Zr基块体非晶合金在过冷液相区的超塑性流变行为

沈军; 王刚; 孙剑飞; 陈德民; 邢大伟; 周彼德

(哈尔滨工业大学材料科学与工程学院; 哈尔滨 150001; 哈尔滨工程大学航天工程系; 哈尔滨 150001

Superplastic Flow Behavior of Zr Base Bulk Metallic Glass in Supercooled Liquid Region

SHEN Jun; WANG Gang; SUN Jianfei;CHEN Demin; XING Dawei; ZHOU Bide

School of Material Science and Engineering; Harbin Institute of Technology; Harbin 150001; Department of Aerospace Engineering; Harbin Engineering University; Harbin 150001

引用本文:

沈军; 王刚; 孙剑飞; 陈德民; 邢大伟; 周彼德 . Zr基块体非晶合金在过冷液相区的超塑性流变行为[J]. 金属学报, 2004, 40(5): 518-522 .
, , , , , . Superplastic Flow Behavior of Zr Base Bulk Metallic Glass in Supercooled Liquid Region[J]. Acta Metall Sin, 2004, 40(5): 518-522 .

全文: PDF(4783 KB)

摘要: 研究了Zr41.25Ti13.75Ni10Cu12.5Be22.5 (原子分数, %)块体非晶合金在玻璃转变终了温度Tg end附近的4个特征温度点(616, 636, 656和676 K)的等温拉伸行为. 结果表明, 块体非晶合金的超塑性能与环境温度及拉伸速度紧密相关. 在656 K, 以5 mm/min的速度拉伸时, 获得了1625%的最大延伸率. 利用速度突变法测出了 636, 656及676 K时的应力敏感指数分别为0.25, 0.65和0.93. 利用自由体积模型对块体非晶合金的超塑性流变行为的微观机制进行了分析.

关键词 ：锆基块体非晶合金, 过冷液相区, 超塑性

Abstract：Isothermal tensile tests of Zr41.25Ti13.75Ni10Cu12.5Be22.5 bulk metallic glass in supercooled liquid region are carried out at four characteristic temperatures of 616 , 636, 656 and 676 K which are in the vicinity of the end temperature of glass transition. Experimental results indicate that the superplastic flow behaviors of the material, viz., the flow stress and the elongation depend strongly on the testing temperature and tensile rate. The elongation increases firstly and then decreases with increasing rate and the maximum elongation reaches 1625% at 656 K and 5 mm/min. The strain rate sensitivity exponents determined by using Backofen method are 0.25, 0.65 and 0.93 at 636 , 656 and 676 K, respectively. The free volume model is used to interpret the observed superplastic flow behavior.

Key words： Zr-based bulk metallic glass supercooled liquid region superplasticity

收稿日期: 2003-05-29

ZTFLH:

TG139.8

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	沈军
	王刚
	孙剑飞
	陈德民
	邢大伟
	周彼德
44.8K

链接本文:

https://www.ams.org.cn/CN/ 或 https://www.ams.org.cn/CN/Y2004/V40/I5/518

[1] Zhang Q S, Guo D Y, Wang A M, Zhang H F, Ding B Z, Hu Z Q. Intermetallics, 2002; 10:1197
[2] Wang W H, Wei Q, Friedrich S. J Mater Sci, 2000; 35: 2291
[3] Jiang S W, Qi M. Res Met Mater, 2003; 29(1) : 44(姜淑文,齐民.金属材料研究,2003;29(1) :44)
[4] Bian Z, Chen G L, He G, Hui X D. Mater Sci Eng, 2001; A316:135
[5] Liu L, Wu Z F, Zhang J. J Alloys Compd, 2002; 339:90
[6] Zhang Y, Ji Y F, Zhao D Q, Wang R J, Pan M X, Dong Y D, Wang W H. Scr Mater, 2001; 44:1107
[7] Kawamura Y, Shibata T, Inoue A, Masumoto T. Scr Mater, 1997; 37: 431．
[8] Kawamura Y, Nakamura T, Kato H, Mano H, Inoue A. Mater Sci Eng, 2001; A304-306:674
[9] Kawamura Y, Nakamura T, Inoue A. Scr Mater, 1998; 39: 301
[10] Nieh T G, Wadsworth J, Liu C T, Ohkubo T, Hirotsu Y. Acta Mater, 2001; 49:2887
[11] Nieh T G, Mukai T, Liu C T. Scr Mater, 1999; 40:1021
[12] Reger-Leonhard A, Heilmaier M, Eckert J. Scr Mater, 2000; 43:459
[13] Johnson W L, Lu J, Demetriou M D. Intermetallics, 2002; 10:1039
[14] Lee K S, Ha T K, Ahn S, Chang Y W. J Non-Cryst Solids, 2003; 317:193
[15] Saotome Y, Hatori T, Zhang T, Inoue A. Mater Sci Eng, 2001; A304-306:716
[16] Saotome Y, Itoh K, Zhang T, Inoue A. Scr Mater, 2001; 44:1541
[17] Wu S D. The Principle of Metal Superplastic Formation. Beijing: National Defense Industry Press, 1997:9(吴诗惇.金属超塑性变形理论.北京;国防工业出版社,1997:9)
[18] Wang W H, Bai H Y, Luo J L, Wang R J, Jin D. Phys Rev, 2000, 62B: 25
[19] Spaepen F. Acta Metall, 1977; 25:407
[20] Beukel V D. Key Eng Mater, 1993; 81-83: 3

[1]	刘帅帅, 侯超楠, 王恩刚, 贾鹏. Zr₆₁Cu₂₅Al₁₂Ti₂ 和Zr_52.5Cu_17.9Ni_14.6Al₁₀Ti₅ 块体非晶合金过冷液相区的塑性流变行为[J]. 金属学报, 2022, 58(6): 807-815.
[2]	王慧远, 夏楠, 布如宇, 王珵, 查敏, 杨治政. 低合金化高性能变形镁合金研究现状及展望[J]. 金属学报, 2021, 57(11): 1429-1437.
[3]	谢广明, 马宗义, 薛鹏, 骆宗安, 王国栋. 工具转速对搅拌摩擦加工Mg-Zn-Y-Zr耐热镁合金超塑性行为的影响[J]. 金属学报, 2018, 54(12): 1745-1755.
[4]	王慧远, 张行, 徐新宇, 查敏, 王珵, 马品奎, 管志平. 超塑性轻合金组织稳定性的研究进展及展望[J]. 金属学报, 2018, 54(11): 1618-1624.
[5]	杨超,王继杰,马宗义,倪丁瑞,付明杰,李晓华,曾元松. 7B04铝合金薄板的搅拌摩擦焊接及接头低温超塑性研究^*[J]. 金属学报, 2015, 51(12): 1449-1456.
[6]	付明杰, 韩秀全, 吴为, 张建伟. Ti-23Al-17Nb合金板材超塑性研究^*[J]. 金属学报, 2014, 50(8): 955-961.
[7]	马品奎, 宋玉泉. 超塑性自由胀形的双目立体视觉测量研究^*[J]. 金属学报, 2014, 50(4): 471-478.
[8]	管志平,马品奎,宋玉泉. 超塑性拉伸断裂分析[J]. 金属学报, 2013, 49(8): 1003-1011.
[9]	沈军,冯艾寒. Ti₂AlNb基合金微观组织调制及热成形研究进展[J]. 金属学报, 2013, 49(11): 1286-1294.
[10]	侯介山,周兰章,郭建亭,袁超. NiAl合金超塑性的人工神经网络预测[J]. 金属学报, 2013, 49(11): 1333-1338.
[11]	曹富荣丁桦王昭东李英龙管仁国崔建忠. 超轻β固溶体Mg-11Li-3Zn合金的准超塑性与变形机理[J]. 金属学报, 2012, 48(2): 250-256.
[12]	王刚徐磊王永郑卓崔玉友杨锐. 高Nb-TiAl合金高温塑性变形行为及微观组织演化[J]. 金属学报, 2011, 47(5): 587-593.
[13]	曹富荣管仁国丁桦李英龙周舸崔建忠. 超轻α固溶体基Mg-6Li-3Zn合金的位错蠕变[J]. 金属学报, 2010, 46(6): 715-722.
[14]	黄彩云谌祺柳林. 无Ni型锆基块体非晶合金在生物模拟体液中的摩擦磨损性能[J]. 金属学报, 2010, 46(6): 681-686.
[15]	宋玉泉马品奎管志平. 超塑性非球面自由胀形的测量[J]. 金属学报, 2010, 46(1): 1-5.

Viewed

Full text

Abstract

Cited

Shared

Discussed