工业纯Al的缝隙腐蚀再钝化电位

梁成浩

大连理工大学

REPASSIVATION POTENTIAL FOR CREVICE CORROSION OF COMMERCIALLY PURE ALUMINUM

LIANG Chenghao(Dalian University of Technology)(Manuscript received 23 June;1993;in revised form 23 September;1993)

梁成浩. 工业纯Al的缝隙腐蚀再钝化电位[J]. 金属学报, 1994, 30(16): 165-168.
. REPASSIVATION POTENTIAL FOR CREVICE CORROSION OF COMMERCIALLY PURE ALUMINUM[J]. Acta Metall Sin, 1994, 30(16): 165-168.

摘要 参考文献 相关文章 Metrics 全文: PDF(237 KB)   摘要: 工业纯Ａｌ的缝隙腐蚀再钝化电位ＥＲ是缝隙结构的特征值，与缝隙腐蚀下限电位ＶＣＲＥＶ一致，比孔蚀电位负约１００ｍＶ，说明缝隙腐蚀更易发生． 关键词 ： 工业纯Ａｌ,  缝隙腐蚀再钝化电位,  孔蚀电位     Abstract：The repassivation potential for crevice corrosion(ER) of commercially pure Al was measured successfully using the method developed for stainless steels.The ER is a characteristic value depending on the geometry of the crevice configuration.The ER coincides with that lower limit of critical potential VCREV for crevice corrosion.The results showed that ER of commercially pure Al was less noble than the pitting potential by 100 mV,confirming that crevice corrosion is the more easily occurring type even in commercially pure Al.Correspondent:LIANG Chenghao,associate professor,(Dalian University of Technology,Dalian 116012) Key words： commercially pure aluminum    repassivation potential crevice corrosion    pitting poteneial      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 梁成浩 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1994/V30/I16/165 1川茂男,久松敬弘．防食技术,1980:29(1):372梁成浩,火时中,谷金香,徐儒庸．太阳能学报,1996:7(3):3223ForoulisZ,A,ThubriarMJ．JElectrochemSOC,1969;116:9064川茂男,张恒,久松敬弘．防食技术,1983;32(3):1495梁成浩,原正,川茂男．防食技术,1988;37(11):6792 [1] 侯嘉鹏, 孙朋飞, 王强, 张振军, 张哲峰. 突破强度-导电率制约关系：晶粒异构设计[J]. 金属学报, 2022, 58(11): 1467-1477. Viewed Full text Abstract Cited   Shared      Discussed