金属学报  1986, Vol. 22 Issue (2): 27-30

论文 本期目录 | 过刊浏览 |

氢对不锈钢室温蠕变的影响

褚武扬;丁威;肖纪美

北京钢铁学院;北京钢铁学院;北京钢铁学院

EFFECT OF HYDROGEN ON CREEP IN AUSTENITIC STAINLESS STEEL

CHU Wuyang; DING Wei; XIAO Jimei (Beijing University of Iron and Steel Technology)

褚武扬;丁威;肖纪美. 氢对不锈钢室温蠕变的影响[J]. 金属学报, 1986, 22(2): 27-30.
, , . EFFECT OF HYDROGEN ON CREEP IN AUSTENITIC STAINLESS STEEL[J]. Acta Metall Sin, 1986, 22(2): 27-30.

摘要 参考文献 相关文章 Metrics 全文: PDF(304 KB)   摘要: <正> 一、引言 氢总是促进铁和钢的蠕变,但解释并不一致,迄今为止,尚未研究过氢对奥氏体不锈钢蠕变的影响。已经表明,即使是不产生α′马氏体的稳定型不锈钢(如310)也能产生氢致滞后开裂,而且发生在氢致滞后塑性变形之后。 Abstract：The dynamic charging does not influence on the creep rate of type 321 austenitic stainless steel if the initial strain was less than 2%, in which the amounts evolving hydrogen after test were below 1.5 ppm (by wt). However, the creep rate increased markedly when the initial strain was larger then 8% or the specimen was precharged for a long time. In the case the corresponding amount evolving hydrogen was 5 to 12 ppm (by wt). 收稿日期: 1986-02-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 褚武扬 丁威 肖纪美 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1986/V22/I2/27 1 Shin, K.S.; Park, C.G.; Nagakawa, J.; Meshii, M., Scr. Metall., 14 (1980) , 279． 2 Oriani, R.A.; Josephic, P.H., Acta Metall., 27 (1979) , 997; 29 (1981) , 669． 3 Chu,W.Y.(褚武扬);Yao,J.(姚京);Hsiao,C.M.(肖纪美),Metall.Trans.,15A (1984) ,729． 4 姚京;褚武扬;肖纪美,金属学报,20 (1984) ,A124 5 Chu,W.Y.(褚武扬);Wang,H.L.(王核力);Hsiao,C.M.(肖纪美),Corrosion,40 (1984) ,487． 6 乔利杰;褚武扬;肖纪美,奥氏体不锈钢Ⅲ型试样的应力腐蚀与氢致开裂,1984,待发表 7 王燕斌;褚武扬;肖纪美,金属学报,18 (1982) ,673． 8 褚武扬;肖纪美;李世琼,金属学报,17 (1981) ,10．R No related articles found! Viewed Full text Abstract Cited   Shared      Discussed