z R,Zhou J E,Miyazaki S.Acta Metall Sin,2003;39: 617 (贺志荣，周敬恩，宫崎修一．金属学报，2003；39：617)
[12]Miyazaki S,Otsuka K.Metall Trans,1986;17A:53
[13]Semba H,Okabe N,Yamaji T,Okita K,Yamauchi K. Mater Trans,2006;47:772
[14]Tan G,Liu Y,Sittner P,Saunders M.Scr Mater,2004; 50:193
[15]Miyazaki S,Imai T,Igo Y.Metall Trans,1986;17A:115
[16]Gong J M,Tobushi H.J Funct Mater,2002;33:391 (巩建鸣，户伏寿昭．功能材料，2002；33：391) |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|