SHORT FATIGUE CRACK BEHAVIOUR IN ISO-STRESS SPECIMENS |
HONG Youshi;LU Yonghua;ZHENG Zhemin C. M. Cheng Institute of Mechanics; Academia Sinica; Beijing Institute of Mechanics;Academia Sinica;Beijing 100080 |
|
Cite this article:
HONG Youshi;LU Yonghua;ZHENG Zhemin C. M. Cheng Institute of Mechanics; Academia Sinica; Beijing Institute of Mechanics;Academia Sinica;Beijing 100080. SHORT FATIGUE CRACK BEHAVIOUR IN ISO-STRESS SPECIMENS. Acta Metall Sin, 1990, 26(1): 46-52.
|
Abstract The fatigue tests were made on the specially designed specimens by avibration testing machine to investigate the initiation and propagation features ofshort fatigue cracks in a weld metal. The specimens were prepared of a kindof triangular shape in which the surface tensile stress is a constant. The resultsshow that the short fatigue cracks originate from the slip bands and initiate insidethe ferrite grains. The development of short fatigue cracks is marked by the grad-ual increase in crack density with fatigue cycles. The coalescence between shortcracks leads to crack propagation and the crack path is predominantly transgranular.
|
Received: 18 January 1990
|
1 Gouda V K, Staehle R W. Br Corros J, 1980; 15: 111--117 2 Timoshenko S,Gere J 著,胡人礼译.材料力学,北京:科学出版社,1978:226--232 |
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|