X-RAY DIFFRACTION ANALYSIS ON THE THICKNESS EFFECT OF γ/γ' LATTICE MISMATCHE IN NICKEL BASE SINGLE CRYSTAL SUPERALLOY DD10
WANG Youdao, WU Erdong, WANG Sucheng, LI Wuhui
Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016
Cite this article:
WANG Youdao WU Erdong WANG Sucheng LI Wuhui. X-RAY DIFFRACTION ANALYSIS ON THE THICKNESS EFFECT OF γ/γ' LATTICE MISMATCHE IN NICKEL BASE SINGLE CRYSTAL SUPERALLOY DD10. Acta Metall Sin, 2011, 47(11): 1418-1425.
Abstract The lattice constants of the matrix phase γ and the precipitated phase γ' in a wafer-like nickel-base single crystal superalloy DD10 were determined by four-axis X-ray diffractometer (XRD). The variations of the lattice constants and lattice mismatches of γ and γ' phases in the alloy wafer with different thicknesses, i.e., different interphase restriction conditions were obtained. A critical thickness of the alloy wafer to reach an unstable stress state was defined based on the observed changes of lattice mismatch associated with a transformation of stress state from the 3D bulk state to 2D plane state. The lattice mismatches corresponding to different mismatch stress states were calculated. The lattice constants of the γ and γ' phases under a relaxed non--mismatch stress state were evaluated based on certain assumptions. The results showed that after the thickness of the alloy wafer reached the critical value, the lattice constant of the γ' phase decreased linearly with the decrease of the thickness, whereas that of the γ phase kept nearly constant, resulting in a linear increase of the absolute value of lattice mismatch. Accompanied with the thinning process, the crystal lattice misorientation and the mosaicity increased, the γ/γ' interphase restraint reduced and the interphase stress relaxed, and the measured stress state changed to the plane state. The estimated critical thickness and the lattice constants under non-mismatch stress state could provide references for the design of the components and the measurement of the residual stress in the superalloy.
Supported by National Natural Science Foundation of China (No.51071157) and High Technology Research and Development Program of China (No.2009AA03Z535)
XIE Youqing(Department of Materials Science and Engineering; Central South University of Technology; ChangSha 410083)CorrsPondent: XIE Youqing; pwtsson Tel: (O731)8879287; Fax: (0731)8826136Manuscript received 1997-12-1; in revised form 1998-0406. RELATIONSHIP BETWEEN PARTIAL AND AVERAGE ATOMIC VOLUMES OF COMPONENTS IN Cu-Ni ALLOYS[J]. 金属学报, 1998, 34(12): 1243-1248.
[5]
XIE Youqing(Department of Materials Science and Engineering; Central South University of Technology; Changsha 410083)Correspondent:XIE Youqing; professor; Tel: (0731)8879287; Fax. (O731)8826136Manuscript received 1997-11-14; in revised form 1998-02-12. LATTICE CONSTANTS OF DISORDERED AND ORDERED PHASES IN Au-Cu SYSTEM[J]. 金属学报, 1998, 34(12): 1233-1242.
XING Pengfei; ZHAI Yuchun; TIAN Yanwen; GENG Yan; CHEN Feng(Northeastern University; Shenyang 110006)(Manuscript received 1995-04-24; in revised form 1995-10-16). STUDY ON THE OXIDATION KINETICS OF WS_2 IN OPEN AIR[J]. 金属学报, 1996, 32(2): 187-190.
XU Wenchong;SUN Fuyu Central Iron and Steel Research Institute; Ministry of Metallurgical Industry; Beijing XU Wenchong; senior engineer; Department Institute; Ministry of Metallurgical Industry No;13. Central Iron and SteelResearch Beijing 100081. LATTICE PARAMETERS OF COMPLEX CARBONITRIDE CONTAINING Ti, Nb AND V[J]. 金属学报, 1989, 25(6): 146-148.