金属学报  1964, Vol. 7 Issue (3): 301-306

论文 本期目录 | 过刊浏览 |

锑单晶体的范性变形

包先格;陈能宽

THE PLASTIC DEFORMATION OF ANTIMONY SINGLE CRYSTALS

BAO SHAN-GER; CHEN NENG-KUAN

包先格;陈能宽. 锑单晶体的范性变形[J]. 金属学报, 1964, 7(3): 301-306.
, . THE PLASTIC DEFORMATION OF ANTIMONY SINGLE CRYSTALS[J]. Acta Metall Sin, 1964, 7(3): 301-306.

摘要 参考文献 相关文章 Metrics 全文: PDF(1238 KB)   摘要: 純度为99.8％的銻单晶体在室溫拉伸很脆,孿生表現为主要的形变机构。在200℃拉伸时,范性显著增加,在金相显微镜下观察到滑移线。用金相和X射线方法定出孿生面K_1为{011}面,孿生方向η1为<100>,滑移面为(111)面。 Abstract：Single crystals of antimony (99.8%) were very brittle at room temperature and twins occurred abundantely during deformation. Their plasticity was improved with increasing temperature and many slip lines were found at 200℃. By means of metallographyic and X-ray methods, it was found that the twinning system is {110} <100> and the slip plane is {111}. 收稿日期: 1964-03-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 包先格 陈能宽 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1964/V7/I3/301 [1] Schmid, E., Boas, W.: Plasticity of Crystals, (Hughes, 1950) , p. 94． [2] Gough, H. J., Cox, H. L.: Proc. Roy. Soc., 1930, A127, 431． Gough, H. J., Cox, H. L.: J. Inst. Metals, 1932, 48, 227． Gough, H. J.: Proc. Am. Soc. Testing Mater., 1933, 33, 3． [3] Georgieff, M., Schmid, E.: Z. Physik., 1926, 36, 759． [4] Berg, W. F.: Nature, 1934, 133, 831． Berg, W. F., Sandler, L.: Nature, 1935, 136, 915． [5] Andrade, E. N. da C.: International Conference on Physics, (Physical Society, London, 1935) , vol. 2, p. 176． [6] Berg, W. F.: Nature, 1934, 134, 143． Berg, W. F.: International Conference on Physics, (Physical Society, London, 1935) , vol. 2, p. 178． [7] Gough, H. J., Cox, H. L.: Nature, 1936, 137, 701． [8] #12 [9] Niggli, P.: Handbuch der Experimental Physik, (Akademle-Verlag GmbH, Berlin, 1928, 7, pt. 1, p. 151． [10] Hall, E. O.: Twinning and Diffusionless Transformations in Metals, (Butterworths, 1954) , p. 83． [11] Barrett, C. S.: Cold Working of Metals, (ASM, 1949) , p. 65． Lee, H. T., Brick, R. M.: Trans. Am. Soc. Metals, 1956, 48, 1003．g No related articles found! Viewed Full text Abstract Cited   Shared      Discussed