金属学报  2008, Vol. 44 Issue (9): 1090-1094

论文 本期目录 | 过刊浏览 |

湿度对恒电场下BaTiO3单晶中畴变的影响

姜冰;白杨;禇武扬;乔利杰;宿彦京

北京科技大学腐蚀与防护中心

Effects of humidity on domain switching in BaTiO3 single crystals under sustained electric field

;;;;

北京科技大学

姜冰; 白杨; 禇武扬; 乔利杰; 宿彦京 . 湿度对恒电场下BaTiO3单晶中畴变的影响[J]. 金属学报, 2008, 44(9): 1090-1094 .

摘要 参考文献 相关文章 Metrics 全文: PDF(4300 KB)   摘要: 通过偏振光显微镜观察了在恒电场作用下湿空气对BaTiO3单晶畴变的影响. 结果表明, 在 恒电场下, 湿度对不同的畴结构有不同的影响. 较低的湿度对a-b和b-c畴结构没有影响. 而 在较高的湿度下, 随着放置时间的增加, b-c畴结构发生了变化, b畴逐渐向c畴转变; 但是较 高的湿度对a-b畴结构无影响. 可用水分子在a(b)畴和c畴上的吸附差别解释上述现象. 关键词 ： 铁电畴变,  湿度,  BaTiO3单晶,  恒电场     Abstract：Effects of humidity on domain switching behaviors in BaTiO3 single crystals under electric field were investigated by polarized light microscopy (PLM). It was found that the humidity has different effect on different domain configurations. The low humidity has no effect on both a-b domain configuration and b-c domain configuration under fields. However, the high humidity can promote b domain switch to c domain under electric fields. The effects were explained by different adsorption of polar H2O molecules on different domain areas in humidity conditions. Key words： Domain switching    Humidity    BaTiO3 single crystals    sustained external field 收稿日期: 2008-01-14      ZTFLH:  N073   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 姜冰 白杨 禇武扬 乔利杰 宿彦京 44.8K 链接本文: https://www.ams.org.cn/CN/Y2008/V44/I9/1090 [1]Weitzing H,Schneider G A,Steffens J,Hammer M,Hoff- mann M J.J Eur Ceram Soc,1999;19:1333 [2]Lynch C S.Acta Mater,1996;44:4137 [3]Njiwa A B K,Lupascu D C,Rodel J.Acta Mater,2004; 52:4919 [4]Wang F,Su Y J,He J Y,Qiao L J,Chu W Y.Scr Mater, 2006;54:201 [5]Shang J K,Tan X.Acta Mater,2001;49:2993 [6]Jiang Y J,Fang D N,Li F X.Appl Phys Left,2007;90: 222907 [7]Tan X L,Xu Z K,Shang J K.Mater Sci Eng,2001;A314: 157 [8]Hackemann S,Pfeiffer W.J Eur Ceram Soc,2003;23:141 [9]Wang Y,Chu W Y,Gao K W,Su Y J,Qiao L J.Appl Phys Lett,2003;82:1583 [10]Su Y J,Wang Y,Chu W Y,Gao K W,Qiao L J.Acta Mater,2004;52:3753 [11]Zhao X W,Chu W Y,Su Y J,Li J X,Gao K W,Qiao L J.Acta Metall Sin,2006;42:13 (赵显武，褚武扬，宿彦京，李金许，高克玮，乔利杰．金属学报，2006；42：13) [12]Merz W J.Phys Rev,1954;95:690 [13]Little E A.Phys Rev,1955;98:978 [14]Munoz Saldana J,Schneider G A,Eng L M.Surf Sci, 2001;480:L402 [15]Hirth J P.Metall Trans,1980;11A:861 [16]Chu W Y,Qiao L J,Chen Q Z,Gao K W.Fracture and Environmental Fracture.Beijing:Science Press,2000:36 (褚武扬，乔利杰，陈奇志，高克玮．断裂与环境断裂．北京：科学出版社，2000：36) [1] 姜冰 郭志猛 邢献然. 外场作用下BaTiO3单晶裂纹扩展和畴变[J]. 金属学报, 2011, 47(5): 605-610. [2] 王瑞敏; 褚武扬; 宿彦京; 高克玮; 乔利杰 . BaTiO3单晶压痕裂纹的畴变和裂纹扩展的原位观察[J]. 金属学报, 2006, 42(12): 1274-1278 . [3] 赵显武; 褚武扬; 宿彦京; 李金许; 高克玮; 乔利杰 . 恒应力下BaTiO3单晶压痕裂纹的滞后扩展和畴变[J]. 金属学报, 2006, 42(1): 13-18 . [4] 王瑞敏; 褚武扬; 宿彦京; 高克玮; 乔利杰 . 浸蚀促进BaTiO3单晶的畴变和裂纹扩展的研究[J]. 金属学报, 2005, 41(3): 297-301 . [5] 王瑞敏; 宿彦京; 高克玮; 乔利杰; 褚武扬 . 恒电场下BaTiO3陶瓷压痕裂纹的滞后扩展[J]. 金属学报, 2004, 40(11): 1175-1178 . Viewed Full text Abstract Cited   Shared      Discussed