Study of Magnetic Property of Co/Pd Multilayers by Electrocrystallization on Monocrystalline Silicon

Acta Metall Sin

2008, Vol. 44

Issue (4): 445-450 DOI:

Research Articles

Current Issue | Archive | Adv Search

Study of Magnetic Property of Co/Pd Multilayers by Electrocrystallization on Monocrystalline Silicon

上海大学

Cite this article:

. Study of Magnetic Property of Co/Pd Multilayers by Electrocrystallization on Monocrystalline Silicon. Acta Metall Sin, 2008, 44(4): 445-450 .

Download:

PDF(469KB)
Export: BibTeX | EndNote (RIS)

Abstract Multilayered Co/Pd nanostructure films are deposited on monocrystalline silicon(111) by using double-bath method and the technological conditions are determined. The mechanism of the growth kinetics for Co and Pd layers have been studied ,It is showed that the growth kinetics for Co and Pd are consistent with progressive nucleation.The mass change of layers are exactly measured by EQCM . XRD results suggest that the multilayer have good crystal lattice，and alloy-intermediate of Co and Pd are also found .In addition，hysteresis loops are measured by PPMS at room temperature .The result showed that : with decrease of Co thickness ,coercive force was increased and which up to 1130 Oe.

Key words:

Received: 24 September 2007

ZTFLH:

TG115.21

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

URL:

https://www.ams.org.cn/EN/ OR https://www.ams.org.cn/EN/Y2008/V44/I4/445

[1]Iton H,Hori T,Inoue J,Maekawa S.J Magn Magn Mater, 1994;136:33
[2]Mosca D H,Petroff F,Fert A.J Magn Magn Mater,1991; 94:L1
[3]Carcia P F,Meinhaldt A D,Suna A.Appl Phys Lett,1985; 47:178
[4]Carcia P F,Coulman D,Mclean R S,Reilly M.J Magn Magn Mater,1996;164:411
[5]Tanaka M,Kawaji J,Kimura K.J Magn Magn Mater, 2005;287:188
[6]Schindler W,Schneider O,Kirschner J.J Appl Phys,1997; 81:3915
[7]Sato Y,Kudo K,Kobayakawa K.Chem Lett,1998;9:945
[8]Kudo K,Kobayakawa K,Sato Y.Electrochem Acta,2001; 47:353
[9]Wang K,Picketing H W,Weil K G.J Electrochem Acta, 2001;46:3835
[10]Shiomi K,Ogawa S.IEEE Trans Magn,1999;35:3025
[11]Xun K,Shen D F.J Funct Mater Devices,1999;5:81 (荀坤，沈德芳．功能材料与器件学报，1999；5：81)
[12]Hills G,Montenegro I,Scharifker B.J Electroanal Chem, 1982;138:225
[13]Scharifker B R,Hills G.J Electrochem Acta,1983;28:879
[14]Oskam G J,Long G,Natarajan A,Searson P C.J Phys, 1998;31D:1927
[15]Zuo Z Z,Xia S C.J Wuhan Univ,1998;44:150 (左正忠，夏绍春．武汉大学学报，1998；44：150)
[16]Liu H.Master Thesis.Capital Normal University,Beijing, 2001 (刘洪．首都师范大学硕士学位论文，北京，2001)

[1]	WANG Luning, LIU Lijun, YAN Yu, YANG Kun, LU Lili. *Influences of Protein Adsorption on the in vitro* Corrosion of Biomedical Metals**[J]. 金属学报, 2021, 57(1): 1-15.
[2]	TUNG Feng'en;WANG Yuming Institute of Materials Science; Jilin University; Changchun. X-RAY ANALYSIS OF WORK-HARDENING PROCESS FOR POLYCRYSTALLINE а-BRASS DURING UNIAXIAL TENSILE TEST[J]. 金属学报, 1989, 25(2): 82-84.
[3]	WANG Jinliang, WANG Chenchong, HUANG Minghao, HU Jun, XU Wei. The Effects and Mechanisms of Pre-Deformation with Low Strain on Temperature-Induced Martensitic Transformation[J]. 金属学报, 2021, 57(5): 575-585.
[4]	DU Hegui;LIU Xin Northeast University of Technology; Shenyang. KINETICS OF CARBON COMBUSTION IN PLASMA AIR[J]. 金属学报, 1989, 25(2): 85-88.
[5]	. [J]. 金属学报, 2001, 37(1): 42-46 .
[6]	. [J]. 金属学报, 1999, 35(3): 320-324 .
[7]	. [J]. 金属学报, 2000, 36(1): 72-76 .
[8]	. [J]. 金属学报, 1999, 35(3): 330-333 .
[9]	. [J]. 金属学报, 1999, 35(3): 334-336 .
[10]	. [J]. 金属学报, 2000, 36(6): 647-650 .
[11]	. [J]. 金属学报, 2000, 36(6): 655-658 .
[12]	No Author. ACTA METALLURGLCA SLNLCA Volume 28 Series A 1992 SUBJECT INDEX[J]. 金属学报, 1992, 28(12): 63-90.
[13]	. [J]. 金属学报, 2000, 36(7): 780-784 .
[14]	No Author. ACTA METALLURGICA SINICA(JINSHU XUEBAO) Volume 28 1992 AUTHOR INDEX[J]. 金属学报, 1992, 28(12): 71-94.
[15]	Хань Яо-вэнь Инсмцмум мемаддов АН КНР;Г.н.Ойкс Московскц цнсмцмум смадц. НЗУЧЕНИЕ ПРОЦЕССОВ ДЕСУЛЬФУРАЦИИ ХНДКОΓО МЕТАЛЛА В ВАКУУМЕ[J]. 金属学报, 1963, 6(2): 98-110.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed