EFFECT OF SPECIMEN TEMPERATURE ON CRYSTALLIZATION DURING LASER REMELTITNG Zr55Cu30Al10Ni5 BULK METALLIC GLASS
Received date: 2013-04-07
Revised date: 2013-06-18
Online published: 2013-08-11
Zr55Cu30Al10Ni5 bulk metallic glasses were remelted by pulsed laser at liquid N (Ar) cooling, room temperature and 473 K. The results show that the effect of specimen temperatures on the crystallization of specimens during laser remelting metallic glasses depends on the Ar blowing. If there is no Ar blowing, the crystallization of the specimen during laser remelting under liquid Ar cooling and room temperature is similar while the molten pool is deeper for liquid Ar cooling. And the specimen remelted at 473 K was most seriously crystallized with the deepest molten pool. But comparing the specimen at room temperature, the crystallization of the specimen at liquid N was suppressed during laser remelting with Ar blowing. The effects of specimen temperatures on the crystallization of metallic glasses during laser remelting are: First, the lower specimen temperature can increase the cooling rate of specimen and therefore reduce its crystallization. Secondly, the lower specimentemperature makes the atmosphere around the specimen cooled down, reduces the shielding effect of plasma and increases the actual laser energy input into the specimen, resulting in more serious crystallization of the specimen. If there is Ar blowing, the atmosphere temperatures are similar to that at the liquid Ar cooling leading to the crystallization of the specimen to reduced. If there is no Ar blowing, the atmosphere temperature is similar to the temperature of specimen itself. In this case, the crystallization of the specimens is jointly determined by the temperature of the specimen itself and the atmosphere temperature around the specimens, which is not monotonous.
YANG Gaolin , LIN Xin , HU Qiao , SONG Menghua , WANG Zhitai , HUANG Weidong . EFFECT OF SPECIMEN TEMPERATURE ON CRYSTALLIZATION DURING LASER REMELTITNG Zr55Cu30Al10Ni5 BULK METALLIC GLASS[J]. Acta Metall Sin, 2013 , 49(8) : 925 -931 . DOI: 10.3724/SP.J.1037.2013.00166
[1] Wang C, Zhang Q S, Jiang F, Zhang H F, Hu Z Q. Acta Metall Sin, 2002; 38: 765
(王成, 张庆生, 江峰, 张海峰, 胡壮麒. 金属学报, 2002; 38: 765)
[2] Inoue A, Takeuchi A. Acta Mater, 2011; 59: 2243
[3] Byrne C, Eldrup M. Science, 2008; 321: 502
[4] Kumagai N, Samata Y, Kawashima A, Asami K, Hashimoto K. J Non-Cryst Solids, 1987; 93: 78
[5] Kim J H, Lee C, Lee D M, Sun J H, Shin S Y, Bae J C. Mater Sci Eng, 2007; A449-451: 872
[6] Chen B, Pang S, Han P, Li Y, Yavari A R, Vaughan G, Zhang T. J Alloys Compd, 2010; 504: S45
[7] Yue T M, Su Y P, Yang H O. Mater Lett, 2007; 61: 209
[8] Yang G L, Lin X, Liu F C, Hu Q, Ma L, Li J F, Wei D H. Intermetallics, 2012; 22: 110
[9] Lin X, Yang H O, Chen J, Huang W D. Acta Metall Sin, 2006; 42: 361
(林鑫, 杨海欧, 陈静, 黄卫东. 金属学报, 2006; 42: 361
[10] Cao J, Liu F C, Lin X, Huang C P, Chen J, Huang W D. Opt Laser Technol, 2013; 45: 228
[11] Liu F C, Lin X, Huang C P, Song M H, Yang G L, Chen J, Huang W D. J Alloys Compd,2011; 509: 4505
[12] Cervo R, Ferro P, Tiziani A, Zucchi F. J Mater Sci, 2010; 45: 4378
[13] Liu F C, Lin X, Yang G L, Song M H, Chen J, Huang W D. Opt Laser Technol, 2011; 43: 208
[14] Jia W P, Chen J, Lin X, Zhong C W, Huang W D. Acta Metall Sin, 2007; 43: 546
(贾文鹏, 陈静, 林鑫, 钟诚文, 黄卫东. 金属学报, 2007; 43: 546)
[15] Liu F C, Lin X, Yang G L, Huang C P, Chen J, Huang W D. Acta Metall Sin, 2010; 46: 1047
(刘奋成, 林鑫, 杨高林, 黄春平, 陈静, 黄卫东. 金属学报, 2010; 46: 1047)
[16] Laeng J, Stewart J G, Liou F W. Int J Prod Res, 2000; 38: 3973
[17] Sun H, Flores K M. Metall Mater Trans, 2010; 41A: 1752
[18] Zheng B, Zhou Y, Smugeresky J E, Lavernia E J. Metall Mater Trans, 2009; 40A: 2009
[19] Wang H S, Chen H G, Jang J S C, Chiou M S. Mater Sci Eng, 2010; A528: 338
[20] Yamasaki M, Kagao S, Kawamura Y. Scr Mater, 2005; 53: 63
[21] Hu Q, Lin X, Yang G L, Huang W D, Li J F. Acta Metall Sin, 2012; 48: 1467
(胡桥, 林鑫, 杨高林, 黄卫东, 李金富. 金属学报, 2012; 48: 1467)
[22] Xing D W, Shen J, Zhang L F, Sun J F, Wang X D, Wang H. J Alloys Compd, 2009; 481: 531
[23] Zheng Q G, Gu J H. Interaction between Laser and Matter. Wuhan: Huazhong
University of Science and Technology Press, 1996: 129
(郑启光, 辜建辉. 激光与物质相互作用. 武汉: 华中理工大学出版社, 1996: 129)
[24] Kuo T Y, Lin Y D. Mater Trans, 2007; 48: 219
[25] Shao D, Hu B, Zheng Q G. Advanced Laser Manufacturing Technology and
Device Integration. Beijing: Science Press, 2009: 44
(邵丹, 胡兵, 郑启光. 激光先进制造技术与设备集成. 北京: 科学出版社, 2009: 44)
/
| 〈 |
|
〉 |