Cr含量和pH值对低铬管线钢半钝化行为的影响 |
许立宁(),朱金阳,王贝 |
北京科技大学新材料技术研究院腐蚀与防护中心 北京100083 |
|
Influence of Cr Content and pH Value on the Semi-Passivation Behavior of Low Cr Pipeline Steels |
Lining XU(),Jinyang ZHU,Bei WANG |
Corrosion and Protection Center, Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China |
引用本文:
许立宁,朱金阳,王贝. Cr含量和pH值对低铬管线钢半钝化行为的影响[J]. 金属学报, 2017, 53(6): 677-683.
Lining XU,
Jinyang ZHU,
Bei WANG.
Influence of Cr Content and pH Value on the Semi-Passivation Behavior of Low Cr Pipeline Steels[J]. Acta Metall Sin, 2017, 53(6): 677-683.
[1] | Zhang Z H, Huang Z Y, Sun Y N, et al.Development of 3Cr series oil pipes with good CO2 and H2S corrosion resistant properties[J]. Baosteel Technol., 2006, (3): 5 | [1] | (张忠铧, 黄子阳, 孙元宁等. 3Cr抗CO2和H2S腐蚀系列油套管开发[J]. 宝钢技术, 2006, (3): 5) | [2] | Liang M H, Zhao G X, Feng Y R, et al.The influence of Cr on CO2 corrosion behavior of P110 steel[J]. J. Mater. Eng., 2006, (suppl.1): 31 | [2] | (梁明华, 赵国仙, 冯耀荣等. 添加Cr元素对P110钢CO2腐蚀行为的影响[J]. 材料工程, 2006, (增刊1): 31) | [3] | Xu L N, Wang B, Zhu J Y, et al.Effect of Cr content on the corrosion performance of low-Cr alloy steel in a CO2 environment[J]. Appl. Surf. Sci., 2016, 379: 39 | [4] | Pfennig A, Kranzmann A.Effect of CO2 and pressure on the stability of steels with different amounts of chromium in saline water[J]. Corros. Sci., 2012, 65: 441 | [5] | Wu Q L, Zhang Z H, Dong X M, et al.Corrosion behavior of low-alloy steel containing 1% chromium in CO2 environments[J]. Corros. Sci., 2013, 75: 400 | [6] | Ko M, Ingham B, Laycock N, et al.In situ synchrotron X-ray diffraction study of the effect of chromium additions to the steel and solution on CO2 corrosion of pipeline steels[J]. Corros. Sci., 2014, 80: 237 | [7] | Kermani B, Gonzales J C, Turconi G L, et al.In-field corrosion performance of 3%Cr steels in sweet and sour downhole production and water injection [A]. Corrosion 2004[C]. New Orleans, LA: NACE International, 2004: 04111 | [8] | Nyborg R, Dugstad A.Understanding and prediction of mesa corrosion attack [A]. Corrosion 2003[C]. San Diego, CA: NACE International, 2003: 03642 | [9] | Nice P I, Ueda M.The effect of microstructure and chromium alloying content to the corrosion resistance of low-alloy steel well tubing in seawater injection service [A]. Corrosion 1998[C]. San Diego, CA: NACE International, 1998: 98003 | [10] | Ueda M, Takabe H.Corrosion resistance of low Cr bearing steel in sour and sweet environments [A]. Corrosion 2002[C]. Denver, CO: NACE International, 2002: 02041 | [11] | Kermani B, Dougan M, Gonzales J C, et al.Development of low carbon Cr-Mo steels with exceptional corrosion resistance for oilfield applications [A]. Corrosion 2001[C]. Houston, TX: NACE International, 2001: 01065 | [12] | Paolinelli L D, Simison S N, Pérez T E.The influence of Cr content on the efficiency of inhibitor of C-Mn steel CO2 corrosion [A]. Corrosion 2006[C]. San Diego, CA: NACE International, 2006: 06369 | [13] | Paolinelli L D, Simison S N, Pérez T E.The influence of steel microstructure, chemical composition and precorrosion on CO2 corrosion inhibitor efficiency [A]. Corrosion 2007[C]. Nashville, TN: NACE International, 2007: 07311 | [14] | Scoppio L, Piccolo E L, Cristofaro N D, et al.Corrosion problem and its countermeasure of 3Cr production tubing in NaCl completion brine on the Statfjord field [A]. Corrosion 2006[C]. San Diego, CA: NACE International, 2006: 06134 | [15] | Ueda M, Takabe H, Nice P I.The development and implementation of a new alloyed steel for oil and gas production wells [A]. Corrosion 2000[C]. Orlando, FL: NACE International, 2000: 00154 | [16] | Kermani B, Gonzales J C, Turconi G L, et al.Window of application and operational track record of low carbon 3Cr steel tubular [A]. Corrosion 2006[C]. San Diego, CA: NACE International, 2006: 06133 | [17] | Chen C F, Lu M X, Zhao G X, et al.The ion passing selectivity of CO2 corrosion scale on N80 tube steel [A]. Corrosion 2003[C]. San Diego, CA: NACE International, 2003: 03342 | [18] | Ueda M, Takabe H.The formation behavior of corrosion protective films of low Cr bearing steels in CO2 environments [A]. Corrosion 2001[C]. Houston, TX: NACE International, 2001: 01066 | [19] | Chen C F, Lu M X, Sun D B, et al.Effect of chromium on the pitting resistance of oil tube steel in a carbon dioxide corrosion system[J]. Corrosion, 2005, 61: 594 | [20] | Guo S Q, Xu L N, Zhang L, et al.Corrosion of alloy steels containing 2% chromium in CO2 environments[J]. Corros. Sci., 2012, 63: 246 | [21] | Zhu J Y, Xu L N, Lu M X, et al.Cathodic reaction mechanism of 3Cr low alloy steel corroded in CO2-saturated high salinity solutions[J]. Int. J. Electrochem. Sci., 2015, 10: 1434 | [22] | Dugstad A.Fundamental aspects of CO2 metal loss corrosion-Part I: Mechanisms [A]. Corrosion 2006[C]. San Diego, CA: NACE International, 2006: 06111 | [23] | Sidorin D, Pletcher D, Hedges B.The electrochemistry of 13% chromium stainless steel in oilfield brines[J]. Electrochim. Acta, 2005, 50: 4109 | [24] | Kocijan A, Donik ?, Jenko M.Electrochemical and XPS studies of the passive film formed on stainless steels in borate buffer and chloride solutions[J]. Corros. Sci., 2007, 49: 2083 | [25] | Jung R H, Tsuchiya H, Fujimoto S.XPS characterization of passive films formed on type 304 stainless steel in humid atmosphere[J]. Corros. Sci., 2012, 58: 62 | [26] | Ueda M, Ikeda A.Effect of microstructure and Cr content in steel on CO2 corrosion [A]. Corrosion 1996[C]. Denver, Colorado: NACE International, 1996: 96013 |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|