国产锻造态核级管材316L不锈钢在高温高压水中的应力腐蚀裂纹扩展行为 |
张利涛,王俭秋 |
中国科学院金属研究所金属腐蚀与防护国家重点实验室, 沈阳 110016 |
|
STRESS CORROSION CRACK PROPAGATION BEHAVIOR OF DOMESTIC FORGED NUCLEAR GRADE 316L STAINLESS STEEL IN HIGH TEMPERATURE AND HIGH PRESSURE WATER |
ZHANG Litao,WANG Jianqiu |
State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences,Shenyang 110016 |
引用本文:
张利涛,王俭秋. 国产锻造态核级管材316L不锈钢在高温高压水中的应力腐蚀裂纹扩展行为[J]. 金属学报, 2013, 49(8): 911-916.
ZHANG Litao,
WANG Jianqiu.
STRESS CORROSION CRACK PROPAGATION BEHAVIOR OF DOMESTIC FORGED NUCLEAR GRADE 316L STAINLESS STEEL IN HIGH TEMPERATURE AND HIGH PRESSURE WATER[J]. Acta Metall Sin, 2013, 49(8): 911-916.
[1] Han E H. Acta Metall Sin, 2011; 47: 769
(韩恩厚. 金属学报, 2011; 47: 769)
[2] Han E H, Wang J Q, Wu X Q, Ke W. Acta Metall Sin, 2010; 46: 1379
(韩恩厚, 王俭秋, 吴欣强, 柯伟. 金属学报, 2010; 46: 1379)
[3] Lu Z P, Shoji T, Takeda Y, Ito Y, Kai A, Tsuchiya N. Corros Sci, 2008; 50: 625
[4] Meng F J, Lu Z P, Shoji T, Wang J Q, Han E H, Ke W. Corros Sci, 2011; 53: 2558
[5] Lu Z P, Shoji T, Takeda Y, Ito Y, Yamazaki S. Corros Sci, 2008; 50: 698
[6] Xue H, Li Z J, Lu Z P, Shoji T. Corros Sci, 2011; 241: 731
[7] Andresen P L, Briant C L. Corrosion, 1989; 45: 448
[8] Andresen P L. Corrosion, 1991; 47: 917
[9] Andresen P L. Corrosion, 1993; 49: 714
[10] Andresen P L. Corrosion, 1987; 44: 450
[11] Andresen P L, Kim Y J. Corrosion, 2003; 59: 584
[12] Bali S C, Kain V, Raja V S. Corrosion, 2009; 65: 726
[13] Peng Q J, Teysseyre S, Andresen P L, Was G S. Corrosion, 2007; 63: 1033
[14] Arioka K, Yamada T, Terachi T, Chiba G. Corrosion, 2007; 63: 1114
[15] Arioka K, Yamada T, Terachi T, Chiba G. Corrosion, 2006; 62: 568
[16] Byun T S, Hashimoto N, Farrell K. Acta Mater, 2004; 52: 889
[17] Yamazaki S, Lu Z P, Ito Y, Takeda Y, Shoji T. Corros Sci, 2008; 50: 835
[18] Lu Z P, Shoji T, Takeda Y, Ito Y, Yamazaki S. Corrosion, 2007; 63: 1021
[19] Andresen P L, Morra M M. J Nucl Mater, 2008; 383: 97
[20] Peng Q J, Hou J, Sakaguchi K, Takeda Y, Shoji T. Electrochim Acta, 2011; 56: 8375
[21] Andresen P L. Corrosion, 2008; 64: 439
[22] Andresen P L, Hickling J, Ahluwalia A, Wilson J. Corrosion, 2008; 64: 707
[23] Andresen P L, Briant C L. Corrosion, 1989; 45: 448
[24] Andresen P L. Corrosion, 1988; 44: 450
[25] Lu Z P, Shoji T, Takeda Y, Ito Y, Akira K, Tsuchiya N. Corros Sci, 2008; 50: 625 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|