THE FORMATION OF CUBIC TEXTURE IN NICKEL-IRON ALLOY
L. C. TAI;S. Y. CHANG;R. P. LIU Iron and Steel Research Institute; Peking
Cite this article: 

L. C. TAI;S. Y. CHANG;R. P. LIU Iron and Steel Research Institute; Peking. THE FORMATION OF CUBIC TEXTURE IN NICKEL-IRON ALLOY. Acta Metall Sin, 1959, 4(1): 52-59.

Download:  PDF(880KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  The rolling and recrystallization textures in a 50 percent Ni-Fe alloy have been studied,the X-ray pole figure method being employed. Meanwhile, the formation of the cubic texture in thisalloy has also been investigated. The samples used in the experiments have been given two kinds of cold reduction; i. e., (Ⅰ) 94percent and (Ⅱ) 98.4 percent. The samples of class Ⅰ and class Ⅱ both have been annealed for onehour at 500°, 600°, 700°, 800°, 900°, 1000° and 1100℃. From the experiments, the formation of the cubic texture was found to begin at 600℃, be-coming intensified with the raising of the temperature. The cubic texture in the samples belongingto class Ⅱ, which has been annealed for one hour at 1100℃, was found to be sharp and complete. From the experiments it may be shown that the cubic texture in the 50 percent nickel-iron alloyhas been formed from the rotation of~(123) [121] orientation about the [111]-axes for 40°. Theresults seem to verify that the development of the recrystallization texture in the nickel-iron alloyconforms with the theory of orientation growth.
Received:  18 January 1959     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y1959/V4/I1/52

[1] Six, W., Snoek, J. L., u. Burgers, W. G., Der Ingenieur, 49, (1934) , Nr. 52. 参阅 Becker, R., u. Doring, W., Ferromagnetismus, (1939) , S, 431.
[2] Dnhl, O., u. Pawlek, F., Z. Metallkde., 29, (1936) , 266.
[3] Sachs, G., a. Spretnak, J., Trans. AIME, 140, (1940) , 359.
[4] Burgers, W. G., u. Snoek, J. L., Z. Metallkde., 27 (1935) , 158.
[5] Conradt, H. W., Dahl, O. u. Sixtus, K., Z. Metallkde., 32 (1940) , 231.
[6] Custers, J. F. H., Physica, 8 (1941) , 771.
[7] Keeler, J. H. a. Geisler, A. H., Trans, AIME, 203 (1955) , 395; 206, (1956) , 80.
[8] Assmus, F., Boll, R., Gans, D. u. Pfeifer, F., Z. Metallkde., 48, (1957) , 341 (译文, 具有立方织构的硅钢片, 钢铁译丛, 6 (1958) , 41) .
[9] Grewen, J., Segmuller, A., u. Wassermann, c., Arch. Eisenhuttenw., 29, (1958) , 119.
[10] Barrett, C. S., Trans. AIME, 137, (1940) , 128.
[11] Beck, P. A., Sperry, P. R., a. Hu, H., J. appl. phys., 21 (1950) , 420.
No related articles found!
No Suggested Reading articles found!