镍基非晶态合金晶化过程的研究

王煜明;孟昭富;王钊

吉林大学;吉林大学;吉林大学

ON THE CRYSTALLIZATION OF AMORPHOUS Ni-BASE ALLOY

WANG Yuming; MENG Zhaofu; WANG Zhao (Jilin University; Changchun)

王煜明;孟昭富;王钊. 镍基非晶态合金晶化过程的研究[J]. 金属学报, 1986, 22(2): 119-156.
, , . ON THE CRYSTALLIZATION OF AMORPHOUS Ni-BASE ALLOY[J]. Acta Metall Sin, 1986, 22(2): 119-156.

摘要 参考文献 相关文章 Metrics 全文: PDF(1593 KB)   摘要: 本文研究了非晶态Ni_(83)Cr_7Fe_3Si_4B_3合金在动态加热及等温热处理条件下的晶化过程。结果表明,对于动态加热及等温热处理两种情况,镍基非晶态合金的晶化过程相同,结晶相没有发生变化。但是,在动态加热条件下,初始晶化主要是成核结晶,而在等温热处理晶化过程中晶粒长大起主要作用。 Abstract：The crystallization of amorphous Ni_(83)Cr_7Fe_3Si_4B_3 alloy was investigated under dynamic heating and isothermal annealing conditions. An identical crystallization and unaltered phases are revealed under both treatments. However, the initial crystallization is mainly due to the nucleation of crystals under dynamic heating, while the crystal growth plays a major role under isothermal annealing. It has also been measured that the microhardness approached its highest value just before the specimen being totally crystallized. 收稿日期: 1986-02-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 王煜明 孟昭富 王钊 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1986/V22/I2/119 1 Tiwari, R.S.; Ranganathan, S.; Heimendahl, M.V., Z. Metall, 72 (1981) , 563． 2 Scott, M.G., J. Mater. Sci., 13 (1978) , 291． 3 Von Heimendahl, M.; Maussner, G., J. Mater. Sci., 14 (1979) , 1238． 4 Chang, H.; Sastri, S., Metall. Trans., 8 (1977) , 1063． 5 Waseda, Y; Okazaki, H.; Masumoto, T.J. Mater. Sci., 12 (1977) , 1927． No related articles found! Viewed Full text Abstract Cited   Shared      Discussed