DEFORMATION ANALYSIS OF TUBE SPECIMEN DURING RING HOOP TENSION TEST |
Zhu-Bin He; |
哈尔滨工业大学 |
|
Cite this article:
Zhu-Bin He. DEFORMATION ANALYSIS OF TUBE SPECIMEN DURING RING HOOP TENSION TEST. Acta Metall Sin, 2008, 44(4): 423-427 .
|
Abstract Force and deformation of the specimen during ring hoop tension test were analyzed. Distribution of radial normal force and hoop tension force were discussed and equations derived. FEM analysis and experiments were carried out to verify the theoretical analysis. Results show that the FEM and experimental results agreed well with the distribution of hoop tension fore. The hoop tension force is axisymmetrical about the tension direction and increase from the top position to both sides. The distribution of hoop tension force is even with small friction coefficient, but will increase rapidly from top to side positions, which subsequently result in necking and fracture near the edge of gauge section.
|
Received: 14 September 2007
|
|
[1]Koc M,Altan T.J Mater Process Technol,2001;108:384 [2]Yuan S J,Qi J,He Z B.J Mater Process Technol,2006; 177:680 [3]Banabic D,Bunge H J.Formability of Metallic Materi- als,Plastic Anisotropy,Formability Testing and Forming Limits,Berlin,Germany:Springer,2000:92 [4]Wang Z T,Zhang S H,Xu Y,Xu T F,Mo L H.J Shenyang Inst Technol,2001;20(4):66 (王忠堂,张士宏,许沂,徐亭风,莫立华.沈阳工业学院学报,2001;20(4):66) [5]Murai T,Matsuoka S,Miyamoto S.J Mater Process Tech- nol,2004;146:408 [6]He Z B,Wang X S,Yuan S J,Xu A J.Acta Metall Sin, 2007;43:534 (何祝斌,王小松,苑世剑,许爱军.金属学报,2007;43:534) [7]Chai R X,Wen L M,Xu S Q.Light Alloy Fabr Technol, 2006;34(12):21 (柴蓉霞,温莉敏,许树勤.轻合金加工技术,2006;34(12):21) [8]Neugebauer R,G(?)schel A,Sterzing A.In:Juster N,Roso- chowski A,eds.,Proc ESAFORM Conf on Material Form- ing,Glasgow,UK:Akapit,Poland,2006:263 [9]Liewald M,Wagner S.In:Yuan S J,Manabe K,eds.,Proc Tubehydro,Harbin,China:HIT Press,2007:19 [10]Liewald M,Wagner S,Pop R.In:Cueto E,Chinesta F, eds.,Proc ESAFORM Conf on Material Forming,New York:American Institute of Physics,2007:126 [11]Price E G.Can Metall Ouarterly,1972;11:129 [12]Cohen A B,Majumdar S,Ruther W E,Billone M C, Chung H M,Neimark L A.Office of Scientific & Techni- cal Information,Argonne:Department of Energy,1999: 2 [13]Douglas W B,Donald A K,Arthur T M.Office of Sci- entific & Technical Information,Argonne:Department of Energy,2000:51 [14]Wang H,Bouchard R,Eagleson R.J Test Eval,2002;(30): 382 |
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|