INFLUENCE OF DISSOLVED CARBON CONTENT ON RECRYSTALLIZATION γ TEXTURE IN ULTRA-LOW CARBON DEEP DRAWING STEEL WITH HIGH PURITY
ZHAO Xiang(Northeastern University; Shenyang 110006); SEKI Fumie; ITO Kunio(Universily of Tokyo; Japon); YOSHINADA Naoki(Nippon Steel Compony; Japan) (Manuscript received 1994-03-07; in revised form 1995-01-12)
Cite this article: 

ZHAO Xiang(Northeastern University; Shenyang 110006); SEKI Fumie; ITO Kunio(Universily of Tokyo; Japon); YOSHINADA Naoki(Nippon Steel Compony; Japan) (Manuscript received 1994-03-07; in revised form 1995-01-12). INFLUENCE OF DISSOLVED CARBON CONTENT ON RECRYSTALLIZATION γ TEXTURE IN ULTRA-LOW CARBON DEEP DRAWING STEEL WITH HIGH PURITY. Acta Metall Sin, 1995, 31(18): 262-265.

Download:  PDF(289KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  Influence of dissolved carbon content on recrystallization γ-fibre texture in ultra-low carbon deep drawing steel sheet with high purity was investigated and the relationships between dissolved carbons and recrystallization γ-fibre texture and {111} <112> and {111} < 110 > textures were analysed by 3-dimensional orientation distribution function.
Key words:  dissolved carbon content      recrystallization texture      deep drawing steel sheet     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y1995/V31/I18/262

1福田铁钢,1967;53:5592罔本笃树.铁钢,1984;70:19063UshiodaK,SchlippenbachUV,HutchinsonWB.TexturesMicrostruc,1987;7:114梁志德,徐家桢,王福.织构材料的三维取向分析术.沈阳:东北工学院出版社,1986:1085赵骧,史江,伊藤邦夫,吉永直树.脱炭炭素浓度制御低炭素钢板集合组织,日本铁钢协会春期讲演大会(第5卷),千叶,日本铁钢协会,1992:8366HutchinsonWB,ActaMetall,1989:37:1047(
[1] CHANG Songtao, ZHANG Fang, SHA Yuhui, ZUO Liang. Recrystallization Texture Competition Mediated by Segregation Element in Body-Centered Cubic Metals[J]. 金属学报, 2023, 59(8): 1065-1074.
[2] Quan FU,Yuhui SHA,Zhenghua HE,Fan LEI,Fang ZHANG,Liang ZUO. Recrystallization Texture and Magnetostriction in Binary Fe81Ga19 Sheets[J]. 金属学报, 2017, 53(1): 90-96.
[3] Yan ZHANG,Mingxing GUO,Hui XING,Fei WANG,Xiaofeng WANG,Jishan ZHANG,Linzhong ZHUANG. INFLUENCE OF DIFFERENT THERMOMECHANICAL PROCESSES ON THE MECHANICAL PROPERTIES AND MICROSTRUCTURE OF Al-Mg-Si-Cu ALLOY SHEETS[J]. 金属学报, 2015, 51(12): 1425-1434.
[4] Xiang Zhao. EFFECTS OF ELECTRIC FIELD ANNEALING ON PLASTIC STRAIN RATIO (r VALUE) OF IF STEEL SHEET[J]. 金属学报, 2006, 42(8): 827-829 .
[5] YANG Ping; O.ENGLER(Institute of Metal Science and Metal Physics; Aachen University of Technology; Kopernikusstr. 14; D-52056;Aachen; Germany) Now: School of Materials Science and Engineering; University of Science and Technology Beijing; Beijing;100083 Now: Los Alamos National Laboratory; Center for Materials Science; K765; Los Alamos; NM87545; USACorrespondent: YANG Ping; Tel: (010)62333436; Fax: (010)62332336. PARTICLE STIMULATED NUCLEATION AND THE FORMATION OF RSCRYSTALLIZATION TEXTURE IN Al-Mn ALLOY CONTAINING PARTICLES Ⅱ. Interaction Between Particles and Other Nucleation Sites and the Formation of Recrystallization Texture[J]. 金属学报, 1998, 34(8): 793-801.
[6] YANG Ping; O.ENGLER(Institute of Metal Science and Metal Physics; Aachen University of Technology; Kopernikusstr. 14; D-52056;Aachen; Germany) Now: School of Materials Science and Engineering; University of Science and Technology Beijing; Beijing;100083 Now: Los Alamos National Laboratory; Center for Materials Science; K765; Los Alamos; NM87545; USACorrespondent: YANG Ping; Tel. (010)623s3Js6; Fax: (010)62332336. PARTICLE STIMULATED NUCLEATION AND THE FORMATION OF RECRYSTALLIZATION TEXTURE IN Al-Mn ALLOY CONTAINING PARTICLES Ⅰ. Deformation Zones Around Particles and Particle Stimulated Nucleation[J]. 金属学报, 1998, 34(8): 785-792.
[7] LIU Yansheng;ZHAO Xiong;LIANG Zhide Northeast University of Technology; Shenyang Department of Materials Science and Engineering;Northeast University of Technology;Shenyang 110006. COLD ROLLING TEXTURE AND RECRYSTALLIZATION TEXTURE OF CROSS SHEAR ROLLED COMMERCIAL COPPER[J]. 金属学报, 1990, 26(3): 126-130.
[8] ZHANG Yumei;JIANG Wenhui Northeast University of Technology; ShenyangDept.of Materials Science and Engineering;Northeast University of Technology;Shenyang. SECONDARY RECRYSTALLIZATION TEXTURE IN 50%Ni-Fe ALLOY WITH CUBIC ORIENTATION[J]. 金属学报, 1988, 24(3): 217-220.
No Suggested Reading articles found!