Effects of Helium on Behavior of Point Defect Produced by Irradiation in Low Activation Fe-Cr-Mn(W,V) Alloys

Acta Metall Sin

2004, Vol. 40

Issue (9): 955-961 DOI:

Research Articles

Current Issue | Archive | Adv Search

Effects of Helium on Behavior of Point Defect Produced by Irradiation in Low Activation Fe-Cr-Mn(W,V) Alloys

HU Benfu TAKAHASHI Heishichiro

School of Materials Science and Technology; University of Science and Technology Beijing; Beijing 100083

Cite this article:

HU Benfu; TAKAHASHI; Heishichiro. Effects of Helium on Behavior of Point Defect Produced by Irradiation in Low Activation Fe-Cr-Mn(W,V) Alloys. Acta Metall Sin, 2004, 40(9): 955-961 .

Download:

PDF(15533KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to investigate the effects of helium on the excess point defects and secondary defects processes in low activation Fe-Cr-Mn(W,V) alloys during electron beam and electron-He+ ion dual beam irradiation, the in situ observation was carried out using a high voltage electron microscope connected with an ion accelerator. The experiment result indicates that the interaction between helium and point defect clusters formed in the early stage of irradiation affected the secondary defects (dislocation, dislocation loop and void) formation. The helium enhances the increase in dislocation density and void nucleation site obviously. As a result, the void swelling in Fe-Cr-Mn(W,V) alloy was enhanced. The mechanism of interaction between helium and point defects produced by irradiation was also discussed.

Key words: Fe-Cr-Mn alloy irradiation damage helium

Received: 29 September 2003

ZTFLH:	TN1
	TL8

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	HU Benfu
	TAKAHASHI
	Heishichiro

URL:

https://www.ams.org.cn/EN/ OR https://www.ams.org.cn/EN/Y2004/V40/I9/955

[1] Sizmann R. J Nucl Mater, 1968; 60-70: 386
[2] Kojima S, Satoh Y, Ishida H. Philos Mag, 1989; 59A: 519
[3] Kojima S, Sano Y, Yoshiie T, Yoshida N. J Nucl Mater,1986; 141-143: 571
[4] Takahashi H, Urbovn K. Phys Status Solidi, 1981; 16a:347
[5] Igata N, Kohno Y, Tsunakawa H, Fujihira T. ASTM STP870, 1984: 265
[6] Wilson W V, Baskes M I, Bisson C L. Phys Rev, 1976;13B:2470
[7] Takahashi H, Takeyama T, Ohnuki S, Kato T. In: Taka-mura J, Doyama M, Kiritani M, eds., Point Defeats andDefect Interaction in Metals, New York: ASTM, 1982:861
[8] Zinkle S J, Wolfer W G, Seitzman L E. Philos Mag, 1987;55A: 127
[9] Bourret A. Phys Status Solidi, 1971; 6a: 813
[10] Urban K, Wilkens M. Phys Status Solidi, 1971; 6a: 173
[11] Egata N S. Materials of Fusion Reactors. Tokyo: Ba-fuean, 1986: 131(井形直弘.核融合炉材料.东京:培风馆, 1986:131)
[12] Hu B F, Kinoshita H, Shibayama T, Takahashi H. Metall Mater Trans, 2002; 43: 622

[1]	LIU Wei, CHEN Wanqi, MA Menghan, LI Kailun. Review of Irradiation Damage Behavior of Tungsten Exposed to Plasma in Nuclear Fusion[J]. 金属学报, 2023, 59(8): 986-1000.
[2]	Yucheng WU. Research Progress in Irradiation Damage Behavior of Tungsten and Its Alloys for Nuclear Fusion Reactor[J]. 金属学报, 2019, 55(8): 939-950.
[3]	HUANG Yuan KONG Deyue HE Fang WANG Yulin LIU Wenxi. PREPARATION OF Mo/Ag LAMINAR COMPOSITES BY USING IRRADIATION DAMAGE ALLOYING METHOD[J]. 金属学报, 2012, 48(10): 1253-1259.
[4]	LU Zheng. RADIATION-NDUCED EMBRITTLEMENT AND LIFE EVALUATION OF REACTOR PRESSURE VESSELS[J]. 金属学报, 2011, 47(7): 777-783.
[5]	SUN Chao TAN Jun YING Shihao LI Cong PENG Qian ZHAO Suqiong. PREDICTION OF CRITICAL TEMPERATURE FOR DELAYED HYDRIDE CRACKING IN IRRADIATED N18 ZIRCONIUM ALLOY[J]. 金属学报, 2010, 46(7): 805-809.
[6]	Yong Yu. FORMATION ENERGIES OF POINT DEFFECTS AND HELIUM－VACANCY CLUSTERS IN γ－Fe[J]. 金属学报, 2007, 42(1): 1-5 .
[7]	HU Benfu; HKINOSHITA Hiroshi; SAKAGUCHI Kisiki; TAKAHASHI Heishichiro. Radiation Damage Behavior of Carbide in Long Term Aging Treatmented Low Activation Austenitic Fe-Cr-Mn Alloy[J]. 金属学报, 2006, 42(3): 234-238 .
[8]	WU Zhongcheng; PENG Shuming; YANG Maonian. Calculation Of Diffusion Barriers For Helium Atom In Vanadium By Effective Medium Theory[J]. 金属学报, 2004, 40(1): 36-39 .
[9]	SUN Jiguang;CHEN Chaoqing;ZHANG Xishun (General Research institute for Nonferrous Metals; Beijing 100088)TIAN Yan;SHAN Bingquan;PAN Qingchun (Central Iron & Steel Research institute; Beijing 100081). PROPERTY OF RESISTANCE TO IRRADIATION DAMAGE OF ODS FERRITIC ALLOYS[J]. 金属学报, 1998, 34(11): 1210-1216.
[10]	WAN Farong; HUANG Xuejun; KONG Feng;CHU Wuyang;XIAO Jimei(University of Science and Technology Beijing); TAKAHASHI Heishichiro(Hokkaido University; Japan). BEHAVIOUR OF OXIDE DISPERSION STRENTHENED FERRITIC STEEL UNDER ELECTRON IRRADIATION[J]. 金属学报, 1994, 30(22): 448-452.
[11]	LIANG Gongying;XING Jiandong Xi'an Jiaotong University. A THERMAL ANALYSIS STUDY OF Fe-Cr-Mn HEAT RESISTANT ALLOY[J]. 金属学报, 1991, 27(6): 99-103.
[12]	WAN Farong;XIAO Jimei;YUAN Yi University of Science and Technology Beijing lecturer;Department of Material Physics;University of Science and Technology Beijing; Beijing 100083. MEASUREMENT OF VACANCY MIGRATION ENERGY BY ELECTRON IRRADIATION[J]. 金属学报, 1990, 26(2): 74-78.
[13]	HU Benfu;TAKAHASHI Heishichiro;ITOH Hisatoshi;TAKEYAMA Taro University of Science and Technology Beijing Hokkaido University; Sapporo; Japan Section of Metallography; Department of Materials;University of Science and Technology Beijing; Beijing 100083. BEHAVIOR OF VOID SWELLING AND RADIATION-INDUCED SEGREGATION IN Fe-Cr-Mn ALLOY SYSTEM UNDER ELECTRON IRRADIATION[J]. 金属学报, 1990, 26(1): 1-7.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed