Propagation Behaviors of Small Cracks in Powder Metallurgy Nickel-Based Superalloy FGH4096 |
YANG Qinzheng1, YANG Xiaoguang1,2(), HUANG Weiqing3, SHI Duoqi1,2 |
1.School of Energy and Power Engineering, Beihang University, Beijing 102206, China 2.Beijing Key Laboratory of Aero-Engine Structure and Strength, Beihang University, Beijing 100191, China 3.School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China |
|
Cite this article:
YANG Qinzheng, YANG Xiaoguang, HUANG Weiqing, SHI Duoqi. Propagation Behaviors of Small Cracks in Powder Metallurgy Nickel-Based Superalloy FGH4096. Acta Metall Sin, 2022, 58(5): 683-694.
|
Abstract Inevitable nonmetallic inclusions (NMIs) exist in powder metallurgy (PM) superalloys. These inclusions serve as preferred sites for crack initiation either by fracture of inclusions or inclusion/matrix decohesion. After initiating from NMIs, fatigue cracks will experience the small crack propagation phase. Small fatigue cracks could grow under the fatigue crack growth threshold and propagate at a vibrated rate. To investigate the propagation behavior and reveal the underlying mechanisms, small crack propagation experiments under fatigue loads of different maximum stresses were conducted on PM superalloy FGH4096 using the small fatigue crack-propagation experiment system. The characterization of microstructure was conducted and orientations of grains were calibrated using SEM integrated with EBSD. Focusing on the three-dimensional nature and the physical basis, the propagation and stagnation behavior of small cracks were revealed. Experimental results showed that the small cracks propagated along octahedral slip planes, from initiation to a length even longer than 1.0 mm. During the propagation in the grain-containing twin, small cracks grew along the direction parallel to the twin boundary. However, several twin boundaries impeded crack growth. Small cracks were stagnated at grain and twin boundaries of which M factors were lower than adjacent ones. Three behaviors were observed after the stagnation of small cracks due to the different properties of grain/twin boundaries and the applied load; first, stagnated small cracks could continue to propagate by consuming more cycles; second, small cracks could propagate by alternating to another slip plane in current or other grains on the crack path; third, secondary cracks would initiate within 1-2 grains from the tip of the fully stagnated cracks and connected to the main crack. This behavior was observed only in the specimen in which the maximum stress is close to the lower limit of the yield strength.
|
Received: 21 May 2021
|
|
Fund: National Science and Technology Major Project(2017-IV-0012-0049);National Natural Science Foundation of China(51775019) |
About author: YANG Xiaoguang, professor, Tel: (010)61716792, E-mail: yxg@buaa.edu.cn
|
1 |
Reed R C. The Superalloys: Fundamentals and Applications [M]. Cambridge: Cambridge University Press, 2008: 231
|
2 |
Pollock T M, Tin S. Nickel-based superalloys for advanced turbine engines: Chemistry, microstructure and properties [J]. J. Propul. Power, 2006, 22: 361
doi: 10.2514/1.18239
|
3 |
Chan K S. A fatigue life model for predicting crack nucleation at inclusions in Ni-based superalloys [J]. Metall. Mater. Trans., 2020, 51A: 1148
|
4 |
Texier D, Gómez A C, Pierret S, et al. Microstructural features controlling the variability in low-cycle fatigue properties of alloy Inconel 718DA at intermediate temperature [J]. Metall. Mater. Trans., 2016, 47A: 1096
|
5 |
Jha S K, Caton M J, Larsen J M. A new paradigm of fatigue variability behavior and implications for life prediction [J]. J. Mater. Sci. Eng., 2007, A468-470: 23
|
6 |
Naragani D, Sangid M D, Shade P A, et al. Investigation of fatigue crack initiation from a non-metallic inclusion via high energy X-ray diffraction microscopy [J]. Acta Mater., 2017, 137: 71
doi: 10.1016/j.actamat.2017.07.027
|
7 |
Chang P N. Competing fatigue mechanisms in nickel-base superalloy Rene 88DT [D]. Salt Lake City: The University of Utah, 2011
|
8 |
Zhang Y, Zhang Y W, Zhang N, et al. Fracture character of low cycle fatigue of P/M superalloy FGH97 [J]. Acta Metall. Sin., 2010, 46: 444
doi: 10.3724/SP.J.1037.2010.00444
|
|
张 莹, 张义文, 张 娜 等. 粉末冶金高温合金FGH97的低周疲劳断裂特征 [J]. 金属学报, 2010, 46: 444
|
9 |
Suresh S. Fatigue of Materials [M]. Cambridge: Cambridge University Press, 1998: 541
|
10 |
Milne I, Ritchie R O, Karihaloo B L. Comprehensive Structural Integrity: Cyclic Loading and Fatigue [M]. Amsterdam: Elsevier, 2003: 129
|
11 |
Brown C W, King J E, Hicks M A. Effects of microstructure on long and short crack growth in nickel base superalloys [J]. Met. Sci., 1984, 18: 374
doi: 10.1179/030634584790419881
|
12 |
Caton M J, Jha S K. Small fatigue crack growth and failure mode transitions in a Ni-base superalloy at elevated temperature [J]. Int. J. Fatigue, 2010, 32: 1461
doi: 10.1016/j.ijfatigue.2010.01.015
|
13 |
Pang H T, Reed P. Fatigue crack initiation and short crack growth in nickel-base turbine disc alloys-the effects of microstructure and operating parameters [J]. Int. J. Fatigue, 2003, 25: 1089
doi: 10.1016/S0142-1123(03)00146-4
|
14 |
Naragani D P, Shade P A, Kenesei P, et al. X-ray characterization of the micromechanical response ahead of a propagating small fatigue crack in a Ni-based superalloy [J]. Acta Mater., 2019, 179: 342
doi: 10.1016/j.actamat.2019.08.005
|
15 |
Liu X F. Study on small crack propagation behavior and life prediction of FGH96 powder superalloy [D]. Nanchang: Nanchang Hangkong University, 2019
|
|
刘晓菲. FGH96粉末高温合金疲劳小裂纹扩展行为及寿命预测研究 [D]. 南昌: 南昌航空大学, 2019
|
16 |
Künkler B, Düber O, Köster P, et al. Modelling of short crack propagation-Transition from stage I to stage II [J]. Eng. Fract. Mech., 2008, 75: 715
doi: 10.1016/j.engfracmech.2007.02.018
|
17 |
Lankford J. The influence of microstructure on the growth of small fatigue cracks [J]. Fatigue Fract. Eng. Mater. Struct., 1985, 8: 161
doi: 10.1111/j.1460-2695.1985.tb01201.x
|
18 |
Spangenberger A G, Lados D A, Coleman M, et al. Microstructural mechanisms and advanced characterization of long and small fatigue crack growth in cast A356-T61 aluminum alloys [J]. Int. J. Fatigue, 2017, 97: 202
doi: 10.1016/j.ijfatigue.2016.12.029
|
19 |
He C, Wu Y J, Peng L M, et al. Effect of microstructure on small fatigue crack initiation and early propagation behavior in Mg-10Gd-3Y-0.3Zr alloy [J]. Int. J. Fatigue, 2019, 119: 311
doi: 10.1016/j.ijfatigue.2018.10.002
|
20 |
Panwar S, Adams J F, Allison J E, et al. A grain boundary interaction model for microstructurally short fatigue cracks [J]. Int. J. Fatigue, 2018, 113: 401
doi: 10.1016/j.ijfatigue.2018.04.029
|
21 |
Tao J H, Ji L B, Hu S B. An investigation of the small fatigue crack growth behavior in Ti-6.5Al-2Zr-1Mo-1V alloy [J]. J. Alloys Compd., 2017, 695: 2764
doi: 10.1016/j.jallcom.2016.11.207
|
22 |
Zhang K, Yang K V, Lim S, et al. Effect of the presence of macrozones on short crack propagation in forged two-phase titanium alloys [J]. Int. J. Fatigue, 2017, 104: 1
doi: 10.1016/j.ijfatigue.2017.07.002
|
23 |
Singh R, Singh A, Singh P K, et al. Effect of microstructural features on short fatigue crack growth behaviour in SA508 Grade 3 Class I low alloy steel [J]. Int. J. Press. Vessels Pip., 2020, 185: 104136
|
24 |
Malitckii E, Remes H, Lehto P, et al. Strain accumulation during microstructurally small fatigue crack propagation in bcc Fe-Cr ferritic stainless steel [J]. Acta Mater., 2018, 144: 51
doi: 10.1016/j.actamat.2017.10.038
|
25 |
Schaef W, Marx M, Vehoff H, et al. A 3-D view on the mechanisms of short fatigue cracks interacting with grain boundaries [J]. Acta Mater., 2011, 59: 1849
doi: 10.1016/j.actamat.2010.11.051
|
26 |
Wan V V C, Maclachlan D W, Dunne F P E. Integrated experiment and modelling of microstructurally-sensitive crack growth [J]. Int. J. Fatigue, 2016, 91: 110
doi: 10.1016/j.ijfatigue.2016.05.027
|
27 |
Horstemeyer M F, Farkas D, Kim S, et al. Nanostructurally small cracks (NSC): A review on atomistic modeling of fatigue [J]. Int. J. Fatigue, 2010, 32: 1473
doi: 10.1016/j.ijfatigue.2010.01.006
|
28 |
Simonovski I, Cizelj L. The influence of the grain structure size on microstructurally short cracks [J]. J. Eng. Gas Turbines Power, 2009, 131: 042903
|
29 |
Miao J S, Pollock T M, Wayne Jones J. Microstructural extremes and the transition from fatigue crack initiation to small crack growth in a polycrystalline nickel-base superalloy [J]. Acta Mater., 2012, 60: 2840
doi: 10.1016/j.actamat.2012.01.049
|
30 |
Zhai T, Wilkinson A J, Martin J W. A crystallographic mechanism for fatigue crack propagation through grain boundaries [J]. Acta Mater., 2000, 48: 4917
doi: 10.1016/S1359-6454(00)00214-7
|
31 |
Pineau A. Crossing grain boundaries in metals by slip bands, cleavage and fatigue cracks [J]. Phil. Trans. R. Soc., 2015, 373A: 20140131
|
32 |
Zhang Y Q, Jiang S Y, Zhu X M, et al. Influence of twist angle on crack propagation of nanoscale bicrystal nickel film based on molecular dynamics simulation [J]. Physica, 2017, 87E: 281
|
33 |
Bieler T R, Eisenlohr P, Zhang C, et al. Grain boundaries and interfaces in slip transfer [J]. Curr. Opin. Solid State Mater. Sci., 2014, 18: 212
doi: 10.1016/j.cossms.2014.05.003
|
34 |
Larrouy B, Villechaise P, Cormier J, et al. Grain boundary-slip bands interactions: Impact on the fatigue crack initiation in a polycrystalline forged Ni-based superalloy [J]. Acta Mater., 2015, 99: 325
doi: 10.1016/j.actamat.2015.08.009
|
35 |
Luster J, Morris M A. Compatibility of deformation in two-phase Ti-Al alloys: Dependence on microstructure and orientation relationships [J]. Metall. Mater. Trans., 1995, 26A: 1745
|
36 |
Rovinelli A, Sangid M D, Proudhon H, et al. Predicting the 3D fatigue crack growth rate of small cracks using multimodal data via Bayesian networks: In-situ experiments and crystal plasticity simulations [J]. J. Mech. Phys. Solids, 2018, 115: 208
doi: 10.1016/j.jmps.2018.03.007
|
37 |
Ritchie R O, Lankford J. Small fatigue cracks: A statement of the problem and potential solutions [J]. Mater. Sci. Eng., 1986, 84: 11
doi: 10.1016/0025-5416(86)90217-X
|
38 |
Newman J C, Raju I S. An empirical stress-intensity factor equation for the surface crack [J]. Eng. Fract. Mech., 1981, 15: 185
doi: 10.1016/0013-7944(81)90116-8
|
39 |
Anderson T L. Fracture Mechanics: Fundamentals and Applications [M]. 3rd Ed., Florida: CRC press, 2017: 61
|
40 |
Kacher J, Eftink B P, Cui B, et al. Dislocation interactions with grain boundaries [J]. Curr. Opin. Solid State Mater. Sci., 2014, 18: 227
doi: 10.1016/j.cossms.2014.05.004
|
41 |
Genée J, Signor L, Villechaise P. Slip transfer across grain/twin boundaries in polycrystalline Ni-based superalloys [J]. Mater. Sci. Eng., 2017, A701: 24
|
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|