多晶铝轧制变形的织构演变II. 理论模拟
陈志永;才鸿年;常亚喆;张新明;刘楚明
中南大学材料科学与工程学院
TEXTURE EVOLUTION OF POLYCRYSTALLINE ALUMINUM FOR ROLLING DEFORMATION - II. Theoretical Simulation
Zhiyong Chen;;;;
中南大学
引用本文:

陈志永; 才鸿年; 常亚喆; 张新明; 刘楚明 . 多晶铝轧制变形的织构演变II. 理论模拟[J]. 金属学报, 2008, 44(11): 1322-1331 .
, , , , . TEXTURE EVOLUTION OF POLYCRYSTALLINE ALUMINUM FOR ROLLING DEFORMATION - II. Theoretical Simulation[J]. Acta Metall Sin, 2008, 44(11): 1322-1331 .

全文: PDF(910 KB)  
摘要: 

采用Taylor类型多晶体塑性变形模型, 模拟了初始自由分布和近似立方织构多晶铝的轧制织构演变. 应用取向线分析方法将不同模型的理论计算结果进行了系统分析, 并与实测轧制织构进行了比较. 结果表明: 在低轧制变形程度时, 完全限制(FC)模型计算结果的取向分布较其它模型更符合实际结果. 在较高程度轧制变形时, 对于初始自由分布的多晶铝轧制试样, lath模型与实验符合较好;而对于初始具有近似立方织构的样品, 使用混合模型结果较佳.

关键词 多晶铝轧制变形初始织构自由分布    
Abstract

The rolling texture evolution with initial randomly distributed texture and nearly cube texture was simulated by Taylor-type models. A systematic comparison of the theoretical results obtained by the different type models against the experimental rolling textures is performed by orientation line analysis. The results shows that the orientation distribution calculated by the FC Taylor is closer to experimental results than those by other models at the low rolling deformation degree. During the higher deformation degrees, the results by the lath model agree the measured better for the initial randomly distributed texture while the simulated results obtained by the mixed are closer to the measured than those by the other models for initial cube texture.

Key wordspolycrystalline aluminum    rolling deformation    initial texture    random distribution    Taylor model
收稿日期: 2008-02-28     
ZTFLH: 

TG146

 
[1]Chen Z Y,Cai H N Chang Y Z,Zhang X M,Liu C M. Acta Metall Sin,2008;44:1316 (陈志永,才鸿年,常亚喆,张新明,刘楚明.金属学报,2008;44:1316)
[2]Chen Z Y,Zhang X M,Zhou Z P,Li S Y,Yang Y.Trans Nonferrous Met Soc China,1999;9:307
[3]Taylor G I.J Inst Met,1938;62:307
[4]Mecking H.In:Nagashima S,ed.,Proc 6th Int Conf on Textures of Materials,Tokyo:Iron and Steel Institute of Japan,1981:53
[5]Bunge H J,Leffers T.Scr Metall,1971;5:143
[6]Canova G R,Kocks U F.In:Brakman C M,Jongenburger P,Mittemeijer E J,eds.,Proc 7th Int Conf on Textures of Materials,Noordwijkerhout:Netherlands Society of Ma- terials Science,1984:573
[7]Asaro R J,Needleman A.Acta Metall,1985,33:923
[8]Renouard M,Wintenberger M.C R Acad Sci,1976;283B: 237
[9]Honneff H,Mecking H.In:Gottstein G,L(?)cke K,eds., Proc 5th Int Conf on Textures of Materials,Aachen: Springer,1978:265
[10]van Houtte P.In:Nagashima S,ed.,Proc 6th Int Conf on Textures of Materials,Tokyo:Iron and Steel Institute of Japan,1981:428
[11]Kocks U F,Chandra H.Acta Metall,1982;30:695
[12]Fortunier R,Driver J H.Acta Metall,1987;35:509
[13]Hirsch J,L(?)cke K.Acta Metall,1988;36:2883
[14]Sachs E.Z Vet Deut Ing,1928;72:734
[15]Pérocheau F,Driver J H.Int J Plast,2000;16:73
[16]Raabe D,Zhao Z,Mao W.Acta Mater,2002;50:4379
[17]Cao P,Fang G,Lei L P,Zeng P.Acta Metall Sin,2007; 43:913 (曹鹏,方刚,雷丽萍,曾攀.金属学报,2007;43:913)
[1] 曹育菡,王理林,吴庆峰,何峰,张忠明,王志军. CoCrFeNiMo0.2高熵合金的不完全再结晶组织与力学性能[J]. 金属学报, 2020, 56(3): 333-339.
[2] 陈志永; 才鸿年; 常亚喆; 张新明; 刘楚明 . 多晶铝轧制变形的织构演变I. 实验研究[J]. 金属学报, 2008, 44(11): 1316-1321 .
[3] 张新明; 邓运来; 刘瑛; 唐建国; 周卓平 . 不同温度轧制多晶铝的微观组织与晶界分布[J]. 金属学报, 2005, 41(9): 947-952 .