Acta Metall Sin  2012, Vol. 48 Issue (11): 1321-1328    DOI: 10.3724/SP.J.1037.2012.00225
Current Issue | Archive | Adv Search |
STUDY OF COMPLEX DUCTILE INCLUSIONS CONTROLLING IN MEDIUM-HIGH CARBON STEELS
MA Yue, SU Hang, PAN Tao, YU Yinhong, YANG Caifu, ZHANG Yongquan, PENG Yun
Division of Engineering Steels, Central Iron & Steel Research Institute, Beijing 100081
Cite this article: 

MA Yue SU Hang PAN Tao YU Yinhong YANG Caifu ZHANG Yongquan PENG Yun. STUDY OF COMPLEX DUCTILE INCLUSIONS CONTROLLING IN MEDIUM-HIGH CARBON STEELS. Acta Metall Sin, 2012, 48(11): 1321-1328.

Download:  PDF(1017KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  

Formation of a special kind of complex ductile inclusions (CDI), which were character as oxides covered by sulphides, was investigated in a medium--high carbon steel. It was believed that fatigue and toughness properties of carbon steels were benefited from CDI formation, for oxides were separated from steel matrix. By means of thermodynamic calculation and inclusion microscopy in medium-high carbon steels with different S content and with Ca-treated, CDI in 0.55C steels has been researched. And thermal-stability of the CDI was researched by high temperature quenching. The results show that the frequency of CDI formation increase with S content changes from 0.001% to 0.01%. However, the fraction of covered oxides is no more than 90% without Ca-treated and can be promoted to about 100% in 0.006% S steel after Ca-treated. The reason of improved CDI formation by increasing S content and Ca-treated is that sulphides precipitation temperature could be promoted to higher than solid line of matrix, which is clearly showed by thermodynamic calculation. Furthermore, thermo-stability of CDI is affected heavily by heating history of matrix steel. Sulphide will dissolute from oxide when heat steel casting to an improper high temperature. Fortunately, the dissolution process could be stunted with redundant S content. It shows that thermo-stability of CDI could be received in Ca-treated steels with more than 0.006%S.

Key words:  medium-high carbon steel      complex ductile inclusion      S content      Ca-treated      thermodynamic calculation     
Received:  24 April 2012     
Fund: 

Supported by Key Research and Development Program of the Ministry of Railway of China  (Nos.2009J015 and 2009J016)

URL: 

https://www.ams.org.cn/EN/10.3724/SP.J.1037.2012.00225     OR     https://www.ams.org.cn/EN/Y2012/V48/I11/1321

[1] Lyne C M, Kasak A. Trans ASM, 1968; 61: 10

[2] Mine K, Yoshida H. Jpn Pat, s55–041910, 1980

[3] Deng Z S. Acta Metall Sin, 1976; 12: 187

(邓枝生. 金属学报, 1976; 12: 187)

[4] Wang C W, Dong H S, Yang Z N. J China Text Univ (Engl Ed), 1989; 6(1): 26

[5] Zhang W P. J Sichuan Norm Univ (Nat Sci), 2005; 28: 619

(张维平. 四川师范大学学报(自然科学版), 2005; 28: 619)

[6] Ma Y, Pan T, Jiang B, Cui Y H, Su H, Peng Y. Acta Metall Sin, 2011; 47: 978

(马跃, 潘涛, 江波, 崔银会, 苏航, 彭云. 金属学报, 2011; 47: 978)

[7] Brooksbank D, Andrews K W. J Iron Steel Inst, 1968; 206: 595

[8] Brooksbank D, Andrews K W. J Iron Steel Inst, 1969; 207: 474

[9] Pan T, Yang Z G, Bai B Z, Fang H S. Acta Metall Sin, 2003; 39: 1037

(潘涛, 杨志刚, 白秉哲, 方鸿生. 金属学报, 2003; 39: 1037)

[10] Oh Y J, Lee B S, Hong J H. J Nuclear Mater, 2002; 301: 108

[11] Li J, Guo F, Li Z, Wang J L, Yan M G. J Iron Steel Res Int, 2007; 14: 254

[12] Garrison Jr W M, Wojcieszynski A L. Mater Sci Eng, 2007; A464: 321

[13] Salter W J M, Pickering F B. J Iron Steel Inst, 1969; 207: 992

[14] Yang C W, L¨u N B, Zhuo X J, Wang X H, Wang W J. Iron Steel, 2010; 45(11): 32

(杨成威, 吕迺冰, 卓晓军, 王新华, 王万军. 钢铁, 2010; 45(11): 32)

[15] Zhuo X J, Wang Y Q, Wang X H, Lee H G. J Iron Steel Res Int, 2010; 17(2): 10

[16] Kim T G, Lee W K, Park J H, Min D J, Song H S. ISIJ Int, 2001; 41: 1460

[17] Miyamoto G, Shinyoshi T, Yamaguchi J, Furuhara T, Maki T, Uemori R. Scr Mater, 2003; 48: 371

[18] Li S J, Ren X C, Gao K W, Su Y J, Jiang B, Chen G, Zhao H. Trans Mater Heat Treat, 2011; 32(12): 48

(李胜军, 任学冲, 高克玮, 宿彦京, 江波, 陈刚, 赵海. 材料热处理学报, 2011; 32(12): 48)

[19] Lu X Z, Wu R, Li S L,Wu H T, ZhaiWL, Huang L, Wu D B, Song S P. J Wuhan Univ Sci Technol, 2010; 34: 147

(卢献忠, 吴润, 李书黎, 吴海涛, 翟万里, 黄雷, 吴德炳, 宋述鹏. 武汉科技大学学报, 2010; 34: 147)

[20] Ye G Z, J¨onsson P, Lund T. ISIJ Int, 1996; 36: S105

[21] Kusano Y, Kawauchi Y, Wajima M, Sugawara K, Yoshida M, Hayashi H. ISIJ Int, 1996; 36: S77

[22] Yuan F M, Wang X H, Yang X F. J Univ Sci Technol Beijing, 2006; 13: 486

[23] Taguchi K, Ono–Nakazato H, Nakai D, Usui T, Marukawa K. ISIJ Int, 2003; 43: 1705

[24] Oikawa K, Ohtani H, Ishida K, Nishizawa T. ISIJ Int, 1995; 35: 402

[25] Wakoh M, Sawai T, Mizoguchi S. ISIJ Int, 1996; 36: 1014

[26] Wang Y, Zhao A M, Chen Y L, Zuo B Q, Xue J P. Iron Steel, 2011; 46(1): 60

(王岩, 赵爱民, 陈银莉, 左碧强, 薛俊平. 钢铁, 2011; 46(1): 60)

[1] MU Yahang, ZHANG Xue, CHEN Ziming, SUN Xiaofeng, LIANG Jingjing, LI Jinguo, ZHOU Yizhou. Modeling of Crack Susceptibility of Ni-Based Superalloy for Additive Manufacturing via Thermodynamic Calculation and Machine Learning[J]. 金属学报, 2023, 59(8): 1075-1086.
[2] CHEN Wei, CHEN Hongcan, WANG Chenchong, XU Wei, LUO Qun, LI Qian, CHOU Kuochih. Effect of Dilatational Strain Energy of Fe-C-Ni System on Martensitic Transformation[J]. 金属学报, 2022, 58(2): 175-183.
[3] YU Jiaying, WANG Hua, ZHENG Weisen, HE Yanlin, WU Yurui, LI Lin. Effect of the Interface Microstructure of Hot-Dip Galvanizing High-Strength Automobile Steel on Its Tensile Fracture Behaviors[J]. 金属学报, 2020, 56(6): 863-873.
[4] Yu HUANG, Guoguang CHENG, You XIE. Modification Mechanism of Cerium on the Inclusions in Drill Steel[J]. 金属学报, 2018, 54(9): 1253-1261.
[5] HAN Guomin, HAN Zhiqiang, Alan A. Luo, Anil K. Sachdev, LIU Baicheng. PHASE FIELD SIMULATION ON MORPHOLOGY OF CONTINUOUS PRECIPITATE Mg17Al12IN Mg-Al ALLOY[J]. 金属学报, 2013, 49(3): 277-283.
[6] LIANG Jingjing, ZHU Ming, YUAN Zhonghua, WANG Junwu, JIN Tao,SUN Xiaofeng, HU Zhuangqi. INFLUENCE OF Re ON THE PHASE CONSTITUENT OF A NiCoCrAlY COATING ALLOY[J]. 金属学报, 2013, 49(3): 330-340.
[7] WANG Yi SUN Feng DONG Xianping ZHANG Lanting SHAN Aidang. THERMODYNAMIC STUDY ON EQUILIBRIUM PRECIPITATION PHASES IN A NOVEL Ni-Co BASE SUPERALLOY[J]. 金属学报, 2010, 46(3): 334-339.
[8] Chun-guang Kuai; Zhifang Peng. ELEMENTAL PARTITIONING CHARACTERISTICS AND STABILITY OF EQUILIBRIUM PHASES DURING 450-1200℃ IN T/P91 HEAT-RESISTANT STEEL[J]. 金属学报, 2008, 44(8): 897-900 .
[9] ;. RESEARCH ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF A NEW WROUGHT SUPERALLOY[J]. 金属学报, 2008, 44(5): 540-546 .
[10] DING Xueyong;WANG Wenzhong(Northeastern University;Shenyang). A NEW THERMODYNAMIC CALCULATION FORMULA FOR ACTIVITY OF COMPONENT IN BINARY SYSTEM[J]. 金属学报, 1994, 30(22): 444-447.
[11] DING Xueyong;WANG Wenzhong;HAN Qiyong Northeastern University University of Science and Technology Beijing. THERMODYNAMIC CALCULATION OF Fe-P-j SYSTEM MELT[J]. 金属学报, 1993, 29(12): 21-26.
No Suggested Reading articles found!