Influence of Size Design on Microstructure and Properties of 304L Stainless Steel by Selective Laser Melting

  • HOU Juan ,
  • DAI Binbin ,
  • MIN Shiling ,
  • LIU Hui ,
  • JIANG Menglei ,
  • YANG Fan
Expand
  • 1State Key Laboratory of Nuclear Power Safety Monitoring Technology and Equipment, China Nuclear Power Engineering Co., Ltd., Shenzhen 518172, China
    2Academy of Materials and Chemistry, University of Shanghai Science and Technology, Shanghai 200082, China

Received date: 2021-06-18

  Revised date: 2021-09-08

  Online published: 2021-12-06

Supported by

National Natural Science Foundation of China(52073176);Shenzhen International Cooperation Research Science and Technology Program(GJHZ20200731095203011);State Key Laboratory of Nuclear Power Safety Monitoring Technology and Equipment Opening Project(CSO-102-001)

Abstract

As one of the most promising metal additive manufacturing methods, selective laser melting (SLM) is very attractive for fabricating complex-shaped structure components of austenitic stainless steels in the nuclear field. SLMed austenitic 304L stainless steel has been demonstrated to have excellent mechanical properties and superior corrosion resistance due to the unique hierarchical microstructure produced by the ultrafast cooling rate and high-thermal gradient. Scanning tracks (T) and depositing layers (L) are key factors for geometry design by affecting the processing efficiency and the solidification structure of the components. Hence, it is essential to clarify the effecting mechanism of sample size and geometry on material performance. In this work, samples of different sizes are designed to study the influence of geometry on the microstructure and mechanical properties of 304L stainless steel components made via SLM. Various solidification conditions are achieved by varying the temperature gradients and cooling rates by adjusting T and L. Metallographic microscopic observations in samples with various T × L combinations demonstrate that a columnar structure is formed along the build direction, which is significantly impacted by the geometry effect. The columnar grains grow preferentially along the heat dissipation direction with an increase in the sample size. The columnar grains gradually change from having a low length-diameter ratio (LDR) with a rice grain shape to a higher LDR with a short rod-like shape and then a long strip shape. Grain coarsening could also be identified along with the formation of “long strip” columnar grains. Moreover, consistent microstructure evolution behavior is observed in large-sized samples. The influence of geometry on the mechanical properties is examined via tensile testing to demonstrate the decrease in yield strength and increased plastic elongation with the rise in sample size. As the sample size increases, the mechanical properties become consistent. The comprehensive analysis concludes that grain size and columnar grains play critical roles in determining the mechanical properties according to the Hall-Petch relationship. In larger-sized samples, “long strip” columnar grains with a high proportion could lead to a decrease in material strength and an increase in plasticity. The geometry mechanism affecting the solidification process, microstructure formation, and mechanical properties of 304L stainless steel processed by SLM is explored by combining the solidification rate and thermal gradient simulation results using ANSYS ADDITIVE.

Cite this article

HOU Juan , DAI Binbin , MIN Shiling , LIU Hui , JIANG Menglei , YANG Fan . Influence of Size Design on Microstructure and Properties of 304L Stainless Steel by Selective Laser Melting[J]. Acta Metall Sin, 2023 , 59(5) : 623 -635 . DOI: 10.11900/0412.1961.2021.00248

References

1 Das S, Wohlert M, Beaman J J, et al. Processing of titanium net shapes by SLS/HIP[J]. Mater. Des., 1999, 20: 115
2 Leuders S, Th?ne M, Riemer A, et al. On the mechanical behaviour of titanium alloy TiAl6V4 manufactured by selective laser melting: Fatigue resistance and crack growth performance[J]. Int. J. Fatigue, 2013, 48: 300
3 Ni M, Chen C, Wang X J, et al. Anisotropic tensile behavior of in situ precipitation strengthened Inconel 718 fabricated by additive manufacturing[J]. Mater. Sci. Eng., 2017, A701: 344
4 Mordike B L, Ebert T. Magnesium: Properties-applications-potential[J]. Mater. Sci. Eng., 2001, A302: 37
5 Witte F. The history of biodegradable magnesium implants: A review[J]. Acta Biomater., 2010, 6: 1680
6 Shuai C J, Yang Y W, Wu P, et al. Laser rapid solidification improves corrosion behavior of Mg-Zn-Zr alloy[J]. J. Alloys Compd., 2017, 691: 961
7 Anderson S, Baca G, O'Connor M. NEET-AMM final technical report on laser direct manufacturing (LDM) for nuclear power components[R]. United States: n. p., 2015. doi:10.2172/1233481
8 Li P F, Gong Y D, Xu Y C, et al. Inconel-steel functionally bimetal materials by hybrid directed energy deposition and thermal milling: Microstructure and mechanical properties[J]. Arch. Civ. Mech. Eng., 2019, 19: 820
9 Wang Y M, Voisin T, McKeown J T, et al. Additively manufactured hierarchical stainless steels with high strength and ductility[J]. Nat. Mater., 2018, 17: 63
10 Trevisan F, Calignano F, Aversa A, et al. Additive manufacturing of titanium alloys in the biomedical field: Processes, properties and applications[J]. J. Appl. Biomater. Funct. Mater., 2018, 16: 57
11 Hou J, Chen W, Chen Z E, et al. Microstructure, tensile properties and mechanical anisotropy of selective laser melted 304L stainless steel[J]. J. Mater. Sci. Technol., 2020, 48: 63
12 Cordero Z C, Meyer III H M, Nandwana P, et al. Powder bed charging during electron-beam additive manufacturing[J]. Acta Mater., 2017, 124: 437
13 Guan Q F, Ji L, Cai J, et al. Surface microstructure and properties of 3Cr13 martensitic stainless steel after high current pulsed electron beam bombardment[J]. J. Jilin Univ. (Eng. Technol. Ed.), 2014, 44: 712
  关庆丰, 季 乐, 蔡 杰 等. 强流脉冲电子束轰击作用下3Cr13不锈钢的微观结构及性能[J]. 吉林大学学报(工学版), 2014, 44: 712
14 El Cheikh H, Courant B, Branchu S, et al. Direct Laser Fabrication process with coaxial powder projection of 316L steel. Geometrical characteristics and microstructure characterization of wall structures[J]. Opt. Lasers Eng., 2012, 50: 1779
15 Antonysamy A A, Meyer J, Prangnell P B. Effect of build geometry on the β-grain structure and texture in additive manufacture of Ti-6Al-4V by selective electron beam melting[J]. Mater. Character., 2013, 84: 153
16 Wang D, Yang Y Q, Su X B, et al. Study on energy input and its influences on single-track, multi-track, and multi-layer in SLM[J]. Int. J. Adv. Manuf. Technol., 2012, 58: 1189
17 Gu H, Wei C, Li L, et al. Multi-physics modelling of molten pool development and track formation in multi-track, multi-layer and multi-material selective laser melting[J]. Int. J. Heat Mass Transf., 2020, 151: 119458
18 Hussein A, Hao L, Yan C Z, et al. Finite element simulation of the temperature and stress fields in single layers built without-support in selective laser melting[J]. Mater. Des., 2013, 52: 638
19 Du L, Gu D D, Dai D H, et al. Relation of thermal behavior and microstructure evolution during multi-track laser melting deposition of Ni-based material[J]. Opt. Laser Technol., 2018, 108: 207
20 Tang X, Zhang S, Zhang C H, et al. Optimization of laser energy density and scanning strategy on the forming quality of 24CrNiMo low alloy steel manufactured by SLM[J]. Mater. Character., 2020, 170: 110718
21 Song Y N, Sun Q D, Guo K, et al. Effect of scanning strategies on the microstructure and mechanical behavior of 316L stainless steel fabricated by selective laser melting[J]. Mater. Sci. Eng., 2020, A793: 139879
22 Rajeshkumar R, Niranjani V L, Devakumaran K, et al. Fusion boundary microstructure evolution and mechanical properties of cold metal transfer welded dissimilar A5754 and A5083 joint[J]. Mater. Lett., 2021, 284: 128877
23 Kim C K, Kim J H, Hong H U, et al. Behavior of weld pool convection and columnar-to-equiaxed grain transition in gas tungsten arc welds of ferritic stainless steels with different aluminum contents[J]. J. Mater. Process. Technol., 2021, 289: 116946
24 Chen W, Hou J, Huang A J. Effect of heat treatment on microstructure and mechanical property of 304L stainless steel prepared by selective laser melting[J]. Trans. Mater. Heat Treat., 2020, 41(3): 103
  陈 伟, 侯 娟, 黄爱军. 热处理对选区激光熔化304L不锈钢组织和力学性能的影响[J]. 材料热处理学报, 2020, 41(3): 103
25 Geng S N, Jiang P, Shao X Y, et al. Heat transfer and fluid flow and their effects on the solidification microstructure in full-penetration laser welding of aluminum sheet[J]. J. Mater. Sci. Technol., 2020, 46: 50
26 Leicht A, Klement U, Hryha E. Effect of build geometry on the microstructural development of 316L parts produced by additive manufacturing[J]. Mater. Character., 2018, 143: 137
27 Chong Y, Deng G Y, Gao S, et al. Yielding nature and Hall-Petch relationships in Ti-6Al-4V alloy with fully equiaxed and bimodal microstructures[J]. Scr. Mater., 2019, 172: 77
28 Kang B, Lee J, Ryu H J, et al. Microstructure, mechanical property and Hall-Petch relationship of a light-weight refractory Al0.1CrNbVMo high entropy alloy fabricated by powder metallurgical process[J]. J. Alloys Compd., 2018, 767: 1012
29 Zhang K, Li Z D, Sun F L, et al. Effect of cooling rate on microstructure evolution and mechanical properties of Ti-V-Mo complex microalloyed steel[J]. Acta Metall. Sin., 2018, 54: 31
  张 可, 李昭东, 隋凤利 等. 冷却速率对Ti-V-Mo复合微合金钢组织转变及力学性能的影响[J]. 金属学报, 2018, 54: 31
30 Wang X, Liu R C, Cao R X, et al. Effect of cooling rate on boride and room temperature tensile properties of β-solidifying γ-TiAl alloys[J]. Acta Metall. Sin., 2020, 56: 203
  王 希, 刘仁慈, 曹如心 等. 冷却速率对β凝固γ-TiAl合金硼化物和室温拉伸性能的影响[J]. 金属学报, 2020, 56: 203
Outlines

/