Please wait a minute...
金属学报  2010, Vol. 46 Issue (2): 227-232    DOI: 10.3724/SP.J.1037.2009.00383
  论文 本期目录 | 过刊浏览 |
Ti粉的高速压制成形及表征
闫志巧;陈峰;蔡一湘;崔亮
广州有色金属研究院粉末冶金研究所; 广州 510650
HIGH VELOCITY COMPACTION AND CHARACTERISTICS OF Ti POWDER
YAN Zhiqiao; CHEN Feng; CAI Yixiang; CUI Liang
Department of Powder Metallurgy; Guangzhou Research Institute of Nonferrous Metals; Guangzhou 510650
引用本文:

闫志巧 陈峰 蔡一湘 崔亮. Ti粉的高速压制成形及表征[J]. 金属学报, 2010, 46(2): 227-232.
, , , . HIGH VELOCITY COMPACTION AND CHARACTERISTICS OF Ti POWDER[J]. Acta Metall Sin, 2010, 46(2): 227-232.

全文: PDF(1364 KB)  
摘要: 

以Ti粉为原料, 高速压制内、外径分别为30和60 mm的圆环状及直径为20 mm的圆柱状两种试样, 探讨冲击能量、装粉量等对压坯密度的影响, 并寻求高速压制过程的合适表征方式. 结果表明: 对于内、外径分别为30和60 mm的圆环试样, 当冲击能量为3.804 kJ时, 可成形的压坯密度最大, 为4.00 g/cm3, 致密度为88.9%; 对于直径为20 mm的圆柱试样, 当冲击能量为1.217 kJ时, 可成形的压坯密度最大, 为4.38 g/cm3,致密度为97.4%. 对于同种试样, 压坯密度随冲击能量的增加而增大, 随装粉量的增加而减小. 质量能量密度能全面地表征试样大小、冲击能量和装粉量等不同参数下的压坯密度.

关键词 Ti粉高速压制压坯密度冲击能量质量能量密度    
Abstract

High velocity compaction (HVC) is a recently developed technology for forming high density metallic parts with high efficiency, whose densification is realized through the strong impact wave generated by liquid–pressure controlled by heavy hamper. This technology is thought to have an excellent balance between properties and cost and has several advantages over other existing forming technologies, including high and homogeneous green density, low cost, low springback and high precision. It is extremely competitive to prepare powder metallurgy parts with high density, high strength, high precision and low cost. With a high hardening rate, Ti powder is difficult to be formed through traditional pressing methods, although advanced forming methods are effective for increasing its density, such as hot–pressing and isothermal–statistic pressing, they are very expensive. HVC would thus be highly attractive to solve these problems of low density and high cost in forming Ti powder. In this paper, the process of HVC forming Ti powder was studied. Two kinds of samples, the rings with 60 mm outer and 30 mm inner diameters and the cylindricals with 20 mm diameter were prepared through HVC, respectively. The influences of impact energy and filling weight on the green density were investigated. The results show that, for the ring samples, the maximum of green density is 4.00 g/cm3 and its relative density is 88.9% at an impact energy of 3.804 kJ. However, for the cylindrical samples, the maximum of green density is 4.38 g/cm3 and its relative density is 97.4% at an impact energy of 1.217 kJ. For the both kinds of samples, the green density increases with increasing impact energy while decreases with increasing filling weight. Impact energy per weight is helpful to characterize the green density obtained at different dimension, impact energy and filling weight.

Key wordsTi powder    high velocity compaction    green density    impact energy    impact energy per weight
收稿日期: 2009-06-08     
作者简介: 闫志巧, 女, 1980年生, 工程师, 博士

[1] Caroline E. Met Powder Rep, 2001; 56: 6
[2] Orban P L. Rom Rep Phys, 2004; 56: 505
[3] Skoglund P. Powder Metall, 2001; 44: 15
[4] Jonsen P, Haggblad H A, Troive L, Furuberg J, Allroth S, Skoglund P. Mater Sci Forum, 2007; 534–536: 289
[5] Eriksson M, Andersson M, Adolfsson E, Carlstrom E. Powder Metall, 2006; 49: 70
[6] Eriksson M, Haggblad H A, Berggren C, Andersson M, Holmersson R, Carlstrom E. Powder Metall, 2004; 47: 335
[7] Souriou D, Goeuriot P, Bonnefoy O, Thomas G, Drapier S, Bourdin S, Lazzarotto L. Adv Sci Technol, 2006; 45: 893
[8] Azhdar B, Stenberg B, Kari L. Polym Test, 2006; 25: 114
[9] Jauffr`es D, Lame O, Vigier G, Dor´e F. Polymer, 2007; 48: 6374
[10] Grinder O, Tengzelius J. Int J Powder Metall, 2008; 44: 41
[11] Wang J Z, Qu X H, Yin H Q, Zhou S Y, Yi M J. Trans Nonferrous Met Soc China, 2008; 18: 1498
(王建忠, 曲选辉, 尹海清, 周晟宇, 易明军. 中国有色金属学报, 2008; 18: 1498)
[12] Wang J Z, Qu X H, Yin H Q, Zhou S Y. Chin J Mater Res, 2008; 22: 589
(王建忠, 曲选辉, 尹海清, 周晟宇. 材料研究学报, 2008; 22: 589)
[13] Wang J Z, Qu X H, Yin H Q, Yi M J, Yuan X J. Powder Technol, 2009; 192: 131
[14] Guo S J, Chi Y, Meng F, Yang X. Mater Sci Eng Powder Metall, 2006; 11: 24
(果世驹, 迟悦, 孟飞, 杨霞. 粉末冶金材料科学与工程, 2006; 11: 24)
[15] Saito T, Takamiya H, Furuta T. Mater Sci Eng, 1998; A243: 273
[16] Chen Z H. Modern Powder Metallurgy Technique. Beijing: Chemical Industry Press, 2007: 322
(陈振华. 现代粉末冶金技术. 北京: 化学工业出版社, 2007: 322)
[17] Huang P Y. Powder Metallurgy Principle. 2nd Ed., Beijing: Metallurgical Industry Press, 1997: 173
(黄培云. 粉末冶金原理(第2版). 北京: 冶金工业出版社, 1997: 173)
[18] Sethi G, Hauck E, German R M. Mater Sci Technol, 2006; 22: 955
[19] Skoglund P, Kejzelman M, Hauer I. Met Powder Rep,2002; 57: 26

[1] 闫志巧 陈峰 蔡一湘. 不同粒径Ti粉的高速压制行为和烧结性能[J]. 金属学报, 2012, 48(3): 379-384.