Acta Metall Sin  2004, Vol. 40 Issue (10): 1018-1022     DOI:
Research Articles Current Issue | Archive | Adv Search |
Recognition of Metal Fracture Surface Morphologies Based on the Fuzzy Texture Spectrum
ZHANG Xiaoqing; SUN Yongqing; ZHANG Zheng
School of Materials Science and Engineering; Beijing University of Aeronautics and Astronautics; Beijing 100083
Cite this article: 

ZHANG Xiaoqing; SUN Yongqing; ZHANG Zheng. Recognition of Metal Fracture Surface Morphologies Based on the Fuzzy Texture Spectrum. Acta Metall Sin, 2004, 40(10): 1018-1022 .

Download:  PDF(10576KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  Fuzzy uncertainty texture spectrum (FUTS) is applied for the pattern recognition of fracture surface morphologies. Linear minor distance classifier is used to classify five typical fracture surface morphologies, including equiaxed dimple, elongated dimple, cleavage failure, fatigue and intergranular cracking. With testing results, the method of FUTS is highly efficient in fracture morphologies classification.
Key words:  pattern recognition      fracture surface      texture spectrum      
Received:  31 July 2003     
ZTFLH:  TG11.5  

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y2004/V40/I10/1018

[1] Zhang D. Practical Analysis of Machinery Failure. Beijing: National Defense Press, 1997: 24(张栋.机械失效的实用分析.北京:国防工业出版社,1997:24)
[2] Komai K, Minoshima K, Ishii S. JSME. Inter J (A). 1993;3(2) : 220
[3] Yan Y H, Wang D J, Huang Y H, Wang Q H, Wang T B.Acta Metall Sin, 1997; 33: 386(颜云辉,王德俊,黄雨华,王清昊,王彤波.金属学报,1997;33:386)
[4] Yan Y H, Gao J H, Liu Y, Cao Y G, Lei S C. Acta Metal Sin, 2002; 38: 309(颜云辉,高金鹤,刘勇,曹宇光,雷世超.金属学报,2002;38:309)
[5] Ye Y F, Zhang Z. J Mater Eng, 2003; (4) : 44(叶宇飞,张峥.材料工程,2003;(4) :44)
[6] Lee Y G, Lee J H, Hsueh Y C. Neurocomputing, 1998; 20: 115
[7] Lee Y G, Lee J H, Hsueh Y C. Electron Lett, 1995; 31(12) : 959
[8] Ramze Rezaee M, Goedhart B, Lelieveldt B P E. Pattern Recognition, 1999; 32: 2011
[9] Li S Y. Fuzzy Control.Neurocontrol and Intelligent Cybernetics. Harbin: Harbin Institute of Techonology Press, 1998: 35 (李士勇.模糊控制·神经控制和智能控制论.哈尔滨:哈尔滨工业大学出版社,1998:35)
[10] Bian Z Q, Zhang X G. Pattern Recognition. Beijing: Ts-inghua University Press, 1999: 186(边肇祺,张学工.模式识别.北京:清华大学出版社,1999:186)
[11] American Socity For Metals ed, translated by Deng R H. Metals Handbook (8th Edition, Vol.9) . Beijing: China Machine Press, 1985: 52, 76(美国金属学会著,邓日红译.金属手册(第八版,第九卷).北京:机械工业出版社,1985:52,76)
[12] Engel L, Klingele H eds, translated by Meng X M. An Atlas of Metal Damage. Beijing: China Machine Press, 1990: 32, 36, 79(Engel L,Klingele H著,孟锡明译.金属损伤图谱(下).北京:机械工业出版社,1990:32,36,79)
[1] Xiaoguang WANG,Jiarong LI,Jian YU,Shizhong LIU,Zhenxue SHI,Xiaodai YUE. TENSILE ANISOTROPY OF SINGLE CRYSTAL SUPERALLOY DD9[J]. 金属学报, 2015, 51(10): 1253-1260.
[2] YAN Ying, LU Meng, LI Xiaowu. EFFECTS OF PRE-FATIGUE DEFORMATION ON THE  UNIAXIAL TENSILE BEHAVIOR OF COARSEGRAINED PURE Al[J]. 金属学报, 2013, 49(6): 658-666.
[3] . Research Of Flaking And Its Fractography In A Wheel Steel[J]. 金属学报, 2006, 42(3): 273-279 .
[4] WEI Xuejun;LI Jin;LIU Su'e;KE Wei (State Key Laboratory of Corrosion and Protection; Institute of Corrosion and Protection of Metals; The Chinese Academy of Sciences; Shenyang 110015). ANALXSIS OF FATIGUE FRACTURE WITH CYCLIC OVERLOADING FOR A537 STEEL IN 3.5%NaCl SOLUTION AT AN APPLIED CATHODIC POTENTIAL[J]. 金属学报, 1998, 34(2): 146-150.
[5] ZHANG Zhaochun; WU Zhu; LI Chonghe; QIN Pei; CHEN Nianyi(Shanghai Institute of Metallurgy; The Chinese Academy of Sciences; Shanghai 200050)Correspondent: WU Zhu; Tel: (021)62511070-8932; Fax: (021)62513510. APPLICATION OF PATTERN RECOGNITION AND ARTIFICIAL NEURAL NETWORK TO IMPROVE THE MECHANICAL PROPERTIES OF CYLINDER BLOCK CAST OF AUTOMOBILE ENGINE[J]. 金属学报, 1998, 34(10): 1068-1072.
[6] YAN Yunhui; WANG Dejun;HUANG Yuhua; WANG Qinghao; WANG Tongbo (Northeastern University; Shenyang 110006)(Manuscript received 1996-05-20; in revised form 1996-07-04). FOURIER TRANSFORM METHOD FOR ANALYSIS OF FATIGUE FRACTOGRAPHS[J]. 金属学报, 1997, 33(4): 386-390.
[7] YAN Yunhui;WANG Dejun(Northeastern University; Shenyang 110006)(Manuscript received 1995-08-21). IMAGE PROCESSING TECHNIQUES IN ANALYSIS OF METAL FRACTURE SURFACE[J]. 金属学报, 1996, 32(5): 552-556.
[8] LI Xiaowu; TIAN Jifeng; KANG Yan; WANG Zhongguang(State Key Laboratory for Fatigue and Fracture of Materials; Institute of Metal Research; Chinese Academy of Sciences; Shenyang 110015)(Manuscript received 1994-11-23; in revised form 1995-03-03). QUANTITATIVE ANALYSIS ON SURFACE ROUGHNESS OF FRACTURE[J]. 金属学报, 1995, 31(19): 311-317.
[9] CONG Peisheng; LI Tonghua (Tongji University; Shanghai) CHEN Yu; CHEN Nianyi (Shanghai Institute of Metallurgy; Academia Sinica; Shanghai). NEURON ADAPTIVE ALGORITHM APPLIED TO EXPERIMENTAL DESIGN IN STEEL PRODUCTION[J]. 金属学报, 1992, 28(11): 59-61.
[10] ZHOU Diangen; CHEN Nianyi (Shanghai Institute of Metallurgy; Academia Sinica; Shanghai). PATTERN RECOGNITION APLLIED TO STABILITY OF FILLED Ti_2Ni PHASES[J]. 金属学报, 1992, 28(11): 20-22.
[11] CHEN Yu; CHEN Nianyi (Shanghai Institute of Metallurgy; Academia Sinica)PENG Ping; KONG Bingyu (Iron and Steel Research Institute; Shanghai Baoshan Iron and Steel Complex). ASPRES—AN EXPERT SYSTEM FOR ALLOY STEEL DEVELOPMENT[J]. 金属学报, 1992, 28(10): 91-94.
[12] LIU Miaoxiu;CHENG Zhaonian;CHEN Nianyi;KE Jiajun Shanghai Institute of Metallurgy; Academia Sinica Institute of Chemical Metallurgy; Academia Sinica; Beijing. FACTORS AFFECTING SILICA CONTENT OF ALUMINIUM HYDROXIDE PRODUCT IN CARBONIZATION PROCESS[J]. 金属学报, 1990, 26(5): 156-159.
[13] QI Yunxin Nei Monggol Institute of Metallic Materials; Baotou P.O. Box No.4; Baotou; Nei Monggol. SAM ANALYSIS OF NITRIDE IN 30CrNi STEEL[J]. 金属学报, 1990, 26(2): 132-135.
No Suggested Reading articles found!