金属学报  2004, Vol. 40 Issue (3): 301-304

论文 本期目录 | 过刊浏览 |

一种新型Nd基块体非晶合金

任英磊;左景辉;邱克强;张海峰;胡壮麒

沈阳工业大学材料科学与工程学院

A New Nd--Based Bulk Metallic Glass

REN Yinglei; ZUO Jinghui;QIU Keqiang; ZHANG Haifeng; HU Zhuangqi

Faculty of Materials Science and Engineering; Shenyang University of Technology

任英磊; 左景辉; 邱克强; 张海峰; 胡壮麒 . 一种新型Nd基块体非晶合金[J]. 金属学报, 2004, 40(3): 301-304 .
, , , , . A New Nd--Based Bulk Metallic Glass[J]. Acta Metall Sin, 2004, 40(3): 301-304 .

摘要 参考文献 相关文章 Metrics 全文: PDF(12327 KB)   摘要: 在铜模铸造条件下制备了直径2.5 mm的Nd61Fe30Zn9块状非晶合金. 在普通DSC 条件下, 没有观察到这种合金的玻璃转变温度, 晶化温度为730 K, 比Nd60Fe30Al10非晶合金的晶化温度低约70 K, 因此该合金的热稳定性较低. 熔化行为分析表明,合金Nd61Fe30Zn9的熔化过程为单峰吸热过程,且熔化区间仅为54 K, 说明该合金的成分接近合金的共晶成分, 但母合金的自然凝固组织不具有共晶凝固特点,表现为粗大的枝晶状组织. 讨论了成分和组织对合金非晶形成能力的影响. 关键词 ： Nd--Fe--Zn块体非晶合金,  形成能力     Abstract：A new Nd61Fe30Zn9 bulk metallic glass with a diameter of 2.5 mm was obtained using copper mold casting. No glass transition temperature or supercooled liquid region was observed by using conventional DSC--7 facility. The crystallization temperature for the bulk sample is 730 K, which is about 70 K lower than that of Nd60Fe30Al10 bulk metallic glass. The melting characteristics of Nd61Fe30Zn9 alloy show that its compositional is at a eutectic point, but the alloys exhibit non--eutectic microstructure due to high tendency of undercooled ability. Key words： Nd--Fe--Zn bulk metallic glass    glass- forming ability 收稿日期: 2003-06-05      ZTFLH:  TB383   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 任英磊 左景辉 邱克强 张海峰 胡壮麒 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y2004/V40/I3/301 [1] Chen H S. Acta Metall, 1974; 22:1505 [2] Inoue A, Nishiyama N, Matsuda T. Mater Trans JIM, 1996; 37:181 [3] Schwarz. R B, He Y. Mater Sci Forum, 1997; 235-238:231 [4] Inoue A, Zhang T, Masumoto T. Mater Trans JIM, 1989; 30:965 [5] Inoue A, Ohtera K, Kita K, Masumoto T. Jpn J appl Phys, 1988; 27:L2248 [6] Inoue A, Zhang T, Masumoto T. Mater Trans JIM, 1990; 31:177 [7] Peker A, Johnson W L. Appl Phys Left, 1993; 63:2342 [8] Inoue A, Shibata, T. Zhang T. Mater Trans JIM, 1995; 36:1420 [9] He Y, Price C, J Pooh S. Philos Mag Let, 1994; 70:371 [10] Zhang T, Inoue A. Mater Trans JIM, 1998; 39:1001 [11] Zhang T, Inoue A. Mater Trans JIM, 1999; 40:301 [12] Inoue A, Zhang T, Zhang W, Takeuchi A. Mater Trans JIM, 1996; 37:99 [13] Inoue A, Zhang T, Takeuchi A, Zhang W. Mater Trans JIM, 1996; 37:636 [14] Inoue A, Takeuchi A, Zhang T. Metall Trans, 1998; A29: 1779 [15] Busch R. JOM, 2002; 52:39 [16] Chen W, Wang Y, Qing J, Dong C. Acta Metall, 2003; 51:1899 [17] Lu Z P, Li Y, Ng S C. J Non-Cryst Solids, 2000; 270:103 [18] Qiu K Q, Zhang Q S, Wang A M, Zhang H F, Ding B Z, Hu Z Q. Acta Metall Sin, 2001; 37:829(邱克强,张庆生,王爱民,张海峰,丁炳哲,胡壮麒.金属学报,2001;37:829) [19] Qiu K Q, Zhang H F, Wang, A M, Ding B Z, Hu Z Q. Acta Metall, 2002; 50:3567 [20] Lu Z P, Li Y, Ng S C, Feng Y P. In: Johnson W L, Inoue A, Liu C T eds, Bulk Metallic Glasses, Pittsburgh, PA: Material Research Society, 1999:205 [21] Guo F Q, Enouf S, Shiflet G, Pooh J. Mater Trans JIM, 2000; 41:1406 [22] Turnbull D M. Contempt Phys, 1969; 10:473 [23] Li Y. Mater Trans JIM, 2001; 42:556 [24] Qiu K Q, Zhang H F, Wang A M, Ding B Z, Hu Z Q. Mater Left (in submitted) [1] 李金富, 李伟. 铝基非晶合金的结构与非晶形成能力[J]. 金属学报, 2022, 58(4): 457-472. [2] 杨群, 彭思旭, 卜庆周, 于海滨. 非晶态Ni80P20合金的玻璃转变和过冷液体性质[J]. 金属学报, 2021, 57(4): 553-558. [3] 黄火根, 张鹏国, 张培, 王勤国. U-Co与U-Fe基础体系非晶形成能力的比较[J]. 金属学报, 2020, 56(6): 849-854. [4] 黄火根,徐宏扬,张鹏国,王英敏,柯海波,张培,刘天伟. 具有反常非晶形成能力的U-Cr二元合金[J]. 金属学报, 2017, 53(2): 233-238. [5] 彭超, 李媛, 邓永和, 彭平. 近共晶成分Ni-P非晶合金微结构特征的原子模拟分析[J]. 金属学报, 2017, 53(12): 1659-1668. [6] 吕宝臣 刘海涛 任鑫 王晓亮 李刚 孙跃军. 高溶质浓度(伪)三元系金属玻璃原子密堆垛模型[J]. 金属学报, 2012, 48(2): 240-244. [7] 胡强 曾燮榕 钱海霞 谢胜辉 盛洪超. 铁基块体非晶合金玻璃形成能力与特征自由体积的关系[J]. 金属学报, 2012, 48(11): 1329-1334. [8] 孙亚娟 魏先顺 黄永江 沈 军. 稀土Gd掺杂对锆基块体非晶合金玻璃形成能力及力学性能的影响[J]. 金属学报, 2009, 45(2): 243-248. [9] 吴泽宇 郭胜锋 李宁 柳林. Co对Fe--B--Y--Nb块体非晶合金玻璃形成能力及软磁性能的影响[J]. 金属学报, 2009, 45(2): 249-252. [10] 王娜; 李长荣; 杜振民 . 二元合金过冷液态的形核驱动力和非晶形成能力的热力学分析[J]. 金属学报, 2008, 44(9): 1111-1115 . [11] 戚力; 董立峰; 程华; 崔占全; 马明臻; 景勤 ; 李工 . 高压条件下Pd--Ni合金熔体非晶形成过程及微观结构演化的分子动力学研究[J]. 金属学报, 2008, 44(2): 233-236 . [12] 董盼; 张甲; 常新春; 侯万良; 全明秀; 王建强 . Al--Co--Y体系中富 Al区非晶相的形成与结构演化[J]. 金属学报, 2008, 44(2): 227-232 . [13] 徐民; 孙羽; 全明秀; 王沿东; 左良 . Fe--Co--Nd--Nb--B非晶合金的形成和软磁性能[J]. 金属学报, 2007, 43(7): 699-704 . [14] 李宏祥; Seonghoon.Yi; 张新房; 王晓东 . Fe--C--Si--B--P--Cr--Mo--Al块体非晶合金的制备与压缩性能[J]. 金属学报, 2006, 42(7): 777-780 . [15] 贺林; 孙军 . 氧对Zr-Cu-Ni-Al-Ti块体非晶合金热稳定性的影响[J]. 金属学报, 2006, 42(2): 134-138 . Viewed Full text Abstract Cited   Shared      Discussed