PARTICLE STIMULATED NUCLEATION AND THE FORMATION OF RSCRYSTALLIZATION TEXTURE IN Al-Mn ALLOY CONTAINING PARTICLES Ⅱ. Interaction Between Particles and Other Nucleation Sites and the Formation of Recrystallization Texture
YANG Ping; O.ENGLER(Institute of Metal Science and Metal Physics; Aachen University of Technology; Kopernikusstr. 14; D-52056;Aachen; Germany) Now: School of Materials Science and Engineering; University of Science and Technology Beijing; Beijing;100083 Now: Los Alamos National Laboratory; Center for Materials Science; K765; Los Alamos; NM87545; USACorrespondent: YANG Ping; Tel: (010)62333436; Fax: (010)62332336
Cite this article:
YANG Ping; O.ENGLER(Institute of Metal Science and Metal Physics; Aachen University of Technology; Kopernikusstr. 14; D-52056;Aachen; Germany) Now: School of Materials Science and Engineering; University of Science and Technology Beijing; Beijing;100083 Now: Los Alamos National Laboratory; Center for Materials Science; K765; Los Alamos; NM87545; USACorrespondent: YANG Ping; Tel: (010)62333436; Fax: (010)62332336. PARTICLE STIMULATED NUCLEATION AND THE FORMATION OF RSCRYSTALLIZATION TEXTURE IN Al-Mn ALLOY CONTAINING PARTICLES Ⅱ. Interaction Between Particles and Other Nucleation Sites and the Formation of Recrystallization Texture. Acta Metall Sin, 1998, 34(8): 793-801.
Abstract On the basis of analyzing the subgrain rotations around paricles within deformed matrices and their nucleation, a further investigation of the orientations of grains formed at particles locating at grain boundaries and cube bands was carried out and the formation of recrystallization texture was analyzed. Results reveal that the orientations of the grains at these places retain the orientational features of particle stimulated nucleation within deformed matrices and possess the characteristics of nucleation at grain boundaries or at cube bands. Recrystallization texture is produced by nucleation at different sites.
1 Bleck W, Bunge H J. Acta Metall, 1981; 29: 1401 2 rsund R, Nes E. Scr Metall, 1988; 22: 665 3 Juul Jensen D, Hansen N, Humpherys F J. Acta Metall, 1985; 33: 2155 4 Weiland H, Rouns T N, Liu J. Z Metallkd, 1994; 85: 592 5 Humphreys F J, Ferry M, Johnson C, Pailard P. 16th Ris Inter Sym, Ris National Lab., Denmark1995: 87 6 Johnson C P, Humphreys F J. In: Liang Z et al eds., ICOTOM-11, X'ian, China, 1996: 1263 7 Engler O, Yang P, Kong X. Actd Maten 1996; 44: 3349 8 Nes E, In: Hansen N et al eds., 1st Ris Inter Sym Ris National Lab., Denmark, 1980: 85 9 杨平, Engler 金属学报, 1998; 34: 785(Yang P, Engler O. Acta Metall Sin, 1998; 34: 785) 10 Engler O, Escher C, Gottstein G. Textures Mcrostrvct, 1996; 26: 337 11 Yang P, Engler O. In: Hansen N eds., 16th Ris Inter Symp, Ris National Lab., Denmark, 1995: 595 12 Humphreys F J. In: Hansen N ed., 1st Ris Inter Symp, Ris National Lab., Denmark, 1980: 35 13 Humphreys P J. In: Chandra T ed., Recrystallization'90. The Minerals, Metals & Society 1990: 113