INVESTIGATION OF THE MICROSTRUCTURE AND IMPACT PROPERTIES OF THE HIGH NITROGEN STAINLESS STEEL WELD

  • LI Dongjie ,
  • LU Shanping ,
  • LI Dianzhong ,
  • LI Yiyi
Expand
  • Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016

Received date: 2012-09-04

  Revised date: 2012-11-05

  Online published: 2013-02-11

Supported by

 

Abstract

The high nitrogen stainless steel (HNS) is widespread attention in recent years because of the high strength, good toughness and corrosion resistance. Weld ability and welding efficiency are received extensive attention in the HNS welding. Using the double shielded TIG welding method, the active element, oxygen, was transferred into weld pool so as to change the convection of the liquid metal from outward to inward. This proposed welding process could effectively reduce the width of the pool surface, which is beneficial to reducing the overflow of nitrogen content in the weld. The influence of heat input (different welding current) on the weld pool shape and the impact properties of welds were investigated. The weld penetration increased with the increasing heat input and the 10 mm thick work piece was welded thoroughly under the 250 A welding current. The XRD test and calculation results showed that the δ ferrite content in the welds was increased with the increasing welding current, while the impact properties of welds change little. The poor impact properties of the weld are another focus of this study. The fracture surfaces of the Charpy V-notch specimens were characterized using the scanning electron microscope (SEM).

Cite this article

LI Dongjie , LU Shanping , LI Dianzhong , LI Yiyi . INVESTIGATION OF THE MICROSTRUCTURE AND IMPACT PROPERTIES OF THE HIGH NITROGEN STAINLESS STEEL WELD[J]. Acta Metall Sin, 2013 , 49(2) : 129 -136 . DOI: 10.3724/SP.J.1037.2012.00514

References

[1] Berns H. ISIJ Int, 1996; 36: 909


[2] Ikegami Y, Nemoto R. ISIJ Int, 1996; 36: 855

[3] Rawers I C, White H, Doan R. ISIJ Int, 1996; 36: 746

[4] Gavriljuk V G. ISIJ Int, 1996; 36: 738

[5] Liu W, Zheng Y G, Liu C S, Yao Z M, Ke W.  Acta Metall Sin, 2003; 39:85

(柳伟, 郑玉贵, 刘常升, 姚治铭, 柯伟. 金属学报, 2003; 39: 85)

[6] Bi H Y, Jiang X X, Li S Z, Yang J X. Acta Metall Sin, 1997; 33: 1069

(毕红运, 姜晓霞, 李诗卓, 杨景祥. 金属学报, 1997; 33: 1069)

[7] Lu S P, Li D J, Li D Z, Li Y Y. Trans Chin Weld Inst, 2010; 31(2):21

(陆善平, 李冬杰, 李殿中, 李依依. 焊接学报, 2010; 31(2): 21)

[8] Tanaka M, Terasaki H, Ushio M, Lowke J J.  Plasma Chem Plasma Process,2003; 23: 585

[9] Tanaka M, Tashiro S, Ushio M, Mita T, Murphy A B, Lowke J J. Vacuum,2006; 80: 1195

[10] Burgardt P, Heiple C R. Weld J, 1986; 65(6): 150

[11] Sahoo P, DebRoy T, McNallan M J. Metall Trans, 1988; 19B: 483

[12] Katayama S, Fujimoto T, Matsunawa A. Trans JWRI, 1985; 14(1): 123

[13] Arata Y, Matsuda F, Katayama S. Trans JWRI, 1976; 5(2): 135

[14] Brooks J A, Thompson A W, Williams J C. Weld J, 1984; 63(3): 71s

[15] Fredriksson H. Metall Trans, 1972; 3: 2989

[16] Leone G L, Kerr H W. Weld J, 1982; 61(1): 13s

[17] Lippold J C, Savage W F. Weld J, 1980; 59(2): 48s

[18] Lu S P, Fujii H, Nogi K. Scr Mater, 2004; 51: 271

[19] Lu S P, Fujii H, Nogi K. Sci Technol Weld Join, 2007; 12: 689

[20] Howse D S, Lucas W. Sci Technol Weld Join, 2000; 15(5): 189

[21] Liu L M, Zhang Z D, Song G, Wang L. Metall Mater Trans, 2007; 38A:649

[22] Huang H Y. Metall Mater Trans, 2010; 41A: 2829

[23] Anderko K, Schafer L, Materna-Morris E. J Nucl Mater, 1991; 179-181:492

[24] Schafer L. J Nuclear Mater, 1998; 258-263: 1336

[25] Wang P, Lu S P, Xiao N M, Li D Z, Li Y Y. Mater Sci Eng, 2010; A527: 3210
Outlines

/