金属学报  2007, Vol. 43 Issue (3): 311-314

论文 本期目录 | 过刊浏览 |

Fe-Al合金中与Al反位置原子弛豫有关的内耗峰

孙蔚 韩福生 吴杰

浙江工贸职业技术学院; 温州325003

The internal friction peak correlated to the relaxation of Al antisite atoms in Fe-Al alloys

SUN Wei

Zhejiang Industry and Trade Polytechnic College; Wenzhou 325003

孙蔚; 韩福生; 吴杰 . Fe-Al合金中与Al反位置原子弛豫有关的内耗峰[J]. 金属学报, 2007, 43(3): 311-314 .
, , . The internal friction peak correlated to the relaxation of Al antisite atoms in Fe-Al alloys[J]. Acta Metall Sin, 2007, 43(3): 311-314 .

摘要 参考文献 相关文章 Metrics 全文: PDF(625 KB)   摘要: 利用内耗方法对Fe-Al合金中Al反位置原子的运动特征进行了研究。在410℃附近观察到了一个与合金热历史相关的弛豫型内耗峰，在快冷样品中内耗峰高度明显高于慢冷样品，而对于快冷样品，升温测量时内耗峰高度又明显高于随后的降温测量，这表明该内耗峰与快冷时残留的缺陷有关。由于该内耗峰激活能为1.88eV，与B2 Fe-Al合金中Fe空位的迁移能相当，因此该峰应产生于应力诱导下Al反位置原子在Fe空位之间的运动。 关键词 ： B2,  FeAl合金,  内耗,  Fe空位,  Al反位置原子     Abstract：Internal friction behavior of Fe-Al alloys was examined to understand the motion of Al antisite atoms. A relaxational internal friction peak was observed at about 410℃ that was dependent on the thermal histories of the alloy. The peak height is much higher in the rapidly cooled specimens than in the slowly cooled ones, and similarly, it is much higher in heating than in subsequent cooling for the rapidly cooled specimens. It is therefore suggested that the peak should be related to retained defects due to rapid cooling. In terms of the activation energy of the peak, that is 1.88eV, comparable to the migration energy of the Fe vacancy, it is proposed that the peak originates from the stress-induced movement of Al antisite atoms between Fe vacancies. Key words： B2 Fe-Al alloys    internal friction    Fe vacancies 收稿日期: 2006-07-14      ZTFLH:  TG113   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 孙蔚 韩福生 吴杰 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y2007/V43/I3/311 [1]de Diego N,Plazaola F,Jimnez J A,Serna J,R(?)o J D. Acta Mater,2005;53:163 [2]Deevi S C,Sika V K.Intermetallics,1996;4:357 [3]Wolff J,Franz M,Broska A,Kerl R,Weinhagen M,K(?)hler B,Brauer M,Faupel F,Hehenkamp Th.Intermetallics, ??1999;7:289 [4]Chang Y A,Pike L M,Liu C T,Bilbrey A R,Stone D S. Intermetallics,1993;1:107 [5]Schaefer H-E,Frenner K,W (?) rshum R.Phys Rev Lett, 1999;82:948 [6]W(?)rshum R,Grupp C,Schaefer H E.Phys Rev Lett,1995; 75:97 [7]Schaefer H E,Damson B,Weller M,Arzt E,George E P. Phys Status Solidi,1997;160a:531 [8]Blanter M S,Golovin I S,Sinning H R.Scr Mater,2005; 52:57 [9]Golovin I S,Divinski S V,(?)ek J,Procházka I,Stein F. Acta Mater,2005;53:2581 [10]Han F S,Zhu Z G,Gao J C.Metall Mater Trans,1999; 30 A:771 [11]Nowick A S,Berry B S.Anelastic Relaxation in Crys- talline Solids.New York:Academic Press,1972 [12]Bevington P R.Data Reduction and Error Analysis for the Physical Science.New York:McGraw-Hill,1969:235 [13]Kubaschewski O.Iron-Binary Phase Diagrams.Berlin: Springer,1982 [14]Fu C L.Phys Rev,1995;52B:3151 [15]Fu C L,Ye Y Y,Yoo M H,Ho K M.Phys Rev,1993;48 B:6712 [16] Wu J,Han F S,Gao Z Y,Hao G L,Wang Q Z.Phys Status Solidi,2006;203a:485 [17]Haraguchi T,Yoshimi K,Yoo M H,Kato H,Hanada S, Inoue A.Acta Mater,2005;53:3751 [18]Zhou Z C,Han F S,Gao Z Y.Acta Mater,2004;52:4049 [19]Kogachi M,Haraguchi T.Mater Sci Eng,1997;A230:124 [20]Lang H,Rohrhofer K,Rosenkranz P,Kozubski R,P(?)schl W,Pfeiler W.Intermetallics.2002;10:283 [1] 刘仁慈, 王鹏, 曹如心, 倪明杰, 刘冬, 崔玉友, 杨锐. 700℃热暴露对 β 凝固 γ-TiAl合金表面组织及形貌的影响[J]. 金属学报, 2022, 58(8): 1003-1012. [2] 丛鸿达, 王金龙, 王成, 宁珅, 高若恒, 杜瑶, 陈明辉, 朱圣龙, 王福会. 新型无机硅酸盐复合涂层制备及其在高温水蒸气环境的氧化行为[J]. 金属学报, 2022, 58(8): 1083-1092. [3] 张丽丽, 江鸿翔, 赵九洲, 李璐, 孙倩. 溶质Ti对Al-Ti-B中间合金细化Al影响的新认识：TiB2粒子的动力学行为及溶质Ti的影响[J]. 金属学报, 2017, 53(9): 1091-1100. [4] 李克俭,蔡志鹏,吴瑶,潘际銮. FB2马氏体耐热钢在焊接热作用下奥氏体相变过程研究[J]. 金属学报, 2017, 53(7): 778-788. [5] 李克俭,蔡志鹏,李轶非,潘际銮. FB2马氏体耐热钢中Laves相在焊接过程中演化行为的研究*[J]. 金属学报, 2016, 52(6): 641-648. [6] 李维娟, 张恒毅, 付豪, 张建平, 戚翔宇. 低碳钢烘烤硬化机制的内耗研究[J]. 金属学报, 2015, 51(4): 385-392. [7] 沈勇,徐坚. Zr46.9Cu45.5Al5.6Y2.0金属玻璃含B2-CuZr相内生复合材料的制备及其力学性能*[J]. 金属学报, 2015, 51(11): 1407-1415. [8] 王华 史文 何燕霖 符仁钰 李麟. Mn和P在超低碳烘烤硬化钢中的分布形态及对其拉伸行为的影响研究[J]. 金属学报, 2011, 47(3): 263-268. [9] 柯常波 马骁 张新平. 孔隙对NiTi形状记忆合金中B2-R相变影响的相场模拟[J]. 金属学报, 2011, 47(2): 129-139. [10] 吴杰 崔洪芝 迟静 姚树玉 韩福生. B2 Fe-Al合金有序化过程中的内耗峰[J]. 金属学报, 2009, 45(4): 396-399. [11] 张建; 李秀艳; 赵明久; 戎利建 . 晶界相对Fe-Ni-Cr奥氏体合金氢脆的影响[J]. 金属学报, 2008, 44(9): 1095-1098 . [12] 栾卫志; 姜传海; 王浩伟 . TiB2/6351Al复合材料喷丸层再结晶过程X射线衍射分析[J]. 金属学报, 2008, 44(6): 671-674 . [13] 吕鹏; 茹红强; 喻亮; 刘立显; 孙旭东 . TiB2含量对B4C--TiB2--Al复合材料组织[J]. 金属学报, 2008, 44(3): 314-318 . [14] 彭志坚; 杨义勇; 王成彪; 付志强 . Bi2O3与Sb2O3掺杂对ZnO力学性能的影响[J]. 金属学报, 2008, 44(10): 1265-1270 . [15] 闫世成; 闫果; 卢亚锋; 刘春芳; 周廉 . 原始Mg粉形状对Mg-B体系成相行为的影响[J]. 金属学报, 2007, 43(4): 358-362 . Viewed Full text Abstract Cited   Shared      Discussed