金属学报  2007, Vol. 43 Issue (11): 1171-1175

论文 本期目录 | 过刊浏览 |

Sr对AZ91D镁合金枝晶生长和相析出的影响

周吉学 汪 彬 童文辉 杨院生

中国科学院金属研究所

Effect of Strontium Addition on Dendrite Growth and Phase Precipitation in AZ91D Magnesium Alloy

ZHOU Jixue; WANG Bin; TONG Wenhui; YANG Yuansheng

Institute of Metal Research; Chinese Academy of Sciences

周吉学; 汪彬; 童文辉; 杨院生 . Sr对AZ91D镁合金枝晶生长和相析出的影响[J]. 金属学报, 2007, 43(11): 1171-1175 .
, , , . Effect of Strontium Addition on Dendrite Growth and Phase Precipitation in AZ91D Magnesium Alloy[J]. Acta Metall Sin, 2007, 43(11): 1171-1175 .

摘要 参考文献 相关文章 Metrics 全文: PDF(1235 KB)   摘要: 研究了微量Sr（0.01-0.1%，质量分数）对AZ91D镁合金枝晶生长和相析出的影响. 结果表明，加入微量Sr可明显细化AZ91D合金晶粒；随着添加量增加，初生相α-Mg枝晶逐渐球化，非平衡析出相β-Mg17A112增多；加入0.1% Sr后，在枝晶间β-Mg17A112相上依附析出针状或杆状Al4Sr新相. AZ91D合金凝固过程中Sr在固液界面前沿富集，并且优先在曲率较大的枝晶端面富集，抑止晶粒长大，从而增加允许形核时间，提高了形核数量，同时Sr的尖端富集降低了初生相α-Mg的尖端生长优势，球化了枝晶组织. 关键词 ： AZ91D镁合金,  锶,  组织细化,  Al4Sr析出相     Abstract：Effects of Sr addition on dendrite growth and phase precipitation of AZ91D alloy was studied. The experimental results showed that addition of 0.01-0.1wt%Sr to AZ91D alloy decreased the grain size obviously and promoted formation of globular grains. With the increase of Sr content the morphology of β-Mg17A112 phase in the alloy was changed and the amount of the phase increased. Meanwhile, the needle-like or pole-like Al4Sr phase adhering to the β-Mg17A112 phase at grain boundaries was observed. The enrichment of Sr element at solidification interface front, especially at the tip of α-Mg dendrite, restricts the growth of α-Mg dendrite and changes the preferential growth of α-Mg, which results in the grain refinement and modification of α-Mg dendrite. Key words： magnesium alloy AZ91D    Sr    grain refinement    Al4Sr precipitation 收稿日期: 2007-02-12      ZTFLH:  TG146   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 周吉学 汪彬 童文辉 杨院生 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y2007/V43/I11/1171 [1]Wislei R O,Celia M F,Amauri G.Mater Sci Eng,2005; A402:22 [2]Wang Y X,Guan S K,Wang J Q.Chin J Nonferrous Met, 2003;13:616 (王迎新，关绍康，王建强．中国有色金属学报，2003；13：616) [3]Bamberger M.Mater Sci Technol,2001;17:15 [4]Lee Y C,Dahle A K,Stjohn D H.Metall Mater Trans, 1999;31A:2895 [5]Flemings M C.Metall Trans,1991;22A:957 [6]Vires C.Met Trans,1992;23B:189 [7]Kumar N V R,Blandin J J,Desrayaud C,Montheillet F, Su(?)ry M.Mater Sci Eng,2003;A359:150 [8]Govind,Nair K S,Mittal M C,Lal K,Mahanti R K, Sivaramakrishnan C S.Mater Sci Eng,2001;304-306A: 520 [9]Cai J,Ma G C,Liu Z,Zhang H F,Hu Z Q.J Alloys Compd,2006;422:92 [10]St John D H,Ma Q,Easton M A,Cao P,Hildebrand Z. Metall Mater Trans,2005;36A:1669 [11]Nussbaum G,Bridot P,Warner T J,Charbonnier J, Regazzoni G.In:Mordike B L,Hehmam F.eds.,Mag- nesium Alloys and Their Applications,Oberursel:DMG Informationsgesellschaft,1992:351 [12]Gruzleski J E,Aliravci C A.U S Pat,No.5143564,1992 [13]Makoto T,Suzuki T,Fukui I.J Jpn Inst Light Met,1979; 29:437 [14]Sasaki H,Adachi M,Sato S.J Jpn Inst Light Met,1997; 47:133 [15]Haitani T,Tamura Y,Yano E.J Jpn Inst Light Met,2001; 51:403 [16]Massalski T B,Okamoto H,Subramanian P R,Kaeprzak L.Binary Alloy Phase Diagrams.2nd ed,Metals Park, OH:ASM International,1990:170 [1] 刘洁, 徐乐, 史超, 杨少朋, 何肖飞, 王毛球, 时捷. 稀土Ce对非调质钢中硫化物特征及微观组织的影响[J]. 金属学报, 2022, 58(3): 365-374. [2] 李根, 兰鹏, 张家泉. 基于Ce变质处理的TWIP钢凝固组织细化[J]. 金属学报, 2020, 56(5): 704-714. [3] 魏恺文,王泽敏,曾晓雁. AZ91D镁合金在激光选区熔化成形中的元素烧损*[J]. 金属学报, 2016, 52(2): 184-190. [4] 祁明凡, 康永林, 周冰, 朱国明, 张欢欢. 强制对流搅拌流变压铸AZ91D镁合金的组织与性能*[J]. 金属学报, 2015, 51(6): 668-676. [5] 吴斯, 李秀程, 张娟, 尚成嘉. Nb对中碳钢相变和组织细化的影响*[J]. 金属学报, 2014, 50(4): 400-408. [6] 贾晓帅,左训伟,陈乃录,黄坚,唐新华,戎咏华. 经新型Q－P－T工艺处理后Q235钢的组织与性能[J]. 金属学报, 2013, 49(1): 35-42. [7] 彭云 王爱华 肖红军 田志凌. Cu对690 MPa级HSLA钢熔敷金属组织形成和细化的作用[J]. 金属学报, 2012, 48(11): 1281-1289. [8] 高古辉 张寒 白秉哲. 回火温度对Mn系低碳贝氏体钢的低温韧性的影响[J]. 金属学报, 2011, 47(5): 513-519. [9] 李龙飞 李伟 孙祖庆 杨王玥. 基于离异共析转变的共析钢组织细化[J]. 金属学报, 2009, 45(6): 704-710. [10] 郑伟超; 李双寿; 汤彬; 曾大本 . 混合稀土对AZ91D镁合金组织和力学性能的影响[J]. 金属学报, 2006, 42(8): 835-842 . [11] 刘生发; 黄尚宇; 徐萍 . Ce对AZ91镁合金铸态组织细化的影响[J]. 金属学报, 2006, 42(4): 443-448 . [12] 周全; 杨院生; 唐军立; 胡壮麒 . 直流电流作用下AZ91D镁合金半固态等温处理过程中的组织演变[J]. 金属学报, 2006, 42(1): 28-34 . [13] 毛卫民; 殷爱美; 钟雪友 . 半固态AZ91D镁合金的压缩变形研究[J]. 金属学报, 2005, 41(5): 539-544 . [14] 廖恒成; 孙国雄 . 铸造Al-Si合金中Sr与B间反应产物的研究[J]. 金属学报, 2003, 39(2): 155-158 . [15] 王学敏; 尚成嘉; 杨善武; 贺信莱 . 组织细化的控制相变技术机理研究[J]. 金属学报, 2002, 38(6): 661-666 . Viewed Full text Abstract Cited   Shared      Discussed