Be对铸态Al-11Si-0.3Mg合金时效效果的影响

王桂青;边秀房;张均艳

山东大学材料液态结构及其跗性教育部重点实验室;济南 250061；山东建筑工程学院材料科学与工程系;济南 250014

Effect of Be on the Age-Hardening Characteristics of As-Cast Al-11Si-0.3Mg Alloy

WANG Guiqing; BIAN Xiufang; ZHANG Junyan

Key Laboratory of Liquid Structure and Heredity of Materials; Ministry of Education; Shandong University; Jinan 250061;Department of Material Science and Technology; Shandong architectural engineering institute; Jinan 250014

王桂青; 边秀房; 张均艳 . Be对铸态Al-11Si-0.3Mg合金时效效果的影响[J]. 金属学报, 2003, 39(1): 43-46 .
, , . Effect of Be on the Age-Hardening Characteristics of As-Cast Al-11Si-0.3Mg Alloy[J]. Acta Metall Sin, 2003, 39(1): 43-46 .

摘要 参考文献 相关文章 Metrics 全文: PDF(161 KB)   摘要: 采用差分扫描量热分析和硬度测定手段，研究了元素Be对铸态Al-11Si-0.3Mg(质量分数,%)合金时效效果的影响.结果表明:在Al-11Si-0.3Mg合金中加入0.25%的Be,铸态时效时硬化相析出速度加快,析出热效应增大,时效硬化效果明显增加.动力学分析表明:亚稳相 β’的析出符合Avrami公式,Be的加入对亚稳相β’的生长方式参数n影响不大,但明显增大了亚稳相β’的形核率参数k.金属型铝硅合金铸件中存在很多空位“陷阱”,Be与空位结合阻止空位迁移消失可以解释Be对亚稳相β’形核率的影响. 关键词 ： 铝硅合金,  Be添加,  铸态时效     Key words： 收稿日期: 2002-03-21      ZTFLH:  TG166.9   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 王桂青 边秀房 张均艳 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y2003/V39/I1/43 [1] Shivkumar S, Keller C, Apelian D. AFS Trans, 1990; 98:905 [2] Kang H G, Kida M, Miyahara H, Ogi K. AFS Trans, 1999;107: 507 [3] Kaczorowski M, Bindas J. Aluminium, 1994; 9/10: 566 [4] Crowell N, Shivkumar S. AFS Trans, 1995; 103: 721 [5] Caceres C H, Wang Q G. AFS Trans, 1996; 104: 1039 [6] Shivkumar S, Wang L, Keller C. AFS Trans, 1995; 103:705 [7] Bailey W A. J Inst Met, 1967; 95: 443 [8] Ouellet P, Samuel F H. J Mater Sci, 1999; 34: 4671 [9] Murali S, Raman K S. Cast Met, 1991; 4: 31 [10] Gregson P J, Flower H M, Tite C N J. Mater Sci Technol,1986; 2: 349． [11] Xiao T, Youdelis W V. Mater Sci Technol, 1989; 5: 991 [12] Youdelis W V, Fang W. Mater Sci Technol, 1994; 10: 1031 [13] Zhen 1, Fei W D, Kang S B. J Mater Sci, 1997; 32: 1895 [14] Eskin D G, Massardier V, Merle P A. J Mater Sci, 1999;34: 811 [15] Malinov S, Guo Z. Metall Mater Trans A, 2001; 32A: 879 [16] Xu Z Y. The Theory of Phase Transformations. Beijing: Science Press, 1988: 32(徐祖耀.相变原理.北京:科学出版社, 1988:32) [17] Friend C M, Luxton S D. J Mater Sci, 1988; 23: 3173 [18] kim T S, kim T H, Oh K H, I.Lee H. J Mater Sci, 1992;27: 2599 [19] Samuel A M, Samuel F H. AFS Trans, 1994; 102: 397x [1] 李树索; 赵爱民 . 半固态过共晶Al-Si合金显微组织中近球形α相形成机理的研究[J]. 金属学报, 2000, 36(5): 545-549 . [2] 袁晓光; 崔成松 . 时效处理微晶（2024Al）—20Si—5Fe合金的组织及性能[J]. 金属学报, 1999, 35(5): 482-486 . [3] 陈宁;余宗森. Si在Al—0.35wt—%Si合金表面的非平衡偏聚[J]. 金属学报, 1992, 28(9): 63-66. Viewed Full text Abstract Cited   Shared      Discussed