金属学报  2004, Vol. 40 Issue (1): 99-102

论文 本期目录 | 过刊浏览 |

[013]取向Cu单晶体在NaCl水溶液中腐蚀疲劳位错结构的观察

杨继红;贾维平;李守新

沈阳师范大学物理系

Observation Of The Dislocation Structure In [013] Copper Single Crystal During Corrosion Fatigue In Nacl Aqueous Solution

YANG Jihong;JIA Weiping; LI Shouxin

Department of Physics; Shenyang Normal University

杨继红; 贾维平; 李守新 . [013]取向Cu单晶体在NaCl水溶液中腐蚀疲劳位错结构的观察[J]. 金属学报, 2004, 40(1): 99-102 .
, , . Observation Of The Dislocation Structure In [013] Copper Single Crystal During Corrosion Fatigue In Nacl Aqueous Solution[J]. Acta Metall Sin, 2004, 40(1): 99-102 .

摘要 参考文献 相关文章 Metrics 全文: PDF(312 KB)   摘要: 利用扫描电镜电子通道衬度技术(SEM--ECC)和透射电子显微镜(TEM)对[013]取向Cu单 晶体在空气中和NaCl水溶液中疲劳到饱和的位错结构进行观察. 结果表明: 在0.5mol/L NaCl 水溶液中, 腐蚀疲劳饱和位错结构主要是迷宫和脉络位错结构, 这与空气中的驻留滑移带 (PSBs)和脉络位错结构不同. 腐蚀疲劳饱和位错结构的观察表明, 介质对疲劳位错结构的影响相当于在其它条件都不变的情况下, 增大了疲劳的塑性切应变幅. 关键词 ： Cu单晶体,  腐蚀疲劳     Abstract：The saturation dislocation microstructures in a [013] orientated coppersingle crystal during fatigue in air and NaCl aqueous solutionwere observed by electron channelingcontrast (ECC) technique in SEM and TEM. The resultsshow that the saturation dislocationstructure during the corrosion fatigue in the aqueous solution of 0.5 mol/L NaCl mainly consists of labyrinth and veins dislocation structures, which differs from the dislocation structures of the PSBs and veins in the air environment. The observation reveals that the influence of environment for fatigued dislocation structures is equivalent to increase the plastic shear strain amplitude to the fatigued sample when other conditions are identical. Key words： copper single crystal    corrosion fatigue 收稿日期: 1900-01-01      ZTFLH:  TG171   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 杨继红 贾维平 李守新 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y2004/V40/I1/99 [1] Laird C, Charsley P, Mugrabi H. Mater Sci Eng, 1986; 81A: 433 [2] Basinski Z S, Basinski S J. Progr Mater Sci, 1992: 36: 89 [3] Yang J H, Li Y, Li S X, Ma C X, Li G Y. Mater Sci Eng, 2001; 299A: 51 [4] Yang J H, Li Y, Cai Z, Li S X, Ma C X, Ke W. Mater Sci Eng, 2003; 345A: 164 [5] Yang J H, Li S X, Li Y, Han E H, Zhu Z Y, Ke W. Progr Nature Sci, 2002; 12(6) : 454 [6] Yang J H, Li Y, Li S X, Ma C X, Li G Y. Acta Metall Sin, 2000; 36: 1015(杨继红,李勇,李守新,马常祥,李广义.金属学报,2000;36:1015) [7] Yang G H, Ma C X, Li S X. J Northeastern Univ, 2001; 22: 229(杨继红,马常祥,李守新.东北大学学报,2001,22:229) [8] Yang J H, Li Y, Li S X, Ma C X, Li G Y, Wang G, Ke W. Acta Metall Sin, 2001, 37: 507(杨继红,李勇,李守新,马常祥,王刚,柯伟.金属学报,2001;37:507) [9] Yang J H, Li S X, Han E H, Ke W, Zhu Z Y, Li Y, Cai Z. Progr Nature Sci, 2002; 12:77(杨继红,李守新,韩恩厚,柯伟,朱自勇,李勇,蔡正.自然科学进展,2002;12:77) [10] Basinski Z S, Korbel A S, Basinski S J. Acta Metall, 1980; 28: 191 [11] Mughrabi H. Acta Metall, 1983; 31: 1367 [12] Ackermann F, Kubin L P, Lepinoux J, Mughrabi H. Acta Metall, 1984; 32: 715 [13] Hahn H N, Duquette D J. Acta Metall, 1978; 26: 279 [14] Yah B D, Farrington G C, Laird C. Acta Metall, 1985; 33: 1533． [15] Yan B D, Farrington G C, Laird C. Acta Metall, 1985; 33: 1593． [16] Yan B D, Farrington, G C, Laird C. Metall Trans, 1985; 16A: 1151 [17] Ortner S, Laird C, Farrington G C. Acta Metall, 1987; 35: 453 [18] Ortner S, Laird C, Farrington G C. Acta Metall, 1987; 35: 867 [19] Mughrabi H. Mater Sci Eng, 1978; 33: 207 [20] Woods P J. Philos Mag, 1973; 28: 155 [21] Winter A T. Philos Mag, 1974; 29: 719 [22] Finney J M, laird C. Philos Mag, 1975; 31: 339． [1] 谭季波, 王翔, 吴欣强, 韩恩厚. 316LN不锈钢管状试样高温高压水的腐蚀疲劳行为[J]. 金属学报, 2021, 57(3): 309-316. [2] 郭巍巍,齐成军,李小武. 共轭和临界双滑移取向Cu单晶体疲劳位错结构的热稳定性研究*[J]. 金属学报, 2016, 52(6): 761-768. [3] 吴欣强, 谭季波, 徐松, 韩恩厚, 柯伟. 核级低合金钢高温水腐蚀疲劳机制及环境疲劳设计模型[J]. 金属学报, 2015, 51(3): 298-306. [4] 郭巍巍,齐成军,李小武. 一个共面双滑移取向Cu单晶体疲劳位错结构的热稳定性研究[J]. 金属学报, 2013, 49(1): 107-114. [5] 吴欣强 徐松 韩恩厚 柯伟. 核级不锈钢高温水腐蚀疲劳机制及环境疲劳设计模型[J]. 金属学报, 2011, 47(7): 790-796. [6] 韩恩厚. 核电站关键材料在微纳米尺度上的环境损伤行为研究------进展与趋势[J]. 金属学报, 2011, 47(7): 769-776. [7] 常; 红; 韩恩厚; 王俭秋; 柯伟 . 阴极极化对LY12CZ铝合金腐蚀疲劳寿命的影响[J]. 金属学报, 2005, 41(5): 556-560 . [8] 方丙炎; 韩恩厚; 王俭秋; 柯伟 . 应变速率对管线钢近中性pH值环境敏感开裂的影响[J]. 金属学报, 2005, 41(11): 1174-1182 . [9] 朱荣; 李守新; 李勇; 李明扬; 晁月盛 . Cu单晶体驻留滑移带的形成与消失[J]. 金属学报, 2004, 40(5): 467-470 . [10] 张波; 张正贵 . LY12CZ铝合金铆接联接件在3.5aCl溶液中的腐蚀疲劳失效行为研究[J]. 金属学报, 2000, 36(8): 842-846 . [11] 张波; 李劲 . 应力幅对LY12CZ铝合金腐蚀疲劳应变电流响应的影响[J]. 金属学报, 2000, 36(10): 1089-1093 . [12] 魏学军;李劲;刘素娥;柯伟. 3.5%NaCl中阴极极化下A537钢间歇超载疲劳断口分析[J]. 金属学报, 1998, 34(2): 146-150. [13] 谢建辉;吴荫顺;朱日彰. 植入不锈钢腐蚀疲劳过程中的晶间腐蚀[J]. 金属学报, 1997, 33(3): 304-308. [14] 邢志强;程咏梅;褚武扬. 两种Ti_3Al在水中的低频疲劳研究[J]. 金属学报, 1995, 31(1): 34-39. [15] 李劲;王政富;柯伟. 波型与电位对A537钢疲劳裂纹扩展的影响[J]. 金属学报, 1993, 29(6): 82-87. Viewed Full text Abstract Cited   Shared      Discussed