THE BEHAVIOR OF INTERFACICAL CREEP DAMAGE OF DISSIMILAR WELDED JOINT BETWEEN MARTENSITE AND BAINITE HEAT-RESISTANT STEEL

Acta Metall Sin

2007, Vol. 43

Issue (12): 1275-1281 DOI:

Research Articles

Current Issue | Archive | Adv Search

THE BEHAVIOR OF INTERFACICAL CREEP DAMAGE OF DISSIMILAR WELDED JOINT BETWEEN MARTENSITE AND BAINITE HEAT-RESISTANT STEEL

zhang Jian－Qiang

武汉大学

Cite this article:

zhang Jian－Qiang. THE BEHAVIOR OF INTERFACICAL CREEP DAMAGE OF DISSIMILAR WELDED JOINT BETWEEN MARTENSITE AND BAINITE HEAT-RESISTANT STEEL. Acta Metall Sin, 2007, 43(12): 1275-1281 .

Download:

PDF(1497KB)
Export: BibTeX | EndNote (RIS)

Abstract Abstract The creep rupture strength, creep damage and characteristics of interfacial failure of dissimilar welded joint between martensite (9Cr1MoVNbN) and bainite steel(12Cr2MoWVTiB) are been investigated by means of argon gas shielded tungsten pulsed arc welding, high temperature accelerated simulation, creep rupture test, in view of dissimilar welded joint between martensite (9Cr1MoVNbN) and bainite steel(12Cr2MoWVTiB).The research results indicate that the interfacial creep damage of undermatching welded joint is very serious, and the interfacial failure occurred, the early failure tendencies are higher than those of overmatching and medium welded joint. The creep damage and early failure tendency of medium matched joint are lower than those of overmatching and undermatching welded joint, and only isolated holes are found in the test. The creep rupture strength ( ) of medium matching joint is almost the same as that of undermatching joint. The creep rupture strength overmatching joint is the least one, therefore, it is reasonable that the medium matched is used for the dissimilar welded joint between martensite and bainite steel. KEY WORDS Martensite heat-resistant steel, bainite heat-resistant steel, dissimilar metal welding joint, creep damage, early failure

Key words:

Received: 20 December 2006

ZTFLH:

TG407

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	zhang Jian－Qiang

URL:

https://www.ams.org.cn/EN/ OR https://www.ams.org.cn/EN/Y2007/V43/I12/1275

[1]Watanabe T,Tabuchi M,Yamazaki M,Hongo H,Tanable T.Int J Pressure Vessels Piping,2006;83:63
[2]Kluech L,Hashimoto N,Maziasz P J.Scr Mater,2005; 53:275
[3]Taneike M,Abe F,Swada K.Nature,2003;424:294
[4]Sawada K,Takeda M,Maruyama K,Ishii R,Yamada M, Nagae Y,Komine R.Mater Sci Eng,1999;A267:19
[5]Abe F,Horiuchi T,Taneike M.Mater Sci Eng,2004; A378:299
[6]Tamur M,Iida A H,Esaka H,Shinozuka K.ISLJ Int,2003; 43:1807
[7]Mackenie M,Craven A J,Collins C L.Scr Mater,2006; 54:1
[8]Gupta G,Was G S.J ASTM Int,2005;2:1
[9]Yoshino M,Mishima Y,Toda Y,Kushima H,Sawada K, Kimura K.ISIJ Int,2005;45:107
[10]Ning B Q,Liu Y C,Yin H Q,Han Y J,Yang L S.Mater Rev,2006;20(12):83 (宁保群，刘永长，殷红旗，韩雅静，畅留栓．材料导报，2006；20(12)：83)
[11]Zhu L H,Zhao Q X,Gu H C,Lu Y X.Mater Mech Eng, 1999;23(1):6 (宋丽慧，赵钦新，顾海澄，陆燕逊．机械工程材料，1999；23(1)：6)
[12]Brozda J,Zeman M.Weld Res Abroad,1995;42(5):58
[13]Brozda J,Zeman M.Weld Res Abroad,1997;43(6):33
[14]Otoguro Y,Matsubara M,Itoh I,Nakazawa T.Nuclear Eng Design,2000;196:51
[15]Zhang J Q,Zhao H Y,Wu S,Lu A L.Weld Res Abroad, 2005;51(1):29
[16]Zhang J Q,Wu S,Zhao H Y,Lu A L.Chin d Mech Eng, 2003;39(2):58 (张建强，吴苏，赵海燕，鹿安娜．机械工程学报，2003；39(2)：58)
[17]Roberts D I,Ryder R H,Viswanthan R.J Pressure Vessel Technol,1985;107:247
[18]Lundin C D.Welding J,1982;61(Suppl.2):58
[19]Bhaduri A K,Venkadesan S,Rodriguez P.Int J Pressure Vessels Piping,1994;58:251
[20]Shi C Y,Tian X T,Chen Z G.Trans Chin Weld Inst, 1995;16:185 (史春元，田锡唐，陈字刚．焊接学报，1995；16：185)
[21]Cane B J.Met Sci,1981;115:302
[22]Onoro J.Int J Pressure Vessels Piping,2006;83:540
[23]Perrin I J,Hayhust D R.Int J Pressure Vessels Piping, 1999;76:599

[1]	WANG Luning, LIU Lijun, YAN Yu, YANG Kun, LU Lili. *Influences of Protein Adsorption on the in vitro* Corrosion of Biomedical Metals**[J]. 金属学报, 2021, 57(1): 1-15.
[2]	TUNG Feng'en;WANG Yuming Institute of Materials Science; Jilin University; Changchun. X-RAY ANALYSIS OF WORK-HARDENING PROCESS FOR POLYCRYSTALLINE а-BRASS DURING UNIAXIAL TENSILE TEST[J]. 金属学报, 1989, 25(2): 82-84.
[3]	WANG Jinliang, WANG Chenchong, HUANG Minghao, HU Jun, XU Wei. The Effects and Mechanisms of Pre-Deformation with Low Strain on Temperature-Induced Martensitic Transformation[J]. 金属学报, 2021, 57(5): 575-585.
[4]	DU Hegui;LIU Xin Northeast University of Technology; Shenyang. KINETICS OF CARBON COMBUSTION IN PLASMA AIR[J]. 金属学报, 1989, 25(2): 85-88.
[5]	. [J]. 金属学报, 2001, 37(1): 42-46 .
[6]	. [J]. 金属学报, 1999, 35(3): 320-324 .
[7]	. [J]. 金属学报, 2000, 36(1): 72-76 .
[8]	. [J]. 金属学报, 1999, 35(3): 330-333 .
[9]	. [J]. 金属学报, 1999, 35(3): 334-336 .
[10]	. [J]. 金属学报, 2000, 36(6): 647-650 .
[11]	. [J]. 金属学报, 2000, 36(6): 655-658 .
[12]	No Author. ACTA METALLURGLCA SLNLCA Volume 28 Series A 1992 SUBJECT INDEX[J]. 金属学报, 1992, 28(12): 63-90.
[13]	. [J]. 金属学报, 2000, 36(7): 780-784 .
[14]	No Author. ACTA METALLURGICA SINICA(JINSHU XUEBAO) Volume 28 1992 AUTHOR INDEX[J]. 金属学报, 1992, 28(12): 71-94.
[15]	Хань Яо-вэнь Инсмцмум мемаддов АН КНР;Г.н.Ойкс Московскц цнсмцмум смадц. НЗУЧЕНИЕ ПРОЦЕССОВ ДЕСУЛЬФУРАЦИИ ХНДКОΓО МЕТАЛЛА В ВАКУУМЕ[J]. 金属学报, 1963, 6(2): 98-110.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed