Ti系合金的贮氢特性
李玉凤;徐德明;陈于才
冶金工业部钢铁研究总院;冶金工业部钢铁研究总院;冶金工业部钢铁研究总院
ON THE HYDROGEN STORING PROPERTY OF Ti SYSTEM ALLOYS
LI Yufeng; XU Demin; CHEN Yucai (Central Iron and Steel Research Institute; Ministry of Metallurgical Industry; Beijing)
引用本文:

李玉凤;徐德明;陈于才. Ti系合金的贮氢特性[J]. 金属学报, 1983, 19(5): 39-45.
, , . ON THE HYDROGEN STORING PROPERTY OF Ti SYSTEM ALLOYS[J]. Acta Metall Sin, 1983, 19(5): 39-45.

全文: PDF(553 KB)  
摘要: 研究了Ti-Mn二元合金以及添加其它元素的多元合金的贮氢特性。结果表明TiMn_(1.5),Ti_(0.8)Zr_(0.2)Mn_(0.8)Cr_(1.0)Fe_(0.2)和Ti_(0.8)Zr_(0.2)Mn_(0.8)Cr_(1.0)Co_(.2)等多种合金都具有易活化、吸氢量大(≥200mL/g)、在20℃及常压下的可逆吸放氢量大于160mL/g以及价格低廉等特点。这类合金将具有广阔的应用前景。
Abstract:The hydrogen storing property of either binary Ti-Mn or similar polynary system Ti alloys has been investigated. It showed that TiMn_(1.5) and a variety of Ti_(0.8) Zr_(0.2) Mn_(0.8) Cr_(1.0) Fe_(0.2) and Ti_(0.8) Zr0_(0.2) Mn_(0.8) Cr_(1.0) Co_(0.2) alloys are characterized by easy activation, abundant hydrogen absorption beyond 200 mL/g and reversible desorption more than 160 mL/g at 20℃ under atmospheric pressure, as well as cheap cost for preparation. It seems that such alloys may be prospective.
收稿日期: 1983-05-18     
1 天野宗幸,佐佐木靖男,松本武彦,日本金属学会誌,43 (1979) ,809.
2 Reilly, J.J.; Wiswall, R.H., J. Inorg. Chem., 13 (1974) , 218.
3 山下敏夫;蒲生孝治;森昭良夫;福田雅太郎,日本金属学会誌,41 (1977) ,148.
4 Gamo, T.; Moriwaki, Y.; Yanagihara, N.; Yamashita, T.; Iwaki, T., Hydrogen Energy Progress Proc. of the 3rd World Hydrogen Energy Conf., Vol. 4, Eds., Veziroglu, T. N.; Fueki, K.; Ohta, T., 1980, Tokyo, p. 2127.
5 蒲生孝治,森脇良夫,山下敏夫,福田雅太郎,日本特许公报,56-20346,(1981) .
6 蒲生孝治,森脇良夫;山下敏夫;福田雅太郎,日本特许公报,54-25911,(1979) .
7 Johnson, J. R.; Reilly, J. J., BNL-25215, (1978) .
8 泉山;昌夫,日本公開特许公报,50-75187 (1975) .
9 Reilly, J.J.; Johnson, J.R., 1st World Hydrogen Energy Conf., Vol. 2, Ed. Veziroglu, T. N., Miami Beach, Florida, USA, 1976, p.8B-3.
10 蒲生孝治;森脇良夫,山下敏夫;福田雅太郎,日本公開特许公报,54-45608,(1979) .
11 蒲生孝治;森脇良夫,山下敏夫;福田雅太郎,日本特许公报,56-15772,(1981) .
12 李玉凤;徐德明;陈于才,仪表材料,13 (1982) ,№ 4,53.h
No related articles found!