Acta Metall Sin  1998, Vol. 34 Issue (5): 455-458    DOI:

Current Issue | Archive | Adv Search |

BULK NANO-SCALE MULTILAYERS PREPARED BY REPEATED PRESSING-ROLLING

HUANG Bin (School of Materials Science and Engineering; Shanghai Jiaotong University; Shanghai 200030)ISHIHARA Keiichi N; SHINGU Hideo P (Graduate School of Energy Science; Kyoto University; Kyoto 606; Japan)

HUANG Bin (School of Materials Science and Engineering; Shanghai Jiaotong University; Shanghai 200030)ISHIHARA Keiichi N; SHINGU Hideo P (Graduate School of Energy Science; Kyoto University; Kyoto 606; Japan). BULK NANO-SCALE MULTILAYERS PREPARED BY REPEATED PRESSING-ROLLING. Acta Metall Sin, 1998, 34(5): 455-458.

Abstract References Related Articles Recommended Metrics Download:  PDF(1769KB)  Export:  BibTeX | EndNote (RIS)       Abstract  Bulk nano-scale multilayers have been prepared by repeated pressing-rolling the initially macroscopically thick layered sample. The SEM and TEM observations revealed that the final layer thickness in the regular laminates is about 10 nm. The Fe/Cu multilayers exhibited a clear magnetoresistance (MR) ratio at 77 K. The tensile strength is over 1500 MPa and its elongation is about 0.8% at room temperature. Key words:  nano-scale material      Fe/Cu multilayer      repeated pressing-rolling      magnetoresistance      Received:  18 May 1998      Service E-mail this article Add to citation manager E-mail Alert RSS （） Articles by authors URL:  https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y1998/V34/I5/455 1 Baral D, Ketterson J B, Hilliard J E.J Appl Phys, 1985; 57: 1076 2Lehoczky S L.J Appl Phys, 1978; 49: 5479 3Baibich M N, Broto J M, Fert A, Nguyen Dan Van F, Petroff Eitenne P F, Greuzet G, Friederich A, Chazelas J. Phys Rev Lett, 1988; 61: 2473 4Parkin S S, Li Z G, Smith D J Appl Phys Lett, 1991 58: 2710 5Petroff F, Bartheleny A, Mosca D H, Lottis D K, Fert A, Schroeder P A, Pratt W P Jr, Loloee R, Lequien S.Phys Rev,1991; B44:5355 6Koehler J S. Phgs Rev, 1970 B2: 547 7Embury J D, Hirth J P. Acta Metall Mater, 1994 42: 2051/ [1] . [J]. 金属学报, 2007, 43(6): 599-602 . [2] ZHANG Xinghua; LI Zhiqing; JIANG Enyong. INFLUENCE OF La DOPING ON THE STRUCTURE,MAGNETIC AND ELECTRICAL TRANSPORT PROPERTIES OF Pr0.75Na0.25MnO3[J]. 金属学报, 2006, 42(9): 974-978 . [3] WANG Lijin; ZHANG Hui; TENG Jiao; ZHU Fengwu. EFFECTS OF Ta SEED LAYER ON THE MICROSTRUCTURE AND MAGNETIC PROPERTY OF Ni65Co35 FILMS[J]. 金属学报, 2006, 42(9): 979-982 . No Suggested Reading articles found! Viewed Full text Abstract Cited   Shared      Discussed