OVERLOAD EFFECTS ON FATIGUE CRACK PROPA-GATION AT ELEVATED TEMPERATURES IN AN Fe-Ni-BASE SUPERALLOY |
by PEI Hongxun; HE Haicai; SHI Changxu (C. H. Shih) (Institute of Metal Research; Academia Sinica; Shenyang) (Manuscript received 4 February; 1982; revised manuscript 28 September; 1982) |
|
Cite this article:
by PEI Hongxun; HE Haicai; SHI Changxu (C. H. Shih) (Institute of Metal Research; Academia Sinica; Shenyang) (Manuscript received 4 February; 1982; revised manuscript 28 September; 1982). OVERLOAD EFFECTS ON FATIGUE CRACK PROPA-GATION AT ELEVATED TEMPERATURES IN AN Fe-Ni-BASE SUPERALLOY. Acta Metall Sin, 1983, 19(4): 63-148.
|
Abstract Effects of a single overload on fatigue crack growth rate have been investigated at elevated temperatures in an Fe-Ni-base superalloy which has different levels of strength and ductility through different heat treatments. All the overload tests were conducted under the condition of constant load with CCT specimen. Crack length was monitored by using d. c. potential-drop technique. It is clear that the effect of overload represented by retardation cycles, N_D, is decreased at elevated temperatures but still of significance up to 700℃. The peak level of overload stress intensity factor, K_(o.p)., the overload ratio, r, the material yield stress, σ_y, and the crack length, a, at which an overload is applied have great influence on the post overload retardation, behaviour of fatigue crack growth. The retardation cycles, measured at 650℃, can be expressed by the following equation:N_D=N_0exp[m(r/aσ_y)~K_(o.p.)]Conditions of heat treatments have great influence on the effects of overloads. Alloy A with higher ductility and lower yield strength shows greater retardation effect than alloy W under the same overload conditions. The fracture surfaces of specimens subjected to overloading at elevated temperatures have been observed by using optical steromicroscope and SEM along with the measurements of the change of potential drops during the overload tests. Some explanations have been given.
|
Received: 18 April 1983
|
1 Bernard, P. J.; Lindley, T. C.; Richards, C. E., Met. Sci., 11 (1977) , 390.
2 黄玉珊;刘雪惠;傀惠玲,科技资料,西北工业大学,1979.
3 Macha, D, E., Eng. Fract. Mech., 12 (1979) , 1.
4 金属研究所疲劳研究组X光实验室,喷丸强化技术(文集),国防工业出版社,1973,p.73.
5 陈篪;蔡其巩;王仁智,工程断裂力学,国防工业出版社,1978,p.238.
6 胡世炎,破断故障金相分析,国防工业出版社,1978. p.167.
7 Bathias, C.; Vancon, M., Eng. Fract. Mech., 10 (1978) , 404.
8 哈宽富,断裂分析与断裂韧性测试研究,中国金属学会和“断裂”编辑部合编,湖南科学技术出版社,1980,p.31.
9 赖祖涵,ibid.,p.3.
10 Dahl, W.; Roth, G., Strength of Metals and Alloys, Eds. Haasen, P.; Gerold, V.; Kostorz, G., Proc. of the 5th Int. Conf. Aachen, W. Germany, 1979, Vol. 2, p. 1249.
11 Matsuoka, S.; Tanaka, K; Kawahara, M., Eng. Fract. Mech., 8 (1976) , 507. |
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|