| POSITRON ANNIHILATION STUDY ON THE DISTRIBUTION OF DEFECTS IN THE PLASTIC ZoNE A-T CRACK TIP |
| XUE Jiayu; JI Guokun (Institute of High Energy Physics; Academia Sinica; Beijing); TIAN Zhongzhou; CHANG Xiangrong; L(?) Rongbang;XIAO Jimei (Beijing University of Iron and Steel Technology) |
|
Cite this article:
XUE Jiayu; JI Guokun (Institute of High Energy Physics; Academia Sinica; Beijing); TIAN Zhongzhou; CHANG Xiangrong; L(?) Rongbang;XIAO Jimei (Beijing University of Iron and Steel Technology). POSITRON ANNIHILATION STUDY ON THE DISTRIBUTION OF DEFECTS IN THE PLASTIC ZoNE A-T CRACK TIP. Acta Metall Sin, 1983, 19(2): 139-142.
|
|
|
Abstract The plastic zone of crack tip of wedge opening loading specimens were studied by positron annihilation technique. The line-shape parameters of Doppler broadening of annihilating radiation were measured. The value of S parameters was calibrated by specimens with known amount of strain. Then the distribution of the plastic strain in the plastic zone as a measure of the density of defects was determined. Experimental results indicate:1. The dimension of plastic zone is exactly the same as that determined by fracture mechanics.2. The distribution of strain in the plastic zone is not homogeneous.3. There is a high strain area at the very tip of the crack.4. The strain in the plastic zone is increased after electrochemical hydrogenation. Iso-strain curves are expanded preferentially in the direction of greatest shear stress. It is concluded that hydrogen facilitates the propagation of dislocations or the sliding of movable dislocations and vacancies can generate at the same time.
|
|
Received: 18 February 1983
|
1 Seeger, A.; J. Phys., F: Met. Phys., 3 (1973) , 248．
2 Nieminen, R. M.; Manninen, M. J., Positrons in Solids, Springer-Verlag, Berlin 1979, p. 145．
3 季国坤;刘年庆;王淑英;姜健;熊良钺;龙期威,金属学报,17(1981) ,677．
4 堂山昌男;山田 裕;福岛 博,铁鋼,61(1975) ,s234．
5 Alex, F.; Hadnagy, T. D.; Lynn, K. G.; Byrne, J. G., Effect of Hydrogen on Behavior of Materials, Pro. Int. Conf. on Effect of Hydrogen on Behavior of Materials, Ed. Thompson, A. W.; Bernstein, I. M., The Metallurgical Society of AIME, U. S. A., 1976． p. 642．
6 Chu, W. Y.; Hsiao, C. M.; Li, S. Q., Advances in Fracture Research, Pro. 51h Int. Conf. on Fracture, Ed. D. Francois, Vol. 2, Pergamon, 1981, p. 1009．
7 Chu, W. Y.; Hsiao, C. M.; Li, S. Q., Scr. Metall., 13 (1979) , 1063．H |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|