MAGNETIC PROPERTIES OF Nd_2(Fe_(1-x)M_x)_(14)B(M=C, Si) ALLOYS |
XING Feng;JIANG Chao;HO Wenwang Department of Physics; Peking University |
|
Cite this article:
XING Feng;JIANG Chao;HO Wenwang Department of Physics; Peking University. MAGNETIC PROPERTIES OF Nd_2(Fe_(1-x)M_x)_(14)B(M=C, Si) ALLOYS. Acta Metall Sin, 1988, 24(5): 420-424.
|
Abstract The magnetic properties of Nd_2(Fe_(1-x)M_x)_(14)B (M=C, Si) compoundshave been investigated. Substituting Fe by a small amount of metalloid C and Siatoms, the compounds are in tetragonal structure and have uniaxial anisotropy. Thesubstitution of C for part of Fe makes the Curie temperature and the intrinsic coer-civity of bond samples decrease at low temperature. The replacement of Fe by Simakes the Curie temperature increase with a maximum at the vicinity of x=0. 15.When the range of the content of Si is 0≤x≤0.10, the coercivity distinctly in-creases at room temperature, from 62.7 kA/m at x=0 to 138.7kA/m at x=0.06, wherethe residual magnetization has a maximum; at the mean time the saturation magne-tization decreases only by a small amount.
|
Received: 18 May 1988
|
1 Herbst J F, Croat J J, Yelon W B. J Appl Phys, 1985; 57: 4086 2 Matsuura Y. Hirosawa S, Yamamo to H, Fujimura S, Sagawa M. Appl Phys Lett, 1985; 46: 308 3 Yang Y C (杨应昌), Ho W W (何文望), Chen H Y (陈海英), Wang J (王进), Lan J (兰健). J Appl Phys, 1985; 57: 4118 4 Abache C, Oesterreicher H. J Appl Phys, 1986; 57: 1114 5 Liuingston J D. Proc 8th Int Wokshop on Rare-Earth Magnets and their Applioations 1985: 423 6 杨应昌,何文望,陈海英,邢峰,兰健,中国稀土学报,1985;3(2) :34 7 Sucksmith W, Thompson J E. Proc Roy Soc London, Ser. A, 1954; 225: 362 8 Koon N C, Das B N, Rubinstein M, Tyson J. J Appl Phys, 1985; 57: 4091 9 Givord D, Li H S, Perrier de la Bathie R. Solid State Commun, 1984; 51: 857 |
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|