金属学报  1998, Vol. 34 Issue (10): 1049-1054

论文 本期目录 | 过刊浏览 |

冷轧变形对Inconel 718合金δ相析出动力学的影响

刘文昌;陈宗霖;肖福仁;姚枚;王少刚;刘润广

燕山大学材料工程学院;秦皇岛;066004;哈尔滨工业大学材料学院;哈尔滨;150001;沈阳黎明发动机制造公司;沈阳;110043;燕山大学材料工程学院;秦皇岛;066004;燕山大学材料工程学院;秦皇岛;066004;沈阳黎明发动机制造公司;沈阳;110043;哈尔滨工业大学材料学院;哈尔滨;150001

EFFECT OF COLD ROLLING ON THE KINETICS OF δ PHASE PRECIPITATION IN INCONEL 718

LIU Wenchang; CHEN Zonglin; XIAO Furen; YAO Mei; WANG Shaogang;LIU Runguang(College of Material Engineering; Yanshan University; Qinhuangdao 066004);(Shenyang Liming Engine Manufacturing Company; Shenyang 110043);(School of Materials Engineering; Harbin Institute of Technology; Harbin 150001)Correspondent:LIU Wenchang;associate professor; Tel: (0335)8057047

刘文昌;陈宗霖;肖福仁;姚枚;王少刚;刘润广. 冷轧变形对Inconel 718合金δ相析出动力学的影响[J]. 金属学报, 1998, 34(10): 1049-1054.
, , , , , . EFFECT OF COLD ROLLING ON THE KINETICS OF δ PHASE PRECIPITATION IN INCONEL 718[J]. Acta Metall Sin, 1998, 34(10): 1049-1054.

摘要 参考文献 相关文章 Metrics 全文: PDF(465 KB)   摘要: 采用X射线衍射测定了冷轧Inconel718合金在不同加热条件下的δ相含量，研究了冷轧变形对δ相析出动力学的影响．结果表明，δ相析出的质量分数与时间的关系符合Avrami方程，在加热温度为960℃时，冷轧变形量对时间指数（n）和δ相析出速率（α）的影响不大；低于910℃，随冷轧变形量的增加和加热温度的提高，n值减小而α值增加．δ相的析出速率与加热温度的关系符合Arrhenius方程，随冷轧变形量增加，δ相析出激活能降低，冷轧变形促进γ＂→δ转变，给出了冷轧Inconel718合金δ相等温析出动力学曲线（PTT），随冷轧变形量增加，C曲线向左移动． 关键词 ： Inconel 718合金,  冷轧,  δ相,  析出动力学     Abstract：The mass percentages of δ phase in Inconel 718 cold rolled to different reductionsand then treated at different temperatures for different times were measured by X-ray diffraction,and the effect of cold rolling on the kinetics of δ phase precipitation was investigated. Therelationship between the mass percentage of δ phase and annealing time follows the Avramiequation. At 960℃, cold rolling has a little effect on the time exponent (n) and the rate constantof δ phase (α). Below 910 ℃, as cold rolling reduction and annealing temperature increases, theValue of n decreases, whereas the value of or increases. The relationship between the rate constantof δ phase and temperature follows Arrhenius equation. As cold roiling reduction increases,the apparent activation energy of δ precipitation decreases. Cold rolling promotes the γ" → δtransformation. According to the kinetics of δ precipitation, the precipitation-temperature-time(PTT) curves of δphase were given.It has been found that the C curve shifts left as cold rolling reduction increases. Key words： Inconel 718    cold rolling    δphase    precipitation kinetics 收稿日期: 1998-10-18      基金资助:中国航空工业总公司重点攻关资助!FWS1006 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 刘文昌 陈宗霖 肖福仁 姚枚 王少刚 刘润广 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1998/V34/I10/1049 1 Desvallees Y, Bouzidi M, Bois F, Beaude N. In: Loria E A ed., Superallous 718, 706 and Various Derivatives,Warrendale, PA: TMS, 1994: 281 2 Pieraggi B, Uginet J F. In: Loria E A ed., Supenalloys 718, 625, 706 and Various Derivatives, Warrendale,PA: TMS, 1994: 535 3 Kirman I, Warrington D H. Metoll Trans, 1970; 1: 2667 4 Sundararaman M, Mukhopadhya P, Banerjee S. Metall Trans, 1988; 19A: 453 5 Dong J X, Xie X S, Xu Z C, Zhang S H. In: Loria E A ed., Supenalloys 718, 625 and Varions Derivatives,Warrendale, PA: TMS, 1994: 649 6 Burger J L, Biederman R R, Couts W H. In: Loria E A ed., Speralloy 718-Metallurgy and Applications,Warrendale, PA: TMS, 1989: 207 7 Singh R P, Hyzak J M, Howon T E, Biederman R R. In: Loria E A ed., Sweralloys 718, 625 and VariousDerivatives, Warrendale, PA: TMS, 1991: 205 8 Liu W C, Xiao P R, Yao M, Chen Z L. Scr Mater, 1997; 37: 53 9 刘文昌,姚枚,肖福仁, 陈宗霖.钢铁, 1997; 32(5): 55(Liu W C, Yao M, Xiao F R, Chen Z L. Iron Steel, 1997; 32(5): 55) 10 Liu W C, Xiao F R, Yao M, Chen Z L. J Mater Sci Lett, 1997; 16: 769 11 草开 清志,早川到,大 耕之.铁钢, 1993; 79: 1210(Kusabiraki K, Hayhawa I, Ooka T. Tetsuo Hagane, 1993; 79: 1210) 12 草开清志,新家伸一,大耕之.铁 钢. 1992; 78: 650(Kusabiraki K, Araie S, Ooka T. Tetsuo Hapane, 1992; 78: 650) [1] 王周头, 袁清, 张庆枭, 刘升, 徐光. 冷轧中碳梯度马氏体钢的组织与力学性能[J]. 金属学报, 2023, 59(6): 821-828. [2] 王长胜, 付华栋, 张洪涛, 谢建新. 冷轧变形对高性能Cu-Ni-Si合金组织性能与析出行为的影响[J]. 金属学报, 2023, 59(5): 585-598. [3] 徐磊, 田晓生, 吴杰, 卢正冠, 杨锐. 热等静压成形Inconel 718粉末合金的显微组织和力学性能[J]. 金属学报, 2023, 59(5): 693-702. [4] 于少霞, 王麒, 邓想涛, 王昭东. GH3600镍基高温合金极薄带的制备及尺寸效应[J]. 金属学报, 2023, 59(10): 1365-1375. [5] 唐帅, 蓝慧芳, 段磊, 金剑锋, 李建平, 刘振宇, 王国栋. 铁素体区等温过程中Ti-Mo-Cu微合金钢中的共析出行为[J]. 金属学报, 2022, 58(3): 355-364. [6] 汤雁冰, 沈新旺, 刘志红, 乔岩欣, 杨兰兰, 卢道华, 邹家生, 许静. 激光选区熔化Inconel 718合金在NaOH溶液中的腐蚀行为[J]. 金属学报, 2022, 58(3): 324-333. [7] 李亚敏, 张瑶瑶, 赵旺, 周生睿, 刘洪军. Cu对Inconel 718合金Nb偏析影响机理的第一性原理研究[J]. 金属学报, 2022, 58(2): 241-249. [8] 许坤, 王海川, 孔辉, 吴朝阳, 张战. 一种新分组团簇动力学模型模拟铝合金中的Al3Sc析出[J]. 金属学报, 2021, 57(6): 822-830. [9] 梁孟超, 陈良, 赵国群. 人工时效对2A12铝板力学性能和强化相的影响[J]. 金属学报, 2020, 56(5): 736-744. [10] 蓝春波,梁家能,劳远侠,谭登峰,黄春艳,莫羡忠,庞锦英. 冷轧态Ti-35Nb-2Zr-0.3O合金的异常热膨胀行为[J]. 金属学报, 2019, 55(6): 701-708. [11] 刘后龙,马明玉,刘玲玲,魏亮亮,陈礼清. 热轧板退火工艺对19Cr2Mo1W铁素体不锈钢织构与成形性能的影响[J]. 金属学报, 2019, 55(5): 566-574. [12] 邵成伟, 惠卫军, 张永健, 赵晓丽, 翁宇庆. 一种新型高强度高塑性冷轧中锰钢的组织和力学性能[J]. 金属学报, 2019, 55(2): 191-201. [13] 赵晓丽, 张永健, 邵成伟, 惠卫军, 董瀚. 两相区退火处理冷轧0.1C-5Mn中锰钢的氢脆敏感性[J]. 金属学报, 2018, 54(7): 1031-1041. [14] 王丽娜, 杨平, 李凯, 崔凤娥, 毛卫民. 高锰TRIP钢冷轧以及α'-M逆转变过程的相变和织构演变[J]. 金属学报, 2018, 54(12): 1756-1766. [15] 刘永长, 张宏军, 郭倩颖, 周晓胜, 马宗青, 黄远, 李会军. Inconel 718变形高温合金热加工组织演变与发展趋势[J]. 金属学报, 2018, 54(11): 1653-1664. Viewed Full text Abstract Cited   Shared      Discussed