ROOM TEMPERATURE AND 750℃ ISOTHERMAL SECTIONS OF Ag-Pd-Gd TERNARY SYSTEM (Gd≤25 at.-%) PHASE DIAGRAM
ZHANG Kanghou;CHEN Lili Kunming Institute of Precious Metals ZHANG Kanghou; Kunming Institute of Precious Metals; 650221 Kunming
Cite this article:
ZHANG Kanghou;CHEN Lili Kunming Institute of Precious Metals ZHANG Kanghou; Kunming Institute of Precious Metals; 650221 Kunming. ROOM TEMPERATURE AND 750℃ ISOTHERMAL SECTIONS OF Ag-Pd-Gd TERNARY SYSTEM (Gd≤25 at.-%) PHASE DIAGRAM. Acta Metall Sin, 1989, 25(5): 139-141.
Abstract The room temperature section and the isothermal section at 750℃ ofthe Ag-Pd-Gd ternary system containing 0--25at.-% Gd are constructed by X-raydiffraction analysis and optical microscopy. Both sections consist of 3 single-, 3 bi-nary-and 1 ternary-regions respectively.
1 Kiessler G, Gebhardt E, Steeb S. J Less-Common Met, 1972; 26: 293 2 Gschneidner K A Jr., McMasters O D, Alexander D G, Venteicher R F. Metall Trans, 1970; 1; 1961 3 McMasters O D, Gschneidner K A Jr., Venteicher R F. Acta Crystallogr, 1970; B26: 1224 4 Bailey D M, Kline G R. Acta Crystallogr, 1971; B27: 650 5 Gschneidner K A Jr., Calderwood F W. Bull Alloy Phase Diagrams, 1985; 6 (2) : 138 6 Loebich O Jr., Raub E. J Less-Common Met, 1973; 30: 47 7 何纯孝,马光辰,王文娜,王永生,赵怀志.贵金属合金相图,北京:冶金工业出版社,1983:16
YUAN Wenxia; MA Shulan; QIAO Hin; ZHUANG Weidong; XING Xianran;QIAO Zhiyu (University of Science and Technology Beijing; Beijing 100083)(General Institute for Non-Ferrous Metals; Beijing 100088)(Manuscript received 1995-04-28; in revised form 1995-11-05). A STUDY ON THE YCl_3-AECl_2(AE=Mg, Ca, Sr, Ba)BINARY PHASE DIAGRAMS[J]. 金属学报, 1996, 32(2): 139-143.
YAN Licheng;FANG Jianhui;XU Jingyan;YANG Jinxiu(Shanghai University of Science and Technology). PHASE DIAGRAM OF KF-LiCl-CaCl_2 SYSTEM[J]. 金属学报, 1994, 30(19): 301-303.
SHEN Jianyun(General Research Institute for Non-Ferrous Metals;Beijing);CHATILLON C(Laboratoire de Thermodynamique et Physico-chimie Metallurgiques;Fracne)(Manuscript received 16 June;1993). THERMODYNAMICS OF Ga-In-As SYSTEM UNDER LATTICE DEFORMATION[J]. 金属学报, 1994, 30(16): 145-149.