李帅雨, 刘泽栋, 杨劼人, 金伟, 彭博, 杜新, 周斯曼. TA18合金铸锭-管坯组织遗传行为及力学性能调控[J]. 金属学报, DOI: 10.11900/0412.1961.2025.00364.
, , , , , , . Microstructural Inheritance Behavior and Mechanical Property Control of TA18 Alloy From Ingot to Tube Blank#br#[J]. Acta Metall Sin, 0, (): 0-.

摘要 相关文章 Metrics 全文: PDF(2172 KB)   摘要: 微观组织遗传性是实现TA18合金微观组织和性能调控的基础。本工作以TA18合金铸锭、不同规格锻棒、挤压管坯为研究对象，研究了从铸锭到管坯全流程中微观组织和织构演变的遗传规律，及其对力学性能的影响，旨在为多尺度微观组织和性能的一体化控制提供指导。结果表明，从铸锭到管坯全流程，其组织遗传特征主要分为三类。(1) 微米级晶粒尺寸和等轴α相组织形貌在粗锻阶段建立后，在后续工序中被稳定遗传，晶粒细化是轴向抗拉强度从400 MPa提升至550 MPa以及延伸率提高的基础。(2) 小角度晶界(LAGB)含量的遗传则呈现动态演化。粗锻与精锻阶段的高LAGB含量遗传贡献了加工硬化，但损害塑性；挤压阶段通过完全再结晶实现LAGB低含量遗传，塑性得以恢复。(3) 晶体学织构的遗传受多重因素控制。铸锭中心区域的{0001}∥AD (轴向)基面织构与1010∥AD织构在后续加工过程中被强烈遗传，且1010∥AD织构强度持续增加；α相的c轴取向随工艺发生受控演变：粗锻后呈随机分布，精锻后转为径向织构，挤压后则形成周向织构。TA18合金通过原始组织的晶体取向、变形、动态再结晶机制的竞争与协同，耦合控制晶体学取向的遗传与演化，可通过对有益遗传(细晶、有利织构)的强化与有害遗传(高含量LAGB、不利织构)的阻断进行一体化设计，获得兼具高强度与良好塑性的TA18合金管坯。 关键词 ： TA18合金,  组织遗传,  织构,  力学性能调控     Abstract：In metallic material processing, the microstructural and textural characteristics developed during each manufacturing stage establish the structural foundation for subsequent processing operations, creating substantial hereditary effects throughout the multistage manufacturing chain. This progressive, cross-process accumulation of microstructural and textural evolution makes precise tracing and effective control of microstructural inheritance pathways particularly complex during full-scale manufacturing from the initial ingot to the final TA18 tube blank. Microstructural inheritance forms the basis for structural design and property optimization in TA18 alloys. This investigation employed a 700-mm diameter TA18 alloy ingot as the starting material. The thermomechanical processing route comprised three stages: initial multipass forging in the β-phase field (1150℃–950℃) followed by forging in the α+β phase field at 900℃ to produce a 170-mm diameter rough-forged bar; subsequent processing of the rough-forged bar in the two-phase region at 850°C to obtain a 125-mm diameter finish-forged bar; finally, peeling, drilling, and canned hot extrusion of the finish-forged bar to fabricate tube blanks with inner and outer diameters of 28 and 42 mm, respectively. This study systematically investigates the hereditary evolution of microstructure and texture throughout the processing route from ingot to tube blank in the TA18 alloy and evaluates its impact on mechanical properties to guide the integrated control of multiscale microstructure and performance. The results demonstrate that microstructural hereditary characteristics can be categorized into three primary types. (1) Once established during rough forging, the micron-scale grain size and equiaxed α-phase morphology remain stably inherited in subsequent processing stages. Grain refinement serves as the fundamental basis for increasing axial tensile strength from 400 to 550 MPa and improving elongation. (2) The inheritance of low-angle grain boundary (LAGB) content exhibits dynamic evolution. The high content inherited during the rough- and finish-forging stages contributes to work hardening but negatively affects plasticity; in contrast, the low content inherited after extrusion, achieved via complete recrystallization, results in plasticity recovery. (3) The inheritance of crystallographic texture is governed by multiple competing mechanisms. The {0001}∥axial direction (AD) basal texture and the1010∥AD texture originating from the central region of the ingot are strongly inherited during subsequent processing, with the intensity of the1010∥AD texture continuously increasing. The c-axis orientation of the α-phase undergoes controlled evolution during processing: it is randomly distributed after rough forging, transforms into a radial texture after finish forging, and finally develops into a circumferential texture after extrusion. The TA18 alloy controls the inheritance and evolution of crystallographic orientation through the competition and synergy of various mechanisms, including initial crystallographic orientation, deformation, and dynamic recrystallization. The integrated design of TA18 alloy tube blanks, possessing high strength and good plasticity can be achieved by reinforcing beneficial hereditary features (such as fine grains and favorable texture) and interrupting harmful features (such as high LAGB content and unfavorable texture). 收稿日期: 2025-11-12      基金资助:高性能钛合金无缝管产业化关键共性技术开发与应用(2023YFB3710700) 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 李帅雨 刘泽栋 杨劼人 金伟 彭博 杜新 周斯曼 44.8K 链接本文: https://www.ams.org.cn/CN/10.11900/0412.1961.2025.00364      或      https://www.ams.org.cn/CN/Y0/V/I/0 [1] 常松涛, 张芳, 沙玉辉, 左良. 晶界偏聚元素Sb作用下无取向硅钢织构的空间分布与演变机制[J]. 金属学报, 2026, 62(4): 627-635. [2] 赵子博, 谭海兵, 张博华, 刘玉敬, 刘建荣, 郭会明, 曾卫东, 田伟, 王清江. 综述：近 α 型和 α + β 两相钛合金的微织构[J]. 金属学报, 2026, 62(2): 275-288. [3] 谭若涵, 宋永锋, 陈超, 李丹, 成庶, 李雄兵. 增材制造钛合金等效弹性张量的细观力学建模与实验研究[J]. 金属学报, 2025, 61(9): 1438-1448. [4] 吴泽威, 颜俊雄, 胡励, 韩修柱. 双峰分离非基面织构AZ31镁合金板材反常中温轧制变形行为及机理[J]. 金属学报, 2025, 61(8): 1165-1173. [5] 徐小严, 方超, 邱建科, 张蒙蒙, 史栋刚, 马英杰, 雷家峰, 杨锐. 峰值应力对Ti6242压气机盘锻件室温保载效应的影响[J]. 金属学报, 2025, 61(8): 1141-1152. [6] 游云翔, 谭力, 高静静, 周涛, 周志明. 利用热轧制-剪切-弯曲工艺及退火调控Mg-Al-Zn-Mn-Ca 镁合金的织构[J]. 金属学报, 2025, 61(6): 866-874. [7] 赵焯雅, 孟令健, 林鹏, 曹晓卿. TC4钛合金跨相区连续热压缩 α 相组织演变规律及织构形成机理[J]. 金属学报, 2025, 61(5): 717-730. [8] 周小卫, 郭云, 荆雪艳, 王宇鑫. 仿生苍耳球冠织构的Ni-Co-Zn超疏水合金涂层及其抗覆冰性能[J]. 金属学报, 2025, 61(5): 783-796. [9] 齐敏, 王倩, 马英杰, 曹贺萌, 黄森森, 雷家峰, 杨锐. Ti6246钛合金 β → α 相变中晶界 α 相生长行为及其对微织构的影响[J]. 金属学报, 2025, 61(2): 265-277. [10] 王子彧, 陈志勇, 王新, 王清江. Ti2AlNb薄板的织构及其对拉伸性能各向异性的影响[J]. 金属学报, 2025, 61(11): 1625-1637. [11] 颜孟奇, 吴泽浩, 佟健博, 黄利军, 黄驿胜. TC18钛合金大尺寸 β 晶粒制备及典型织构对力学性能的影响[J]. 金属学报, 2025, 61(10): 1555-1566. [12] 朱桂杰, 王思清, 查敏, 李眉娟, 孙凯, 陈东风. 稀土元素Ce对挤压态Mg-0.3Al-0.2Ca-0.5Mn合金板材体织构及力学各向异性的影响[J]. 金属学报, 2024, 60(8): 1079-1090. [13] 汪丽佳, 胡励, 苗天虎, 周涛, 何曲波, 刘相果. 预变形对双峰分离非基面织构AZ31镁合金板材室温力学行为及微观组织演变的影响[J]. 金属学报, 2024, 60(7): 881-889. [14] 杨杰, 黄森森, 尹慧, 翟瑞志, 马英杰, 向伟, 罗恒军, 雷家峰, 杨锐. 航空用TC21钛合金变截面模锻件的显微组织和力学性能不均匀性分析[J]. 金属学报, 2024, 60(3): 333-347. [15] 杨平, 马丹丹, 顾晨, 顾新福. 初始组织及冷轧压下量对工业低牌号电工钢相变织构及磁性能的影响[J]. 金属学报, 2024, 60(3): 377-387. Viewed Full text Abstract Cited   Shared      Discussed