环氧树脂修饰微米片状Fe粉的制备与电磁性能

董德明; 官建国; 王维; 李维; 周静

武汉理工大学材料复合新技术国家重点实验室; 武汉 430070

PREPARATION AND ELECTROMAGNETIC PROPERTIES OF MICROMETER Fe FLAKES MODIFIED WITH EPOXY RESIN

DONG Deming; GUAN Jianguo; WANG Wei; LI Wei; ZHOU Jing

State Key Laboratory of Advanced Technology for Materials Synthesis and Processing; Wuhan University of Technology;Wuhan 430070

引用本文:

董德明官建国王维李维周静. 环氧树脂修饰微米片状Fe粉的制备与电磁性能[J]. 金属学报, 2009, 45(9): 1141-1145.
, , , , . PREPARATION AND ELECTROMAGNETIC PROPERTIES OF MICROMETER Fe FLAKES MODIFIED WITH EPOXY RESIN[J]. Acta Metall Sin, 2009, 45(9): 1141-1145.

全文: PDF(913 KB)

摘要:

通过γ氨丙基三乙氧基硅烷--双酚A二缩水甘油醚与微米片状Fe粉表面的化学反应, 制备了表面修饰环氧树脂膜的微米片状Fe粉. 用FTIR, SEM, AFM和矢量网络分析仪分析了表面修饰环氧树脂膜的微米片状Fe粉的结构、形貌、表面状态和微波电磁性能. 结果表明, 在微米片状Fe粉表面修饰环氧树脂, 能在其磁导率基本保持不变的前提下显著降低介电常数, 其中虚部降低达到30%-80%以上, 从而明显改善吸波性能.

关键词 ：微米片状Fe粉, 介电常数, 表面改性, 环氧树脂

Abstract：

Ferromagnetic metallic flakes show high magnetic permeability in gigahertz frequency due to their large saturation magnetization and the effect of particles shape. However, their permittivity is too large to wave impedance matching and to application as microwave absorbent. In this paper, the surfaces of micrometer Fe flakes were modified by a thin layer of epoxy resin based on the reaction of hydroxyl groups anchored in the surface of Fe flakes with 3-aminopropyltriethoxy silane and diglycidyl ether of bisphenol A. The structure, morphology, surface state and microwave electromagnetic properties of the as-prepared products were characterized by Fourier transformed infrared spectra, scanning electron microscopy, atomic force microscopy, and network analyzer. The results show that compared with the pristine Fe flakes, the Fe flakes modified by a thin layer of epoxy resin exhibit a substantially decreased complex permittivity, particularly the imaginary part decreased by 30%-80%, but remain almost the same magnetic permeability, which is an absorber with excellent microwave absorbing properties. At the same time, the surface modification mechanism was prosposed. Compared with traditional core-shell modification, the method presented is effective for continuously tuning permittivity of electromagnetic wave absorbents.

Key words： micrometer Fe flake permittivity surface modification epoxy resin

收稿日期: 2009-02-16

ZTFLH:

TB34

基金资助:

国家高技术研究发展计划项目2006AA03A209和霍英东青年教师基金项目101049资助

作者简介: 董德明, 男, 1984年生, 硕士生

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	董德明
	官建国
	王维
	李维
	周静
44.8K

链接本文:

https://www.ams.org.cn/CN/ 或 https://www.ams.org.cn/CN/Y2009/V45/I9/1141

[1] Yoshida S, Sato M, Sugawara E, Shimada Y. J Appl Phys, 1999; 35: 4636
[2] Hashimoto O, Takase Y, Haga S. Trans IEICE Jpn, 2003; 86B: 113
[3] Smit J, Wijn H P J. Ferrites. Eindhoven: Philips Technical Library, 1959: 78
[4] Naito Y, Suetake K. IEEE Trans Microwave Theory Technol, 1971; 19: 65
[5] Zhang X N. PhD Thesis, Beijing University of Technology, 2003
(张晓宁. 北京工业大学博士学位论文, 2003)

[6] Nie Y, He H H, Zhao Z S, Gong R Z, Yu H B. J Magn Magn Mater, 2006; 306: 125
[7] Xie J L, Lu C L, Deng L J. Acta Mater Compos Sin, 2007; 24: 18
(谢建良, 陆传林, 邓龙江. 复合材料学报, 2007; 24: 18)

[8] Wang Q, Guan J G, Liu Q, Wang W, Zhang Q J. J Alloy Compd, 2006; 413: 155
[9] Tong G X,Wang W, Guan J G, Zhang Q J. J InorgMater, 2006; 21: 1461
(童国秀, 王维, 官建国, 张清杰. 无机材料学报, 2006; 21: 1461)

[10] Jiang M J, Dang Z M, Yao S H, Bai J B. Chem Phys Lett, 2008; 457: 352
[11] Zhang Q Y, Zhang H P, Xie G, Zhang J P. J Magn Magn Mater, 2007; 311: 140
[12] Jiang M J, Dang Z M, Xu H P. Eur Polym J, 2007; 43: 4924
[13] Li H Y, Wang R G, Hu H L, Liu W B. Appl Surf Sci, 2008; 255: 1984
[14] Mittal V, Herle V. J Colloid Interface Sci, 2008; 327: 295
[15] Dash S, Mishra S, Patel S, Mishra B K. Adv Colloid Interface, 2008; 140: 77
[16] Vrkoslav V, Jel´?nek I, Trojan T, Jindˇrich J, Dian J. Physica, 2007; 38E: 200
[17] Walser R M, KangW. IEEE Trans Magn, 1998; 34: 1144
[18] Musal H M, Hahn H T. IEEE Trans Magn, 1989; 25: 3851

[1]	高晗, 刘力, 周笑宇, 周心怡, 蔡汶君, 周泓伶. Ti6Al4V表面微纳结构的制备及生物活性[J]. 金属学报, 2023, 59(11): 1466-1474.
[2]	崔振铎, 朱家民, 姜辉, 吴水林, 朱胜利. Ti及钛合金表面改性在生物医用领域的研究进展[J]. 金属学报, 2022, 58(7): 837-856.
[3]	张二林, 王晓燕, 憨勇. 医用多孔Ti及钛合金的国内研究现状[J]. 金属学报, 2017, 53(12): 1555-1567.
[4]	于振涛, 余森, 程军, 麻西群. 新型医用钛合金材料的研发和应用现状[J]. 金属学报, 2017, 53(10): 1238-1264.
[5]	林潇, 葛隽, 吴水林, 刘宝华, 杨惠林, 杨磊. 兼具成骨和抗感染性能的医用金属材料研究进展[J]. 金属学报, 2017, 53(10): 1284-1302.
[6]	罗新民, 王翔, 陈康敏, 鲁金忠, 王兰, 张永康. 激光冲击诱导的航空铝合金表层高熵结构及其抗蚀性[J]. 金属学报, 2015, 51(1): 57-66.
[7]	罗新民,陈康敏,张静文,鲁金忠,任旭东,罗开玉,张永康. 纯Al和铝合金激光冲击表面改性的位错机制[J]. 金属学报, 2013, 49(6): 667-674.
[8]	张锋刚朱小鹏王明阳雷明凯. 强流脉冲离子束辐照WC-Ni硬质密封材料表面改性研究[J]. 金属学报, 2011, 47(7): 958-964.
[9]	冷崇燕周荣张旭卢德宏刘洪喜. Ag和Ta离子双注入改善Ti6Al4V合金耐磨性能[J]. 金属学报, 2009, 45(6): 764-768.
[10]	王旭; 张俊善; 雷明凯 . 强流脉冲离子束辐照对316L不锈钢表面改性的实验研究[J]. 金属学报, 2007, 43(4): 393-398 .
[11]	梅显秀; 马腾才 . 强流脉冲离子束辐照W6Mo5Cr4V2高速钢表面改性研究[J]. 金属学报, 2003, 39(9): 926-931 .
[12]	武高辉; 于志强; 孙东立; 姜龙涛 . 亚微米Al2O3颗粒表面稀土改性及其对6061 Al复合材料时效行为的影响[J]. 金属学报, 2003, 39(8): 870-874 .
[13]	李伟; 宋春花; 包鹏; 马骏; 朱劲松; 王业宁 . 复合体材料CuFe2O4－Pb（Mg1／3Nb2／3）O3的内耗和介电损耗[J]. 金属学报, 2003, 39(11): 1197-1200 .
[14]	熊华平; 李晓红; 毛唯; 李建平; 马文利; 程耀永 . 表面渗硅处理提高钛铝基合金高温抗氧化性[J]. 金属学报, 2003, 39(1): 66-70 .
[15]	汪雨荻; 周和平; 乔梁; 金海波; 傅仁利 . AlN/聚乙烯复合材料的介电性能[J]. 金属学报, 2001, 37(1): 109-112 .

Viewed

Full text

Abstract

Cited

Shared

Discussed