金属学报  1998, Vol. 34 Issue (10): 1077-1083

论文 本期目录 | 过刊浏览 |

油井管钢氢致开裂门槛值研究

褚武扬;吕荣邦;乔利杰;王燕斌;程以环;陈红星;关永生;阎应龙;孙炜

北京科技大学材料物理系;北京;100083;北京科技大学材料物理系;北京;100083;北京科技大学材料物理系;北京;100083;北京科技大学材料物理系;北京;100083;宝山钢铁公司;上海;201900;宝山钢铁公司;上海;201900;天津钢管公司;天津;300301;天津钢管公司;天津;300301;天津钢管公司;天津;300301

THE THRESHOLD STRESS FOR HYDSOGEN-INDUCED CRACKING OF C90 TUBULAR STEELS

CHU Wuyang; LU Rongbang;QIAO Lijie; WANG Yanbin (Department of Materials Physics; University of Science & Technology Beijing; Beijing 100083)CHENG Yihuan; CHEN Hongxing(Baoshan Iron and Steel Corporation; Shanghai 201900);GUAN Yongsheng; YAN Yinglong; SUN Wei(Tianjin Steel Pipe Corporation; Tianjin 300310)Correspondent:CHU Wuyang; professor Tel: (010)62332906; Fax: (010)62327283;E-mail: ljqiao@public.bta.net.cn

褚武扬;吕荣邦;乔利杰;王燕斌;程以环;陈红星;关永生;阎应龙;孙炜. 油井管钢氢致开裂门槛值研究[J]. 金属学报, 1998, 34(10): 1077-1083.
, , , , , , , , . THE THRESHOLD STRESS FOR HYDSOGEN-INDUCED CRACKING OF C90 TUBULAR STEELS[J]. Acta Metall Sin, 1998, 34(10): 1077-1083.

摘要 参考文献 相关文章 Metrics 全文: PDF(563 KB)   摘要: 四种高强度油并管钢动态充氢时，进入试样的可扩散氢含量c0和充氢电流i成正比；而氢致断裂门槛应力σc与名义屈服强度σt之比和Inc0成正比，即σc／σt=A-BInc0．测量了四种钢在H2S中浸泡时进入试样的c0，求出相应的ic，用ic充氢时测出的门槛应力σc（H）／σt和H2S中应力腐蚀门槛应力σc（H2S）／σt相一致这表明，可用特定电流下的动态充氢来代替H2S应力腐蚀． 关键词 ： 油井管钢,  H_2S应力腐蚀,  氢致开裂,  门槛应力     Abstract：During dynamically charging four kinds of C90 tubular steels with hydrogen,the concentration of divisible hydrogen c0 is directly proportional to cathodic current i, and thenormalized threshold stress σc.(H)/σt decreases linearly with hi c0, i.e., σc(H)/σt=A-B ln c0.The concentrations of diffusible hydrogen in the steels during immersing in the H2S saturationsolution, c0*, have been measured. The values of σc(H)/σt during dynamically charging withic corresponding to c0* for the four steels are consistent with the threshold stress σc(H2S)/ctduring SCC in H2S solution. The result shows that the threshold stress during charging with asuitable current density ic can substitute for the threshold stress during SCC in H2S solution. Key words： C90 tubular steel    SCC in H_2S solution    hydrogen-induced cracking    threshold stress 收稿日期: 1998-10-18      基金资助:国家自然科学基金!59671042，59725104 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 褚武扬 吕荣邦 乔利杰 王燕斌 程以环 陈红星 关永生 阎应龙 孙炜 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1998/V34/I10/1077 1褚武扬.氢损伤与滞后断裂.北京:冶金工业出版社,1988(Chu W Y.Hudrogen Damage and Delayed Fracture.Beijing:The Metallurgicla Industry Press,,1988) 2黄长河,梅东生,俞梦文,王燕斌,褚武扬.中国腐蚀与防护学报,1997;17:129(Huang C H, Mei D S, Yu M W, Wang Y B, Chu W Y. J Chin Soc Corros Prot, 1997; 17: 129) 3于广华,程以环,陈红星,牛学军,乔利杰,褚武扬.金属学报,1996;32:617(Yu G H, Cheng Y H, Chen H X, Niu X J, Qiao L J, Chu W Y. Acta Metall Sin, 1996; 32: 617) 4Gao K W, Wang Y B, Chu W Y. Sci Chin, 1995; 38A: 1501 5Gu B, Gao K W, Huang Y Z, Chu W Y .Sci Chin, 1997; 40E: 235 6Su Y J, Wang Y B, Chu W Y. Sci Chin, 1997; 40E: 661 7Li M D, Zhang T C, Lu H, Chu W Y. Sci Chin, 1997; 40E: 530 8于广华,程以环,陈廉,乔利杰,褚武扬.金属学报,1995;31:A454(Yu G H, Cheng Y H, Chen L, Qiao L J, Chu W Y. Acta Metall Sin, 1995; 31: A454) 9Bao X; Chu W Y, Hsiao C M. Scr Metall, 1987; 21: 613( [1] 李小琳, 刘林锡, 李雅婷, 杨佳伟, 邓想涛, 王海丰. 单一 MX 型析出相强化马氏体耐热钢力学性能及蠕变行为[J]. 金属学报, 2022, 58(9): 1199-1207. [2] 杨柯,史显波,严伟,曾云鹏,单以银,任毅. 新型含Cu管线钢——提高管线耐微生物腐蚀性能的新途径[J]. 金属学报, 2020, 56(4): 385-399. [3] 史显波, 严伟, 王威, 单以银, 杨柯. 新型含Cu管线钢的抗氢致开裂性能[J]. 金属学报, 2018, 54(10): 1343-1349. [4] 赵小宇, 黄峰, 甘丽君, 胡骞, 刘静. MS X70酸性环境用管线钢焊接接头氢致开裂敏感性及氢捕获效率研究[J]. 金属学报, 2017, 53(12): 1579-1587. [5] 周成双 郑树启 陈长风. 湿H2S环境中L360MCS钢焊接热影响区的应力导向氢致开裂行为[J]. 金属学报, 2010, 46(5): 547-553. [6] 任学冲; 武明; 褚武扬; 李金许; 乔利杰; 江波 ; 陈刚; 崔银会 . 连铸温度和低倍组织对轮箍钢氢致开裂的影响[J]. 金属学报, 2007, 43(2): 149-153 . [7] 张颖瑞; 董超芳; 李晓刚; 芮晓龙; 周和荣 . 电化学充氢条件下X70管线钢及其焊缝的氢致开裂行为[J]. 金属学报, 2006, 42(5): 521-527 . [8] 赵显武; 宿彦京; 高克玮; 乔利杰; 褚武扬; 许颖 . 单晶硅压痕裂纹的氢致滞后扩展[J]. 金属学报, 2005, 41(2): 173-177 . [9] 王毅; 褚武扬; 宿彦京; 高克玮; 刘辉; 乔利杰 . PZT压电陶瓷的应力腐蚀[J]. 金属学报, 2003, 39(2): 182-184 . [10] 张涛; 姚远; 褚武扬; 乔利杰 . 管线钢氢致附加应力与氢致门槛应力的相关性[J]. 金属学报, 2002, 38(8): 844-848 . [11] 王毅; 褚武扬; 乔利杰; 宿彦京 . PZT陶瓷的氢致滞后断裂[J]. 金属学报, 2002, 38(6): 625-628 . [12] 李金许; 王燕斌; 乔利杰; 褚武扬 . Ni3Al+NiAl双相合金的氢致开裂过程研究[J]. 金属学报, 2002, 38(5): 512-516 . [13] 胡津; 任文超 . 纯铝基复合材料的应力腐蚀与氢致开裂[J]. 金属学报, 2002, 38(2): 174-176 . [14] 李金许; 王燕斌; 乔利杰; 褚武扬 . 纯Ni中氢致开裂的透射电镜原位观察[J]. 金属学报, 2001, 37(9): 911-916 . [15] 史博; 宿彦京; 乔利杰; 褚武扬 . Al2O3陶瓷的氢致滞后断裂[J]. 金属学报, 2001, 37(9): 932-934 . Viewed Full text Abstract Cited   Shared      Discussed