Corrosion Behavior of GH4169 Alloy in NaCl Solution Spray Environment at 600oC

  • ZHANG Weidong ,
  • CUI Yu ,
  • LIU Li ,
  • WANG Wenquan ,
  • LIU Rui ,
  • LI Rui ,
  • WANG Fuhui
Expand
  • 1.Shenyang National Laboratory for Materials Science, Northeastern University, Shenyang 110819, China
    2.Shi-changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China
LIU Li, professor, Tel: 15904072057, E-mail: liuli@mail.neu.edu.cn;
CUI Yu, associate researcher, Tel: 15004059681, E-mail: ycui@imr.ac.cn

Received date: 2022-04-29

  Revised date: 2022-07-27

  Online published: 2022-08-29

Supported by

Key Projects of Enterprise Innovation Joint Fund of National Natural Science Fundation of China(U20B2026)

Abstract

The corrosion behavior of engine materials of airplanes working in marine environments is accelerated by the synergistic effects of NaCl particles and water vapor at high temperatures. This work examined the corrosion behavior of GH4169 alloy with a NaCl solution spraying at 600oC using an oxidation kinetics test and micro characterization technology in the aspects of corrosion kinetics, corrosion layer phase composition, and microstructure. The weight gain of the GH4169 alloy corroded in the NaCl solution spraying environment was much lower than that in solid NaCl + wet O2 after 20 h corrosion at 600oC. The corrosion products of the GH4169 alloy in the NaCl solution spray environment were less complex than those in the solid NaCl + wet O2 environment, but they were denser. In addition, Cl was concentrated in the inner layer of the corrosion products and accelerated the corrosion of GH4169 alloy via an “active oxidation” mechanism at the initial stage. When NaCl deposition was increased, the corrosion mechanism of GH4169 alloy changed gradually to Cl-induced “active oxidation.” The sensitivity of GH4169 alloy in the NaCl solution spray environment at 600oC was analyzed. Overall, the sensitivity of elements in GH4169 alloy to chlorine activated corrosion was Ti > Al > Nb, Cr > Fe > Mo, Ni, whereas the sensitivity of the oxides was TiO2 > MoO2 > Cr2O3(Nb2O5) > Fe2O3 > Al2O3 > NiO.

Cite this article

ZHANG Weidong , CUI Yu , LIU Li , WANG Wenquan , LIU Rui , LI Rui , WANG Fuhui . Corrosion Behavior of GH4169 Alloy in NaCl Solution Spray Environment at 600oC[J]. Acta Metall Sin, 2023 , 59(11) : 1475 -1486 . DOI: 10.11900/0412.1961.2022.00204

References

1 Wang C, Jiang F, Wang F. Corrosion inhibition of 304 stainless steel by nano-sized Ti/silicone coatings in an environment containing NaCl and water vapor at 400-600oC [J]. Oxid. Met., 2004, 62: 1
2 Shu Y H, Wang F H, Wu W T. Synergestic effect of NaCl and water vapor on the corrosion of Ti60 alloy at 500-700oC [J]. Oxid. Met., 1999, 52: 463
3 Shu Y H, Wang F H, Wu W T. Synergistic effect of NaCl and water vapor on the corrosion of 1Cr-11Ni-2W-2Mo-V steel at 500-700oC [J]. Oxid. Met., 1999, 51: 97
4 Shu Y H, Wang F H, Wu W T. Corrosion behavior of pure Cr with a solid NaCl deposit in O2 plus water vapor [J]. Oxid. Met., 2000, 54: 457
5 Wang F H, Geng S J, Zhu S L. Corrosion behavior of a sputtered K38G nanocrystalline coating with a solid NaCl deposit in wet oxygen at 600 to 700oC [J]. Oxid. Met., 2002, 58: 185
6 Wang F, Shu Y. Influence of Cr content on the corrosion of Fe-Cr alloys: The synergistic effect of NaCl and water vapor [J]. Oxid. Met., 2003, 59: 201
7 Grabke H J, Reese E, Spiegel M. The effects of chlorides, hydrogen chloride, and sulfur dioxide in the oxidation of steels below deposits [J]. Corros. Sci., 1995, 37: 1023
8 Liu L, Li Y, Zeng C L, et al. Electrochemical impedance spectroscopy (EIS) studies of the corrosion of pure Fe and Cr at 600oC under solid NaCl deposit in water vapor [J]. Electrochim. Acta, 2006, 51: 4736
9 Tang Y B, Liu L, Li Y, et al. The electrochemical corrosion mechanisms of pure Cr with NaCl deposit in water vapor at 600oC [J]. J. Electrochem. Soc., 2011, 158: C237
10 Fan L, Liu L, Cao M, et al. Corrosion behavior of pure Ti under a solid NaCl deposit in a wet oxygen flow at 600oC [J]. Metals, 2016, 6: 72
11 Fan L, Liu L, Yu Z F, et al. Corrosion behavior of Ti60 alloy under a solid NaCl deposit in wet oxygen flow at 600oC [J]. Sci. Rep, 2016, 6: 29019
12 Ciszak C, Abdallah I, Popa I, et al., Degradation mechanism of Ti-6Al-2Sn-4Zr-2Mo-Si alloy exposed to solid NaCl deposit at high temperature [J]. Corros. Sci., 2020, 172: 108611
13 Folkeson N, Jonsson T, Halvarsson M, et al., The influence of small amounts of KCl(s) on the high temperature corrosion of a Fe-2.25Cr-1Mo steel at 400 and 500oC [J]. Mater. Corros., 2011, 62: 606
14 Cao M, Liu L, Yu Z F, et al. Studies on the corrosion behavior of Fe-20Cr alloy in NaCl solution spray at 600oC [J]. Corros. Sci., 2018, 133: 165
15 Li R, Cui Y, Liu L, et al. Corrosion behavior of Ti60 alloy in fog of NaCl solution at 600oC [J]. J. Chin. Soc. Corros. Prot., 2021, 41: 595
  李 蕊, 崔 宇, 刘 莉 等. NaCl盐雾环境下Ti60合金的中温腐蚀行为 [J]. 中国腐蚀与防护学报, 2021, 41: 595
16 Mahobia G S, Paulose N, Singh V. Hot corrosion behavior of superalloy IN718 at 550 and 650oC [J]. J. Mater. Eng. Perform., 2013, 22: 2418
17 Pradhan D G, Mahobia G S, Chattopadhyay K, et al. Salt induced corrosion behaviour of superalloy IN718 [J]. Mater. Today Proc., 2018, 5: 7047
18 Shen M L, Zhu S L, Wang F H. Cyclic oxidation behavior of glass-ceramic composite coatings on superalloy K38G at 1100oC [J]. Thin Solid Films, 2011, 519: 4884
19 Yu Z F, Liu L, Liu R, et al. Corrosion behavior of GH4169 alloy under alternating oxidation at 900oC and solution immersion [J]. Materials (Basel), 2019, 12: 1503
20 Pradhan D, Mahobia G S, Chattopadhyay K, et al. Severe hot corrosion of the superalloy IN718 in mixed salts of Na2SO4 and V2O5 at 700oC [J]. J. Mater. Eng. Perform., 2018, 27: 4235
21 Sun W Y, Wang J L, Yang L L, et al. Studies on corrosion behavior of a single-crystal superalloy and its sputtered nanocrystalline coatings with solid NaCl deposit in O2 + 38 vol.% H2O environment at 700oC [J]. Corros. Sci., 2019, 161: 108187
22 Xu S, Long F, Persaud S Y, et al. Oxidation behavior of 9Cr-4.5Al ODS steel in 600oC supercritical water and the effect of pre-oxidation [J]. Corros. Sci., 2020, 165: 108380
23 Zhuang X P, Tan Y, You X G, et al. High temperature oxidation behavior and mechanism of a new Ni-Co-based superalloy [J]. Vacuum, 2021, 189: 110219
24 Jonsson T, Pujilaksono B, Heidari H, et al. Oxidation of Fe-10Cr in O2 and in O2 + H2O environment at 600oC: A microstructural investigation [J]. Corros. Sci., 2013, 75: 326
25 Juez-Lorenzo M, Kolarik V, Stamm W, et al. Oxidation of nickel-based alloys in dry and water vapour containing air [J]. Mater. High Temp., 2012, 29: 229
26 Israelsson N, Hellstr?m K, Svensson J E, et al. KCl-induced corrosion of the FeCrAl alloy Kanthal? AF at 600oC and the effect of H2O [J]. Oxid. Met., 2015, 83: 1
27 Israelsson N, Engkvist J, Hellstr?m K, et al. KCl-induced corrosion of an FeCrAl alloy at 600oC in O2 + H2O environment: The effect of pre-oxidation [J]. Oxid. Met., 2015, 83: 29
28 Fan L. Investigation on corrosion behavior of Ti60 alloy under synergetic effect of solid NaCl deposit and water vapor at 600oC [D]. Shenyang: University of Chinese Academy of Sciences (Institute of Metal Research, Chinese Academy of Scionces), 2016
  范 磊. 固态NaCl和水蒸汽协同作用下Ti60合金中温腐蚀行为的研究 [D]. 沈阳: 中国科学院大学(中国科学院金属研究所), 2016
29 Wang W Q, Cui Y, Liu R, et al. Revealing internal corrosion of GH4169 with stress coupled solid NaCl deposited in a humid environment of 600oC [J]. Corros. Sci., 2022, 195: 110004
30 Phother-Simon J, Hanif I, Liske J, et al. The influence of a KCl-rich environment on the corrosion attack of 304 L: 3D FIB/SEM and TEM investigations [J]. Corros. Sci., 2021, 183: 109315
31 Israelsson N, Unocic K A, Hellstr?m K, et al. Cyclic corrosion and chlorination of an FeCrAl alloy in the presence of KCl [J]. Oxid. Met., 2015, 84: 269
32 Israelsson N, Unocic K A, Hellstr?m K, et al. A microstructural and kinetic investigation of the KCl-induced corrosion of an FeCrAl alloy at 600oC [J]. Oxid. Met., 2015, 84: 105
Outlines

/