ROOM TEMPERATURE SECTION OF Cu-Dy(≤35wt-％)-Ni TERNARY PHASE DIAGRAM

Acta Metall Sin

1989, Vol. 25

Issue (3): 134-136 DOI:

Current Issue | Archive | Adv Search

ROOM TEMPERATURE SECTION OF Cu-Dy(≤35wt-％)-Ni TERNARY PHASE DIAGRAM

LI Dexuan;ZHENG Jianxuan Guangxi University; Nanning

Cite this article:

LI Dexuan;ZHENG Jianxuan Guangxi University; Nanning. ROOM TEMPERATURE SECTION OF Cu-Dy(≤35wt-％)-Ni TERNARY PHASE DIAGRAM. Acta Metall Sin, 1989, 25(3): 134-136.

Download:

PDF(219KB)
Export: BibTeX | EndNote (RIS)

Abstract The room temperature section of Cu-Dy (≤35wt-%)-Ni ternary phasediagram has been determined by means of X-ray diffraction technique. The resultsare as follows: four single-phase regions (α, Dy_2Ni_(17), DyNi_5 and DyCu_5), five two-phase regions (α+Dy_2Ni_(17), Dy_2Ni_(17) + DyNi_5, DyCu_5 + DyNi_5, α+DyNi_5 and DyCu_5+α)and two three-phase regions (α+ Dy_2Ni_(17) + DyNi_5 and α+ DyNi_5 + DyCu_5) exist in thediagram. NO any new phase has been observed. The solubility of Dy in α-phase isup to 2wt-%.

Key words: Cu-Dy-Ni system phase diagram

Received: 18 March 1989

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

URL:

https://www.ams.org.cn/EN/ OR https://www.ams.org.cn/EN/Y1989/V25/I3/134

1 郑建宣,王淳正.物理学报,1982;31:669--672
2 郑建宣,徐国雄.物理学报,1982;31:807--809
3 Smithells C J. Metals Reference Book, 5th ed., London: Butterworth, 1976: 586
4 Buschow K H J, Van Der Goot A S. Acta Crystallogr, Ser. B, 1971; 27: 1085
5 王淳正,郑建宣.金属学报,1985;21:B62--65a

[1]	GAO Xiang, ZHANG Guikai, XIANG Xin, LUO Lizhu, WANG Xiaolin. Effects of Alloying Elements on the Adsorption of Oxygen on V(110) Surfaces: A First-Principles Study[J]. 金属学报, 2020, 56(6): 919-928.
[2]	ZHANG Weibin SHA Chunsheng DU Yong WEN Guanghua XIE Wen WANG Shequan. COMPUTER SIMULATIONS AND VERIFICATION OF GRADIENT ZONE FORMATION IN CEMENTED CARBIDES[J]. 金属学报, 2011, 47(10): 1307-1314.
[3]	ZHANG Huawei; LI Yanxiang; LIU Yuan. Study of Metal--Hydrogen Binary Phase Diagram in Gasar Process[J]. 金属学报, 2005, 41(1): 55-.
[4]	ZHANG Jian(Metallurgical Engineering School; University of Science and Technology Beijing; Beijing 100083). CONSISTENCY(OR SIMILARITY) OF THERMODYNAMIC PROPERTIES OF METALLURGICAL MELTS WITH THEIR PHASE DIAGRAMS[J]. 金属学报, 1998, 34(7): 742-752.
[5]	Zhang Jian (Institute of Metallurgy; University of Science and Technology Beijing; Beijing 100083). CLASSIFICATION OF THERMODYNAMIC PROPERTIES OF BINARY METALLIC MELTS ACCORDING TO THEIR PHASE DIAGRAMS[J]. 金属学报, 1998, 34(1): 75-85.
[6]	ZHOU Hong; WANG Jinguo; JIA Shusheng (Jilin University of Technology; Chanerhun 130025) OGIKeisaku(Kyushu Universily; Japan) (Manuscript received 1996-03-22; in revised form 1997-04- 13). SOLIDIFIED MICROSTRUCTURES AND PHASES OF HIGH SPEED STEELS CONTA1NING DIFFERENT V AND C CONTENT[J]. 金属学报, 1997, 33(8): 838-843.
[7]	FANG Jianhui; TANG Yun; LI Yu; YAN Licheng; CHEN Nianyi (Shanghai University;Shanghai 201800); WANG Jiyang (Shandong University; Jinan 250012)(Manuscript received 1996-04-08; in revised form 1996-09-10). KPO_3-M0O_3 PHASE DIAGRAM[J]. 金属学报, 1997, 33(4): 395-397.
[8]	ZHOU Guozhi(Kuo-Chih Chou) (University of Science and Technology Beijing;Beiing 100083). NEW GENERATION SOLUTION GEOMETRICAL MODEL AND ITS FURTHER DEVELOPMENT[J]. 金属学报, 1997, 33(2): 126-132.
[9]	DING Jinjun;ZHAO Gang;HAO Shiming (Northeastern University; Shenyang 110006). PHASE EQUILIBRIUM RELATIONSHIPS AND INTERDIFFUSION COEFFICIENTS OF β,α ANDγIN THE Ti-Al BINARY SYSTEM[J]. 金属学报, 1997, 33(10): 1105-1109.
[10]	YUAN Wenxia; MA Shulan; QIAO Hin; ZHUANG Weidong; XING Xianran;QIAO Zhiyu (University of Science and Technology Beijing; Beijing 100083)(General Institute for Non-Ferrous Metals; Beijing 100088)(Manuscript received 1995-04-28; in revised form 1995-11-05). A STUDY ON THE YCl_3-AECl_2(AE=Mg, Ca, Sr, Ba)BINARY PHASE DIAGRAMS[J]. 金属学报, 1996, 32(2): 139-143.
[11]	HAO Shiming; ZENG Ninghua (Northeastern University; Shenyang 110006)(Manuscript received 1994-11-16). ISOTHERMAL SECTION OF PHASE DIAGRAM IN Ti-Al-Cr TERNARY SYSTEM AT 1000℃[J]. 金属学报, 1995, 31(16): 152-158.
[12]	YAN Licheng;FANG Jianhui;XU Jingyan;YANG Jinxiu(Shanghai University of Science and Technology). PHASE DIAGRAM OF KF-LiCl-CaCl_2 SYSTEM[J]. 金属学报, 1994, 30(19): 301-303.
[13]	WAN Jinglong(Anhui Institute of Technology; Hefei); BI Qinghua(Shanghai University of Science and Technology). Gd-CoAl VERTICAL SECTION OF Gd-Co-Al PHASE DIAGRAM[J]. 金属学报, 1994, 30(17): 204-207.
[14]	XU Qian;YU Yaxin;QIU Zhuxian(Northeastern University;Shenyang)(Manuscript received 25 June;1993). THERMODYNAMIC PROPERTIES AND PHASE DIAGRAMS OF Li-CaF_2,NaF-CaF_2 AND KF-CaF_2[J]. 金属学报, 1994, 30(16): 150-155.
[15]	SHEN Jianyun(General Research Institute for Non-Ferrous Metals;Beijing);CHATILLON C(Laboratoire de Thermodynamique et Physico-chimie Metallurgiques;Fracne)(Manuscript received 16 June;1993). THERMODYNAMICS OF Ga-In-As SYSTEM UNDER LATTICE DEFORMATION[J]. 金属学报, 1994, 30(16): 145-149.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed