金属学报  2009, Vol. 45 Issue (5): 547-552    
  论文 本期目录 | 过刊浏览 |
拉晶速率对Ni3Al基单晶合金IC6SX凝固组织和高温持久性能的影响
蒋立武1;李树索1;邱自成2;韩雅芳1;3
1. 北京航空航天大学材料科学与工程学院; 北京 100083
2. 中国一航贵州新艺机械厂; 贵阳 561114
3. 北京航空材料研究院; 北京 100095
EFFECTS OF WITHDRAWAL RATE ON MICROSTRUCTURE AND STRESS RUPTURE PROPERTIES OF A Ni3Al–BASED SINGLE CRYSTAL SUPERALLOY IC6SX
JIANG Liwu 1; LI Shusuo 1; QIU Zicheng 2; HAN Yafang 1;3
1. School of Materials Science and Engineering; Beihang University; Beijing 100083
2. Xinyi Machinery Factory; China Aviation Industry Corporation I; Guiyang 561114
3. Beijing Institute of Aeronautical Materials; Beijing 100095
引用本文:

蒋立武 李树索 邱自成 韩雅芳. 拉晶速率对Ni3Al基单晶合金IC6SX凝固组织和高温持久性能的影响[J]. 金属学报, 2009, 45(5): 547-552.
, , , . EFFECTS OF WITHDRAWAL RATE ON MICROSTRUCTURE AND STRESS RUPTURE PROPERTIES OF A Ni3Al–BASED SINGLE CRYSTAL SUPERALLOY IC6SX[J]. Acta Metall Sin, 2009, 45(5): 547-552.

全文: PDF(3263 KB)  
摘要: 

采用螺旋选晶法制备Ni3Al基单晶合金IC6SX试棒, 研究了不同拉晶速率对凝固组织和高温持久性能的影响. 结果表明, Ni3Al基单晶合金IC6SX凝固组织为树枝状, 随着拉晶速率从1.5 mm/min增加到6 mm/min, 一次枝晶间距逐渐减小. 与普通镍基高温合金不同, 位于枝晶干处的次生γ'相尺寸比枝晶间处的大. 随着拉晶速率的增加, 枝晶干和枝晶间处的γ'相尺寸都逐渐减小, 由不规则形状逐渐立方化, 枝晶间处的初生γ'相的数量逐渐增多. 一次枝晶间距和γ'相尺寸对高温持久性能影响显著, 随着拉晶速率的增加, 组织细化, 铸态IC6SX单晶合金的高温持久寿命增加.

关键词 Ni3Al单晶合金拉晶速率一次枝晶间距高温持久    
Abstract

As high–temperature structural materials, Ni3Al possesses excellent comprehensive properties, such as good strength at high temperature, low density, excellent ductility, superior oxidation resistance and so on. A high performance Ni3Al–based alloys IC6 has been developed by authors and successfully applied for aero–engine vanes. It has been found that the high temperature mechanical properties of the single crystal IC6 alloy are superior to both equiaxial crystal and directional columnar IC6 alloys. A lot of research work for IC6 alloys has been carried out on the equiaxial crystal and directional columnar IC6 alloys during the last two decades. In order to further improve the mechanical properties and meet the requirement of turbine blade materials, the single crystal Ni3Al–based alloy IC6SX has been developed and the research work on single crystal processing has been carried out recently. In the present investigation, the influence of withdrawal rate on the microstructure and stress rupture properties of a Ni3Al–based single crystal superalloy IC6SX were studied. The single crystal specimens were prepared by screw selection crystal method. The microstructure analysis by SEM and OM reveals that the microstructure of specimens is dendrite structure, and the primary dendrite arm spacing decreases from 480 μm to 390 μm with withdrawal rate increasing from 1.5 mm/min to 6.0 mm/min. Different with the common Ni–based superalloys, the size of the γ' phase in the dendritic core is larger than that in the interdendritic area. As withdrawal rate increases  the size of the γ' phase decreases. The average size of the γ' phase in the dendritic core decreases from 3 μm to 1.3 μm and the average size of the γ' phase in the interdendritic area decreases from 1.6 μm to 0.8 μm with withdrawal rate increasing. Meanwhile, the shape of γ' phase tends to regular, and more primary eutectic γ' phase precipitates form in the interdendrite region. The volume fractions of primary eutectic γ' phase precipitates are 0.07\%, 0.18\%, 0.36\% and 0.77\%, respectively at the withdrawal rates 1.5, 3.0, 4.5 and 6.0 mm/min. It has been found that the stress rupture properties are affected by primary dendrite arm spacing and size of γ' phase significantly, i.e., the rupture lives of as-cast specimens increase with increasing withdrawal rate, which may be attributed to the refining microstructure. The above results can be used to optimize the process design for both single crystal specimen preparation and component fabrication of the present alloy IC6SX and may be used as a reference for other Ni--based single crystal alloys.

Key wordsNi3Al    single crystal superalloy    withdrawal rate    primary dendrite arm spacing    stress rupture
收稿日期: 2008-10-21     
ZTFLH: 

TG111.7

 
作者简介: 蒋立武, 男, 1983年生, 博士生

[1] Zhang Y G, Han Y F, Chen G L, Guo J T, Wan X J, Feng D. Structural Intermetallics. Beijing: National Defence Industry Press, 2001: 560
(张永刚, 韩雅芳, 陈国良, 郭建亭, 万晓景, 冯 涤. 金属间化合物结构材料. 北京: 国防工业出版社, 2001: 560)
[2] Wilson B C, Cutler E R, Fuchs G E. Mater Sci Eng, 2008; A479: 356
[3] Liu W W, Tang D Z. J Mater Eng, 2006; 1: 16
(刘维维, 唐定中. 材料工程, 2006; 1: 16)
[4] Li J G, Wang Z, Jin T, Zhao N R, Sun X F, Guan H R, Hu Z Q. Mater Mech Eng, 2002; 3: 17
(李金国, 王 震, 金 涛, 赵乃仁, 孙晓峰, 管恒荣, 胡壮麒. 机械工程材料, 2002; 3: 17))
[5] Raj S V, Locci I E. Intermetallics, 2001; 9: 217
[6] Wu Q, Si N C, Guo Y, Li D Y. Chin J Nonferrous Met, 2007; 7: 1101
(吴 强, 司乃潮, 郭 毅, 李达云. 中国有色金属学报, 2007; 7: 1101)
[7] Wang K F, Guo J J, Li C Y, Mi G F, Fu H Z. Foundry, 2007; 56: 1186
(王狂飞, 郭景杰, 历长云, 米国发, 傅恒志. 铸造, 2007; 56: 1186)
[8] Карсев Б Е, translated by Gui Z L, Zhang X H, Xia M R, Sun L. Casting Turbine Blade Manufacturing Engineering . Beijing: Beijing Institute of Aeronautical Materials,
1998: 195
(Карсев Б Е著, 桂忠楼, 张鑫华, 夏明仁, 孙 \ \ 理译. 铸造涡轮叶片制造工程. 北京: 北京航空材料研究院, 1998: 195)
[9] Pan J S, Tong J M, Tian M B. Foundation of Material Science. Beijing: Tsinghua University Press, 1998: 503
(潘金生, 仝健民, 田民波. 材料科学基础. 北京: 清华大学出版社, 1998: 503)
[10] Beattie H J, Hagel W C. Trans AIME, 1965; 233: 277

[1] 苏勇,田素贵,于慧臣,于莉丽. 镍基单晶高温合金中温稳态蠕变期间的变形机制*[J]. 金属学报, 2015, 51(12): 1472-1480.
[2] 赵海根,李树索,裴延玲,宫声凯,徐惠彬. Ni3Al基单晶合金IC21的微观组织及力学性能[J]. 金属学报, 2015, 51(10): 1279-1287.
[3] 丁智 张军 王常帅 苏海军 刘林 傅恒志. DZ125镍基高温合金高温持久断裂后的位错组态[J]. 金属学报, 2011, 47(1): 47-52.
[4] 水丽 金涛 胡壮麒. [011]取向镍基单晶合金蠕变特征[J]. 金属学报, 2009, 45(11): 1349-1355.
[5] 李亚楠; 何迪; 李树索; 韩雅芳 . Ni3Al基单晶合金IC6sx的表面再结晶[J]. 金属学报, 2008, 44(4): 391-396 .
[6] 李尚平 骆合力 曹栩 张喜娥 冯涤. DZ125合金表面碳化铬/Ni3Al堆焊涂层显微组织[J]. 金属学报, 2008, 44(12): 1450-1454.
[7] 赵毅; 赵九洲; 胡壮麒 . 过冷Ni3Al熔体形核的分子动力学模拟[J]. 金属学报, 2008, 44(10): 1157-1160 .
[8] 李尚平; 骆合力; 冯涤; 曹栩; 张喜娥 . Cr3C2/Ni3Al复合材料的高温稳定性[J]. 金属学报, 2007, 43(4): 439-443 .
[9] 彭平; 陈律; 周惦武; 田泽安; 韩绍昌; 金涛 ; 胡壮麒 . Re与Ru合金化对Ni/Ni3Al相界电子结构影响的第一原理研究[J]. 金属学报, 2007, 43(2): 137-143 .
[10] 孟晓娜; 孙文儒; 郭守仁; 卢德忠; 李娜 . 磷对Ni3Al凝固组织的影响[J]. 金属学报, 2004, 40(6): 613-.
[11] 李玉芳; 郭建亭; 周兰章; 叶恒强 . 再结晶Ni3Al(Zr)合金的环境脆性[J]. 金属学报, 2004, 40(5): 499-503 .
[12] 张迪; 单际国; 陈武柱; 任家烈 . Ni-Al系金属间化合物光束堆焊层的成形及析出相特征[J]. 金属学报, 2004, 40(5): 483-488 .
[13] 李玉芳; 郭建亭; 周兰章; 叶恒强 . 含Zr多晶Ni3Al合金在不同热处理温度下的组织与性能[J]. 金属学报, 2003, 39(8): 821-825 .
[14] 岳珠峰; 吕震宙 . 双剪切试样在镍基单晶合金蠕变变形损伤和寿命研究中的应用[J]. 金属学报, 2002, 38(8): 809-813 .
[15] 胡静; 张云; 林栋梁 . Ni3Al中B和Mg的非平衡晶界共偏聚[J]. 金属学报, 2002, 38(8): 829-834 .