STUDY OF COMPLEX DUCTILE INCLUSIONS CONTROLLING IN MEDIUM-HIGH CARBON STEELS
Received date: 2012-04-24
Revised date: 2012-07-20
Online published: 2012-11-11
Supported by
Supported by Key Research and Development Program of the Ministry of Railway of China (Nos.2009J015 and 2009J016)
Formation of a special kind of complex ductile inclusions (CDI), which were character as oxides covered by sulphides, was investigated in a medium--high carbon steel. It was believed that fatigue and toughness properties of carbon steels were benefited from CDI formation, for oxides were separated from steel matrix. By means of thermodynamic calculation and inclusion microscopy in medium-high carbon steels with different S content and with Ca-treated, CDI in 0.55C steels has been researched. And thermal-stability of the CDI was researched by high temperature quenching. The results show that the frequency of CDI formation increase with S content changes from 0.001% to 0.01%. However, the fraction of covered oxides is no more than 90% without Ca-treated and can be promoted to about 100% in 0.006% S steel after Ca-treated. The reason of improved CDI formation by increasing S content and Ca-treated is that sulphides precipitation temperature could be promoted to higher than solid line of matrix, which is clearly showed by thermodynamic calculation. Furthermore, thermo-stability of CDI is affected heavily by heating history of matrix steel. Sulphide will dissolute from oxide when heat steel casting to an improper high temperature. Fortunately, the dissolution process could be stunted with redundant S content. It shows that thermo-stability of CDI could be received in Ca-treated steels with more than 0.006%S.
MA Yue SU Hang PAN Tao YU Yinhong YANG Caifu ZHANG Yongquan PENG Yun . STUDY OF COMPLEX DUCTILE INCLUSIONS CONTROLLING IN MEDIUM-HIGH CARBON STEELS[J]. Acta Metall Sin, 2012 , 48(11) : 1321 -1328 . DOI: 10.3724/SP.J.1037.2012.00225
[1] Lyne C M, Kasak A. Trans ASM, 1968; 61: 10
[2] Mine K, Yoshida H. Jpn Pat, s55–041910, 1980
[3] Deng Z S. Acta Metall Sin, 1976; 12: 187
(邓枝生. 金属学报, 1976; 12: 187)
[4] Wang C W, Dong H S, Yang Z N. J China Text Univ (Engl Ed), 1989; 6(1): 26
[5] Zhang W P. J Sichuan Norm Univ (Nat Sci), 2005; 28: 619
(张维平. 四川师范大学学报(自然科学版), 2005; 28: 619)
[6] Ma Y, Pan T, Jiang B, Cui Y H, Su H, Peng Y. Acta Metall Sin, 2011; 47: 978
(马跃, 潘涛, 江波, 崔银会, 苏航, 彭云. 金属学报, 2011; 47: 978)
[7] Brooksbank D, Andrews K W. J Iron Steel Inst, 1968; 206: 595
[8] Brooksbank D, Andrews K W. J Iron Steel Inst, 1969; 207: 474
[9] Pan T, Yang Z G, Bai B Z, Fang H S. Acta Metall Sin, 2003; 39: 1037
(潘涛, 杨志刚, 白秉哲, 方鸿生. 金属学报, 2003; 39: 1037)
[10] Oh Y J, Lee B S, Hong J H. J Nuclear Mater, 2002; 301: 108
[11] Li J, Guo F, Li Z, Wang J L, Yan M G. J Iron Steel Res Int, 2007; 14: 254
[12] Garrison Jr W M, Wojcieszynski A L. Mater Sci Eng, 2007; A464: 321
[13] Salter W J M, Pickering F B. J Iron Steel Inst, 1969; 207: 992
[14] Yang C W, L¨u N B, Zhuo X J, Wang X H, Wang W J. Iron Steel, 2010; 45(11): 32
(杨成威, 吕迺冰, 卓晓军, 王新华, 王万军. 钢铁, 2010; 45(11): 32)
[15] Zhuo X J, Wang Y Q, Wang X H, Lee H G. J Iron Steel Res Int, 2010; 17(2): 10
[16] Kim T G, Lee W K, Park J H, Min D J, Song H S. ISIJ Int, 2001; 41: 1460
[17] Miyamoto G, Shinyoshi T, Yamaguchi J, Furuhara T, Maki T, Uemori R. Scr Mater, 2003; 48: 371
[18] Li S J, Ren X C, Gao K W, Su Y J, Jiang B, Chen G, Zhao H. Trans Mater Heat Treat, 2011; 32(12): 48
(李胜军, 任学冲, 高克玮, 宿彦京, 江波, 陈刚, 赵海. 材料热处理学报, 2011; 32(12): 48)
[19] Lu X Z, Wu R, Li S L,Wu H T, ZhaiWL, Huang L, Wu D B, Song S P. J Wuhan Univ Sci Technol, 2010; 34: 147
(卢献忠, 吴润, 李书黎, 吴海涛, 翟万里, 黄雷, 吴德炳, 宋述鹏. 武汉科技大学学报, 2010; 34: 147)
[20] Ye G Z, J¨onsson P, Lund T. ISIJ Int, 1996; 36: S105
[21] Kusano Y, Kawauchi Y, Wajima M, Sugawara K, Yoshida M, Hayashi H. ISIJ Int, 1996; 36: S77
[22] Yuan F M, Wang X H, Yang X F. J Univ Sci Technol Beijing, 2006; 13: 486
[23] Taguchi K, Ono–Nakazato H, Nakai D, Usui T, Marukawa K. ISIJ Int, 2003; 43: 1705
[24] Oikawa K, Ohtani H, Ishida K, Nishizawa T. ISIJ Int, 1995; 35: 402
[25] Wakoh M, Sawai T, Mizoguchi S. ISIJ Int, 1996; 36: 1014
[26] Wang Y, Zhao A M, Chen Y L, Zuo B Q, Xue J P. Iron Steel, 2011; 46(1): 60
(王岩, 赵爱民, 陈银莉, 左碧强, 薛俊平. 钢铁, 2011; 46(1): 60)
/
| 〈 |
|
〉 |