High Temperature Creep Behavior Of Cast Ni Base Superalloy K44
HOU Jieshan; ZHANG Yulong; GUO Jianting;JI Guang; ZHOU Lanzhang; YE Hengqiang
Institute of Metal Research; The Chinese Academy of Science; Shenyang 110016
Download:  PDF(24617KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  High temperature tensile creep behaviors of cast nickel—based superalloy K44 in the temperature range of 850---900℃ and under the applied stress range of 225---380 MPa have been studied. The results indicate that all of the creep curves of test alloys have similar shape: a short primary creep and a dominant accelerated creep stage, and the long accelerated stage is due to the interaction between rafting r’ particles and dislocations. As the creep strain is a softening stage, the accelerated creep can be approximately described by expression. The creep fracture data follow the Monkman--Grant relationship. Cracks originate from the cavities at grain boundary or interdendritic.
Key words:  nickel--based superalloy      high temperature creep      creep fracture      
Received:  10 June 2003     
ZTFLH:  TG111.8  
  TG146.1  
Corresponding Authors:  GUO Jianting     E-mail:  jtguo@imr.ac.cn

Cite this article: 

HOU Jieshan; ZHANG Yulong; GUO Jianting; JI Guang; ZHOU Lanzhang; YE Hengqiang. High Temperature Creep Behavior Of Cast Ni Base Superalloy K44. Acta Metall Sin, 2004, 40(6): 579-.

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y2004/V40/I6/579

[1] Huang X Y. Superalloy. Beijing: Metallurgy Industry Press, 2000: 350(黄晓尧.高温合金.北京:冶金工业出版社,2000:350)
[2] Mukherjee A K, Bird J E, Dorn J E. Trans ASM,1969;62: 155
[3] Mclean M. Acta Metall, 1998; 34: 692
[4] Nabarro F R N, de Villiers H L. Physics of Creep. London:Taylor & Francis Ltd, 1995: 241
[5] Mukherji D, Jiao F, Chen W, Wahi R P. Acta Metall,1991; 39(7) : 1515
[6] Tian S G, Zhou H H, Zhang J H, Yang H C, Xu Y B, Hu Z Q. Mater Sci Eng, 2000; 279A: 160
[7] Maldini M, Lupic V. Scr Metall, 1988; 22: 1737
[8] Hou J S, Guo J T, Zhou L Z, Li G S. J Iron Steel Res,2003; 15(7) : 614(侯介山, 郭建亭, 周兰章, 李谷松. 钢铁研究学报, 2005; 15(7) :614)
[9] Dyson B F, Mclean M. Acta Metall, 1983; 31: 25
[10] Dyson B F, Mclean M. Acta Metall, 1983; 31: 18
[11] Link T, Epishin A, Bruckner U. Acta Metall, 2000; 48:1981
[12] Feng D. Metal Physics (Vol.3) . Beijing: Science Press,1988: 565(冯端. 金属物理学(第三卷)北京; 科学出版社, 1988:565)
[13] Monkman F C, Grant J. Proc ASTM 1956; 56: 593
[1] YUAN Chao; GUO Jianting; YANG Hongcai; WANG Shuhe( Institute of Metal Research; The Chinese Academy of Sciences; Shenyang 110015 School of Materials Science and Metallurgy; Northeastern University; Shenyang 110006)Correspondent. Guo Jianting; professor Tel: 25843531-55493; Fax: (024)23891320;E-mail: jtguo .imr.ac.cn. HIGH TEMPERATURE CREEP OF A DIRECTIONALLY SOLIDIFIED Ni-BASE SUPERALLOY[J]. 金属学报, 1998, 34(8): 858-863.
[2] YUAN Chao ; GUO Jianting ; WANG Tieli ; YANG Hongcai ; WANG Shuhe ;ZHANG Hao (Institute of Metal Research; The Chinese Academy of Sciences; Shenyang 110015)(Materials and Metallurgy School; Northeastern University; Shenyang 110006). THE EFFECT OF APPLIED STRESS ORIENTATION ON THE HIGH TEMPERATURE CREEP BEHAIOUR OF DIRECTIONALLY SOLIDIFIED NICKEL BASE SUPERALLOY[J]. 金属学报, 1998, 34(7): 689-695.
[3] ZHOU Qing; MA Zongyi; ZHAO Jie; BI Jing; ZHU Shijie; WANG Fugang (Materials Engineering Department; Dalian University of Technology; Dalian 116024)(Institute of Metal Research; The Chinese Academy of Sciences; Shenyang 110015). CREEP DEFORMATION AND FRACTURE OF DISPERSOIDS AND SiC PARTICULATES REINFORCED Al BASE COMPOSITES[J]. 金属学报, 1998, 34(1): 107-112.
[4] XIAO Jimei (HSIAO Chimei) (University of Science and Technology Beijing; Beiing 100083). MATERIALS DESIGN AGAINST FRACTURE[J]. 金属学报, 1997, 33(2): 113-125.
[5] WANG Daifeng; LI Geyang; LI Pengxing; WU Renjie(State Key Laboratory for MMCs; Shanghai Jiaotong University; Shanghai 200030)(Manuscript received 1995-04-14; in revised form 1995-09-14). CREEP FRACTURE PROCESS COUPLED WITH CAVITATION IN SiC_p-Al COMPOSITE[J]. 金属学报, 1996, 32(4): 433-437.
[6] QIAO Shengru; LUO Rong; YANG Zheng; KANG Mokuang (Northwestern Polytechnical University; Xi'an)(Manuscript received 2 July; 1993; in revised form 15 December;1993). CREEP BEHAVIOUR OF AN UNIDIRECTIONAL C_F/C_P COMPOSITE AT HIGH TEMPERATURES[J]. 金属学报, 1994, 30(23): 524-52.
[7] AI Suhua;V. LUPINC;M. MALDINI State Key Laboratory for Fracture and Fatigue of Materials; Institute of Metal Research; Academia Sinica; Shenyang; Istituto Perla Tecnologia dei Materiali; Consiglio Nazionale Delle Ricerche; Italy. CREEP FRACTURE IN SINGLE CRYSTALLINE Ni-BASE SUPERALLOYS[J]. 金属学报, 1992, 28(3): 32-37.
[8] YAO Xuexing;KANG Feiyu;CHEN Nanping Tsinghua University; Beijing. CREEP FRACTURE OF INTERMETALLIC COMPOUND (Fe_(60)Ni_(40)_3 (V_(98)Ti_2)[J]. 金属学报, 1991, 27(4): 67-70.
No Suggested Reading articles found!