几种钢延性断裂微观过程的动态观察

徐永波;刘民治;李恒武;苏会和;朱桂秋

AN IN-SITU OBSERVATION OF THE MICROPROCESS OF FAILURE BY DUCTILE FRACTURE IN STEEL

Xu Yongbo;Liu Minzhi;Li Hengwu;Su Huihe;Zhu Guiqiu

引用本文:

徐永波;刘民治;李恒武;苏会和;朱桂秋. 几种钢延性断裂微观过程的动态观察[J]. 金属学报, 1979, 15(3): 367-452.
, , , , . AN IN-SITU OBSERVATION OF THE MICROPROCESS OF FAILURE BY DUCTILE FRACTURE IN STEEL[J]. Acta Metall Sin, 1979, 15(3): 367-452.

全文: PDF(3624 KB)

摘要: 将两种碳素结构钢(15,45)和Cr25Ni20不锈钢的试样在扫描电镜中进行拉伸试验,并对它们的延性断裂的微观过程进行了动态观察。结果表明,裂纹总是优先在夹杂物与金属基体的界面上,孪晶与基体之间的界面上以及σ相与基体之间的界面上成核。前二者的裂纹沿界面传播、钝化并沿拉伸方向变宽;对于后者来说,裂纹成核后,在σ相内解理扩展。最后,裂纹沿切变方向彼此连接并导致断裂。

Abstract：The microprocess of failure by ductile fracture under tensile stress in speci-mens of two carbon steels containing 0.15% and 0.45% C respectively and of a25Cr20Ni type stainless-steel has been examined in-situ in SEM. Cracking wasnucleated preferentially in three different ways, e.g., at the inclusion/matrix, atthe twin/matrix boundary and at the σ-phase/matrix interface. In both the firstand second cases, the cracks were formed at the inter-faces and widened in thesteel matrix along the direction of applied stress. In the third case the crackswere nucleated at the σ-phase/matrix interface and grown into σ-phase particle.As the applied stress became greater and greater, other oracks nearby appear tocoalescence along the shear direction of the steel with the result of total failure.

收稿日期: 1979-03-18

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	徐永波
	刘民治
	李恒武
	苏会和
	朱桂秋
44.8K

链接本文:

https://www.ams.org.cn/CN/ 或 https://www.ams.org.cn/CN/Y1979/V15/I3/367

[1] Oron. M. and Tirosh. J., Scanning Electron Microscopy: System and Applications, ed. by W. C. Nixon, Institute of Physics. London, 1973． p. 94．
[2] Dingley, D. J., ibid., 112．
[3] Hazra. J. and Caffarelli. D, et al., ibid., 100．
[4] Roberts. W., Acta Met., 24 (1976) , 745．
[5] Sleeswyk. A. W., Acta Met., 10 (1962) . 803．
[6] Petch. N. J., Fracture. Vol. I, ed. by H. Liebowitz, Academic. New York, 1968． p. 375．
[7] Puttick, K. E., Phil. Mag., 4 (1959) . 964．
[8] Gurdland, J. and Plateau. J.. ASM Trans. Quart., 56 (1963) , 442．
[9] 小野寺,日本金属学会志,39 (1975) ,648．
[10] Ashby, M. F., Phil. Mag., 14 (1966) . 1157．
[11] Lewis. M. H., Acta Met., 14 (1966) , 1421．
[12] Knott. J. F., Advances in Research on the Strength and Fracture of Materials. Vol. I. Ed. by D, M. R. Taplin. 4th Int. Conf. Fracture, June 1977, University of Waterloo, Canada, p. 61

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed