两种涂层和两种钢在液(固)两相流中冲刷与腐蚀的交互作用

金属学报

2004, Vol. 40

Issue (4): 411-415

论文

本期目录 | 过刊浏览

两种涂层和两种钢在液(固)两相流中冲刷与腐蚀的交互作用

张安峰王豫跃邢建东李长久

西安交通大学机械工程学院; 西安 710049

SYNERGISTIC EFFECTS BETWEEN EROSION AND CORROSION OF TWO COATINGS AND TWO STEELS IN TWO--PHASE FLOW

ZHANG Anfeng; WANG Yuyue; XING Jiandong; LI Changjiu

School of Mechanical Engineering; Xi'an Jiaotong University; Xi'an 710049

引用本文:

张安峰; 王豫跃; 邢建东; 李长久 . 两种涂层和两种钢在液(固)两相流中冲刷与腐蚀的交互作用[J]. 金属学报, 2004, 40(4): 411-415 .
, , , , . SYNERGISTIC EFFECTS BETWEEN EROSION AND CORROSION OF TWO COATINGS AND TWO STEELS IN TWO--PHASE FLOW[J]. Acta Metall Sin, 2004, 40(4): 411-415 .

全文: PDF(326 KB)

摘要: 用失重法和电化学法系统地研究了20钢基体、两种Ni基涂层(Ni60JH和Delelo50) 以及对比材料1Cr18Ni9Ti不锈钢在液/固两相流(5%H2SO4+15%石英砂) 中冲刷与腐蚀的交互作用. 实验表明: (1) 在冲刷速率为5---10 m/s时, Ni60JH涂层的耐冲刷腐蚀性能比基体高8---15倍多, 并优于1Cr18Ni9Ti不锈钢; Delelo50涂层的耐冲刷腐蚀性能比基体高3---5倍多. (2) 随着冲刷速率的提高, 4种材料的冲刷腐蚀交互作用失重率在冲刷腐蚀总失重率中所占比例显著增大,由低速时的45%增加到高速时的80%, 从而使冲刷腐蚀交互作用失重率在冲刷腐蚀总失重率中占主导地位.(3) 在纯腐蚀中, Ni60JH涂层和1Cr18Ni9Ti不锈钢以均匀腐蚀为主要特征, 而Delelo50涂层和20钢以选择性腐蚀为主要特征.

关键词 ： Ni基合金涂层, 20钢, 冲刷腐蚀

Abstract：The Synergistic effects between erosion and corrosion of two high velocity oxy--fuel (HVOF) Ni--based coatings (Ni60JH and Delelo50) deposited on a low carbon steel in a liquid--solid two--phase flow were systematically investigated by a weight loss test method and an electrochemical method. And a stainless steel was compared to the two coatings and the substrate. The experiment results indicate: (1) At the erosion rate 5---10 m/s, the erosion--corrosion resistance of Ni60JH and Delelo50 coatings was 8---15 times and 3---5 times higher than that of the substrate, respectively. And the erosion--corrosion resistance of Ni60JH coatings slightly exceeded that of the stainless steel. (2) The weight loss rates of the synergistic effects between erosion and corrosion of the four types of materials changed from 45% to 80% of the total weight loss rates with the erosion rate increasing from 5 m/s to 10 m/s. The weight loss rates of the synergistic effects between erosion and corrosion were primary in the total weight loss rates of erosion and corrosion. (3) In the pure corrosion, the main corrosion characteristic of Ni60JH coating and stainless steel was the uniform corrosion, while that of Delelo50 coating and low carbon steel was the selective corrosion.

Key words： Ni base coating low carbon steel erosion and corrosion

收稿日期: 2003-04-22

ZTFLH:

TG174

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张安峰
	王豫跃
	邢建东
	李长久

44.8K

链接本文:

https://www.ams.org.cn/CN/ 或 https://www.ams.org.cn/CN/Y2004/V40/I4/411

[1] Hodgkiss T, Neville A, Shrestha S. Wear, 1999; 233-235:623
[2] Zelders H G. Metal Corrosion, 1949; 65(1) : 25
[3] Haugen K, Kvernvold O, Ronold A. Wear, 1995; 186-187:179
[4] Bremhors T K, Flint P J. Wear, 1991; 145: 123
[5] Wang Y Y, Li C J, Ohmori A. Mater Protec, 1999; 32(10-B): 128
[6] Toma D, Brandl W, Marginean G. Surf Coat Technol,2001; 138: 149
[7] Li C J, Wang Y Y. J Thermal Spray Technol, 2002; 11:523
[8] Zhang A F, Xing J D, Bao C G. Acta Metall Sin, 2002;38: 521(张安峰,邢建东,鲍崇高.金属学报, 2002;38:521)

[1]	张奇亮, 王玉超, 李光达, 李先军, 黄一, 徐云泽. EH36钢在不同粒径沙砾冲击下的冲刷腐蚀耦合损伤行为[J]. 金属学报, 2023, 59(7): 893-904.
[2]	方信贤白允强王章忠. J4不锈钢及化学镀Ni-P和Ni-Cu-P镀层在液-固两相流中的冲刷腐蚀行为[J]. 金属学报, 2010, 46(2): 239-244.
[3]	董亚伟康国政刘宇杰王弘程晓娟. 室温下20钢高周次单轴棘轮行为的实验研究[J]. 金属学报, 2009, 45(7): 826-829.
[4]	伍翠兰; 罗承萍; 邹敢锋 . 20钢复合渗铬中的相变[J]. 金属学报, 2004, 40(10): 1074-1078 .
[5]	张安峰; 邢建东; 鲍崇高; 贾焕如 . 动态与静态纯腐蚀对定量研究材料冲刷腐蚀交互作用的影响[J]. 金属学报, 2002, 38(5): 521-524 .
[6]	敬和民; 吴欣强; 郑玉贵; 姚治铭; 柯伟 . Mo含量对不锈钢在环烷酸介质中腐蚀与中蚀的影响[J]. 金属学报, 2002, 38(10): 1067-1073 .
[7]	张安峰; 邢建东 . Cr系白口铸铁动态相间腐蚀的定量研究[J]. 金属学报, 2001, 37(1): 77-81 .
[8]	郑玉贵; 姚治铭 . 冲刷与腐蚀的交互作用与耐冲刷腐蚀合金设计[J]. 金属学报, 2000, 36(1): 51-54 .
[9]	戎咏华;王永瑞;王纪文;陈行康;胡赓祥. 20钢奥氏体氮碳共渗后淬火态与时效态的化合物层[J]. 金属学报, 1996, 32(5): 462-468.
[10]	魏翔云;郑玉贵;张玉生;姚治铭;张亚东;张绍鹏;柯伟. 显微组织和元素分布对铁基铸造合金耐冲刷腐蚀性能的影响[J]. 金属学报, 1994, 30(2): 91-96.
[11]	刘向宏;吴晓祖;陈贞国;吴燧华. 界面扩散对316L-20钢复合线机械性能的影响[J]. 金属学报, 1993, 29(7): 40-43.

Viewed

Full text

Abstract

Cited

Shared

Discussed